Related papers: Improved superconducting properties of MgB2
We report magnetic field dependent magnetization and microwave impedance measurements on a MgB2 superconductor prepared by high pressure synthesis. We find that the upper critical field is linearly dependent on temperature near Tc and the…
Transport current values of 7.5 x 104 A/cm2 at 4.2 K and self-field are reported for MbB2-based tapes. MgB2 strands were formed by directly filling commercially available MgB2 powder into Nb-lined, monel tubes and wire drawing. The wires…
The superconducting phase diagram of MgB2 was determined from magnetization, magneto-transport and the first single-crystal specific heat measurements. A zero-temperature in-plane coherence length of 8 nm is determined. The superconducting…
This review paper illustrates the main normal and superconducting state properties of magnesium diboride, a material known since early 1950's, but recently discovered to be superconductive at a remarkably high critical temperature Tc=40K…
The critical current densities of MgB2 monofilamentary strands with and without SiC additions were measured at 4.2 K. Additionally, magnetic Jc at B = 1 T was measured from 4.2 K to 40 K. Various heat treatment times and temperatures were…
The recent discovery of intermediate-temperature superconductivity (ITC) in MgB2 by Akimitsu et al. and its almost simultaneous explanation in terms of a hole-carrier-based pairing mechanism by Hirsch, has triggered an avalanche of studies…
Electrolysis was carried out on fused mixtures of MgCl2, NaCl, KCl and MgB2O4 under an Ar flow at 600C. Electrical resistivity measurements for the grown deposits show an onset of superconducting transition at 37 K in the absence of applied…
The recent discovery of superconductivity at ~39 K in MgB2, by Nagamatsu et al. establishes this simple binary compound as having the highest bulk superconducting transition temperature, Tc, of any non-copper-oxide material. Much of the…
We succeeded in the synthesis of high-Jc MgB2 bulks via high energy ball-milling of elemental Mg and B powder at ambient temperatures. Alternatively to longtime mechanical alloying technique, the mixed powder was ball-milled for only 1h and…
The critical current density of four MgB2 samples was measured inductively and for one of them also by transport. Pure phased and dense bulk samples yield a critical current density which in value, as well as in its magnetic field and…
A polycrystalline sample of the MgB_2 superconductor was investigated by measurements of the electrical resistivity, the thermopower and the thermal conductivity in the temperature range between 1.8K and 300K in zero magnetic field. The…
Based on DC magnetization measurements, the temperature dependencies of the trapped magnetic field have been calculated for two MgB2 samples prepared by two different techniques: the high-pressure sintering and the hot pressing.…
This paper reports specific-heat measurements on superconducting MgB2 in magnetic fields to 9 T. In zero magnetic field the data can be fitted to a two-gap model, which is a generalization of a semi-empirical model for strong-coupled,…
We studied the effect of disorder on the superconducting properties of polycrystalline MgB_2 by specific-heat measurements. In the pristine state, these measurements give a bulk confirmation of the presence of two superconducting gaps with…
The upper critical field Hc2(T) of sintered pellets of the recently discovered MgB_2 superconductor was investigated in magnetic fields up to 16 T. The upper critical field of the major fraction of the investigated sample was determined…
The hydrostatic pressure effect on the newly discovered superconductor MgB2 has been determined. The transition temperature Tc was found to decrease linearly at a large rate of -1.6 K/GPa, in good quantitative agreement with the ensuing…
The synthesis of MgB2-based materials under high pressure gave the possibility to suppress the evaporation of magnesium and to obtain near theoretically dense nanograined structures with high superconducting, thermal conducting, and…
Magnetisation and magnetoresistance measurements have been carried out on superconducting Ba1-xKxFe2As2 samples with x=0.40 and 0.50. From low field magnetization data carried out at different temperatures below TC, HC1 has been extracted.…
Two different hot isostatic pressing cycles (HIPing) were investigated to synthesize bulk MgB2 samples: a "standard" cycle where a low vessel pressure is maintained while heating to the process temperature with a subsequent simultaneous…
If the critical current density Jc is very high for a superconductor, then estimating its value from transport measurements is not very easy. In such cases, the value of Jc, called Jcm for magnetic Jc, is usually obtained from the measured…