We report a simple and easily controllable method where a nano-undulated surface morphology of Nd1/3Eu1/3Gd1/3Ba2Cu3Ox (NEG) films leads to a substantial increase in the critical current density in superconducting YBa2Cu3Ox (YBCO) films…

There are numerous potential applications for superconducting tapes, based on YBa2Cu3O7-x (YBCO) films coated onto metallic substrates. A long established goal of more than 15 years has been to understand the magnetic flux pinning…

Much smoother surfaces and significantly improved superconducting properties of relatively thick YBa2Cu3O7 (YBCO) films have been achieved by introducing a multilayered structure with alternating main YBCO and additional NdBCO layers. The…

A rapid decrease in the critical current density (Jc) of YBa2Cu3O7-x (YBCO) films with increasing film thickness has been observed for multiple YBCO growth processes. While such behavior is predicted from 2D collective pinning models under…

Detailed measurements of the critical current density jc of YBa2Cu3O7 films grown by pulsed laser deposition reveal the increase of jc as function of the filmthickness. Both this thickness dependence and the field dependence of the critical…

Epitaxial NdBa2Cu3O7-x films with a hybrid nanoscale defect structure comprised of BaZrO3 nanodot arrays aligned along the c-axis in one half of the film thickness and aligned perpendicular to the c-axis in the other half thickness of the…

The critical current (Jc) of highly twinned YBa2Cu3O7 films has been measured as a function of temperature, magnetic field and angle. For much of the parameter space we observe a strong suppression of Jc for fields in the twin boundary (TB)…

We have conducted pulsed transport measurements on c-axis oriented magnesium diboride films over the entire relevant ranges of magnetic field $0 \alt H \alt H_{c2}$ (where \hcu is the upper critical field) and current density $0 \alt j \alt…

We have grown and characterized 30 nm thick YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) films, deposited by pulsed laser deposition on both MgO (110) and SrTiO$_3$ (001) substrates, which induce opposite strain to the superconducting layer. By…

Bulk superconductor samples of YBa2Cu3-xZnxO7-{\delta} with x = 0, 0.01, 0.03 are synthesized by solid-state reaction route. The structural characterisation of all samples has been carried out by x-ray-diffraction (XRD) and transmission…

In the present work we study the growth by pulsed laser deposition of YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) films on the r-cut sapphire substrates. To improve the matching of the lattice parameters between the substrate and the film we use…

A laser scanning microscope with a thermal spot size of about 4 $\mu$m is used to measure a quantity proportional to the rf current density in an operating superconducting co-planar waveguide microwave resonator. The twinning of the…

We have studied the local critical current density, jc, in the superconductor thin film of bilayer structures consisting of YBa2Cu3O7 and the ferromagnets La2/3Ca1/3MnO3 and SrRuO3, respectively, by means of quantitative magneto-optics. A…

We have prepared Na-doped YBa2Cu3Oy (YBa1.9Na0.1Cu3Oy +40mol%Y211) (YBNCO) and Na-free YBa2Cu3Oy (YBCO) samples by the Melt-Textured Growth (MTG) method to study the effect of doped Na ion on flux pinning. The ac susceptibility curves (acs)…

The critical current density of epitaxial YBCO films grown on vicinal SrTiO3 substrates was investigated by electrical transport measurements along and across the steps of the SrTiO3 surface for a range of temperatures of 10 K to 85 K and…

Flux pinning scaling laws were developed to explain the observed increase in the critical current density Jc caused by increased density of grain boundaries in polycrystalline low temperature superconductors (LTS) such as Nb3Sn. For four…

We have studied a three-unit-cell-thick YBa2Cu3O7-x (YBCO) superconducting film grown on a slightly vicinal SrTiO3 substrate that was polished from the (001) plane by a small miscut angle (less than 0.5 degrees). This produced, on its…

Large area arrays of through-thickness nanoscale pores have been milled into superconducting Nb thin films via a process utilizing anodized aluminum oxide thin film templates. These pores act as artificial flux pinning centers, increasing…

Dissipation-free current transport in high-temperature superconductors is one of the most crucial properties of this class of materials which is directly related to the effective inhibition of flux line movement by defect structures. In…

We have grown untwinned YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) films on (110) MgO substrates that were pre-annealed at high temperature in oxygen atmosphere. The annealing results in surface reconstruction with shallow facets, which induce the…