Related papers: Improved superconducting properties of MgB2
High-density bulk materials of a newly discovered 40K intermetallic MgB2 superconductor were prepared by high pressure sintering. Superconducting transition with the onset temperature of 39K was confirmed by both magnetic and resistive…
Bulk samples of MgB2 have been formed by hot isostatic pressing (HIPping) of commercial powder at 100MPa and 950=B0C. The resulting material is 100% dense with a sharp superconducting transition at 37.5K. Microstructural studies have…
We synthesized single crystalline and policrystalline MgB_2 under ambient pressures. The single crystals of MgB_2 were of good quality, where the crystal structure refinements were successfully converged with R = 0.020. The specific heat of…
Transport and thermodynamic properties of a sintered pellet of the newly discovered $MgB_2$ superconductor have been measured to determine the characteristic critical magnetic fields and critical current densities. Both resistive transition…
We report synthesis, structure/micro-structure, resistivity under magnetic field [R(T)H], Raman spectra, thermoelectric power S(T), thermal conductivity K(T), and magnetization of ambient pressure argon annealed polycrystalline bulk samples…
Dense pure and doped (Mg1-xAx)B2 samples with A = Na, Ca, Cu, Ag, Zn and Al were synthesized at high pressure - high temperature in a multi anvils press (3.5-6 GPa, 900-1000C) for x up to 0.20. They were studied by x-ray diffraction,…
We have successfully prepared the MgB2 superconducting bulk and powdered materials by the method of combustion synthesis. The starting materials used in this study were powders of Mg and B. X-ray powder diffraction pattern was well assigned…
Superconducting properties of bulk, dense, pure MgB2 and doped (Mg1-xAx)B2 samples with A = Na, Ca, Cu, Ag, Zn and Al were studied for compositional ranges 0 < x < 0.20. The effect on pinning properties and critical current were…
In this letter, we report the first successful fabrication of dense, metal-clad MgB2 superconductor wires as well as the first demonstration of high transport Jc of greater than 36,000 A/cm2 in MgB2. The fabrication technique that we…
The MgB2 bulks were prepared by high energy milling of Mg and B powder. The correlations among milling times, microstructure and superconducting properties were investigated in MgB2 bulks. Samples were characterized by x-ray diffraction…
The specific heat C of a sintered polycrystalline sample of MgB2 with a bulk superconducting transition temperature Tc=36.7 K is measured as a function of the temperature (2-300 K) and magnetic field (0-16 T), together with magnetic…
Highly dense MgB2 policrystalline bulk materials, obtained by reactive liquid infiltration, have been characterized in their superconducting transport and magnetic properties in magnetic field and in a temperature range of interest for the…
We characterize the superconducting state of phase pure polycrystalline samples of the new layered superconductor MgB$_2$ by specific heat measurements in magnetic fields up to 9 T. The characteristic jump at the superconducting transition…
Magnetization studies have been carried out on superconducting MgB$_2$ (T$_c$=37K) in the temperature range of 2-50K and in magnetic field up to 5 Tesla. From these measurements, values of the lower critical field H$_c1$(0), upper critical…
We report on the results of a comparative investigation of highly dense bulk MgB$_2$ samples prepared by three methods: (i) hot deformation; (ii) high pressure sintering; and (iii) mechanical alloying of Mg and B powders with subsequent hot…
The review considers bulk MgB2-based materials in terms of their structure, superconducting and mechanical properties. Superconducting transition temperatures of 34.5-39.4 K, critical current densities of 1.8-1.0 x E6 A/sq.cm in self field…
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…
The high-pressure synthesis is one of the most promising methods to produce MgB2 superconductive (SC) material. The available high-pressure apparatuses have working volume up to 100 cm3 which allows samples up to 60 mm in diameter to be…
The normal state and superconducting properties of MgB2 and Mg1-xAlxB2 are discussed based on structural, transport, and high pressure experiments. The positive Seebeck coefficient and its linear temperature dependence for Tc<T<160 K…
We report synthesis, structural details and complete superconducting characterization of very recently discovered Nb2PdS5 new superconductor. The synthesized compound is crystallized in mono-clinic structure. Bulk superconductivity is seen…