We report the magnetization losses in an experimental multifilament coated conductor. A 4 mm wide and 10 cm long YBCO coated conductor was subdivided into eight 0.5 mm wide filaments by laser ablation and subjected to post-ablation…
We report the data on magnetization losses and critical current of multifilament copper stabilized coated conductors. Eight centimeters long samples of copper stabilized YBa2Cu3O7-x (YBCO) coated conductors manufactured commercially were…
AC losses of YBCO coated conductors are investigated by calculation and experiment for the higher frequency regime. Previous research using YBCO film deposited onto single crystal substrates demonstrated the effectiveness of filamentary…
Coupling losses were studied in composite tapes containing superconducting material in the form of two separate stacks of densely packed filaments embedded in a metallic matrix of Ag or Ag alloy. This kind of sample geometry is quite…
We report an experimental approach to making multifilament coated conductors with low losses in applied time-varying magnetic field. Previously, the multifilament conductors obtained for that purpose by laser ablation suffered from high…
Striation of HTS coated conductors (CCs) as a way to reduce their magnetization AC losses has been the subject of intense research in the past years by several groups. While the principle of this approach is well understood, its practical…
We report the results of a study of the magnetization losses in experimental multifilament, as well as control (uniform), coated superconductors exposed to time-varying magnetic field of various frequencies. Both the hysteresis loss,…
Losses as function of the a.c. magnetic field amplitude ($B_0$) were measured at 77 K in untwisted BSCCO(2223)/Ag tapes, at different frequencies, by measuring the imaginary part of the a.c. susceptibility. In particular, loss measurements…
Striating HTS coated conductor (CC) tapes into narrow filaments offers the possibility of reducing the tapes' magnetization losses without unreasonably decreasing their current-carrying capability. However, realizing well-separated…
In high power density superconducting motors, superconducting tapes are usually stacked and connected together at terminals to improve the current capacity. When a parallel sinusoidal magnetic field is applied on this partially coupled…
The magnetic oscillations in YBCO high-temperature superconductors have been widely studied over the last decade and consist of three equidistant low frequencies with a central frequency several times more intense than its two shoulders.…
We report the results of a magnetization losses study in experimental multifilament, multiply connected coated superconductors exposed to time-varying magnetic field. In these samples, the superconducting layer is divided into parallel…
The investigation of transport characteristics in high-temperature superconductors under magnetic fields is one of the most important topics in condensed matter physics and transport applications. For YBa$_2$Cu$_3$O$_7$ (YBCO), the…
The electrical resistivity rho_c of the underdoped cuprate superconductor YBCO was measured perpendicular to the CuO_2 planes on ultra-high quality single crystals in magnetic fields large enough to suppress superconductivity. The…
Many superconducting power applications contain REBCO coils. Superconducting motors are very interesting for mobile applications like aviation, thanks to their high power per unit weight. In order to reduce the inductance, multi-tape…
AC losses in conductor-on-rounded-core (CORC) cables of YBCO high-temperature superconducting (HTS) tapes are a significant challenge in HTS power applications. This study employs two finite element analysis (FEA) models to investigate the…
The damping of the oscillations of a small permanent magnet (spherical shape, radius 0.1 mm) levitating between two parallel YBCO surfaces is measured as a function of oscillation amplitude and temperature. The losses in the samples…
The competition of superconductivity and magnetism in superlattices composed of alternating YBa$_2$Cu$_3$O$_{7-d}$ and La$_{0.67}$Ca$_{0.33}$MnO$_{3}$ thin films is investigated using low-energy optical spectroscopy. The thickness of the…
The influence of YBa2Cu3O4 (YBCO) superconductor layer (S-layer) with varying thickness d-YBCO = 20 to 50 nm on the magnetic coupling between two La0.67Ca0.33MnO3 (LCMO) ferromagnet layers (F-layer, thickness d-LCMO = 50 nm) in F/S/F…
The possibility of a substantial reduction of weight and size of electrical generators is the main incentive behind the effort to develop superconducting armature windings based on coated conductors in the form of wide tapes with large…