We have exposed seven full length production quality crystals of the electromagnetic calorimeter (ECAL) of the CMS detector to a 20 GeV/c proton beam at the CERN PS accelerator. The exposure was done at fluxes of 10**12 p/cm**2/h and 10**13…
Eight production quality PbWO4 crystals of CMS have been irradiated in a 20 GeV/c proton beam up to fluences of 5.4E13cm-2. The damage recovery in these crystals has been followed for over a year. Comparative irradiations with 60Co photons…
We employed two independent methods to study possible damage to the scintillation mechanism in lead tungstate crystals due to irradiation by a 34 GeV pion beam. First, 10 crystals were irradiated simultaneously over 30 hours by a narrow…
A Lead Tungstate crystal produced for the electromagnetic calorimeter of the CMS experiment at the LHC was cut into three equal-length sections. The central one was irradiated with 290 MeV/c positive pions up to a fluence of (5.67 +-…
Kinetics of radiation damage of the PWO crystals under irradiation and recovery were studied. Crystals were irradiated with dose corresponding to average one expected in the electromagnetic calorimeter (working dose irradiation). Radiation…
Lutetium-Yttrium Orthosilicate doped with Cerium (LYSO:Ce), as a bright scintillating crystal, is a candidate for calorimetry applications in strong ionizing-radiation fields and large high-energy hadron fluences as are expected at the CERN…
The anticipated performance of calorimeter crystals in the environment expected after the planned High-Luminosity upgrade of the Large Hadron Collider (HL-LHC) at CERN has to be well understood, before informed decisions can be made on the…
High light collection efficiency is an important requirement in any application of scintillation detectors. The purpose of this study is to investigate the possibility for improving this parameter in cryogenic scintillation bolometers,…
A Cerium Fluoride crystal produced during early R&D studies for calorimetry at the CERN Large Hadron Collider was exposed to a 24 GeV/c proton fluence Phi_p=(2.78 +- 0.20) x 10EE13 cm-2 and, after one year of measurements tracking its…
We measure and explain scintillator non-proportionality and gamma quenching of CaWO4 at low energies and low temperatures. Phonons that are created following an interaction in the scintillating crystal at temperatures of 15mK are used for a…
Lead fluoride (PbF$_2$) crystals represent an excellent and relatively innovative choice for high resolution electromagnetic calorimeters with high granularity and fast timing for high intensity environments. For this reason two PbF$_2$…
Scintillating LFS-3 and LFS-8 crystals were exposed to a 155 MeV/c proton fluence $\Phi_{p}=(4.4\pm0.4)\cdot10^{12}cm^{-2}$. There was negligible reduction in transmission spectrum of LFS-3 crystal measured in 30 days after irradiation.
A hybrid dual-readout calorimeter concept, comprising both electromagnetic and hadronic sections, has recently been proposed to meet the performance requirements of experiments at future e$^{+}$e$^{-}$ colliders. The front compartment…
Future cryogenic experiments searching for rare events require reliable, efficient and robust techniques for the detection of photons at temperatures well below that to which low-temperature photomultipliers (PMT) were characterised.…
Measurements are presented of the reduction of signal output due to radiation damage for plastic scintillator tiles used in the hadron endcap (HE) calorimeter of the CMS detector. The tiles were exposed to particles produced in…
This article reports on the installation and initial commissioning of a large-scale lead tungstate (PbWO4) scintillating crystal calorimeter developed for high-rate photon detection and precise energy measurement. The calorimeter comprises…
Scintillating homogeneous detectors represent the state of the art in electromagnetic calorimetry. Moreover, the currently neglected crystalline nature of the most common inorganic scintillators can be exploited to achieve an outstanding…
In prospect of its application in cryogenic rare-event searches, we have investigated the low-temperature scintillation properties of CaWO4 crystals down to 3.4 K under {\alpha} and {\gamma} excitation. Concerning the scintillation decay…
Ensuring the radiation hardness of PbWO4 crystals was one of the main priorities during the construction of the electromagnetic calorimeter of the CMS experiment at CERN. The production on an industrial scale of radiation hard crystals and…
Measurements of the degradation in performance of 30 cm long CsI(Tl) scintillation crystals exposed to 1 MeV photon doses of 2, 10, 35, 100 and 1000 Gy are presented. The light yield, light yield longitudinal non-uniformity, scintillation…