相关论文: Phonon scattering and stability of Na_0.5CoO_2

Polarized Raman scattering measurements have been performed on Na0.5CoO2 single crystal from 8 to 305 K. Both the A1g and E1g phonon modes show a softening below Tc1 ~ 83 K. Additionally, the A1g phonon mode, which is forbidden in the…

Raman scattering experiments on Na_{x}CoO_2 yH_2O single crystals show a broad electronic continuum with a pronounced peak around 100 cm-1 and a cutoff at approximately 560 cm-1over a wide range of doping levels. The electronic Raman…

We report Raman scattering experiments on the strongly correlated electron system NaxCoO2 with x= 0.71 and ordered Na vacancies. In this doping regime, NaxCoO2 exhibits a large and unusual thermopower and becomes superconducting upon…

We investigate phonon lifetimes in VO2 single crystals. We do so in the metallic state above the metal-insulator transition (MIT), where strong structural fluctuations are known to take place. By combining inelastic X-ray scattering and…

We use polarization-resolved Raman scattering to study lattice dynamics in NaFe$_{0.53}$Cu$_{0.47}$As single crystals. We identify 4 $A_{1g}$ phonon modes at 125, 172, 183 and 197 cm$^{-1}$, and 4 $B_{3g}$ phonon modes at 101, 138, 173, 226…

In order to investigate the origin of the phase transition observed in NaV$_2$O$_5$, as well as its electronic structure, we have measured Raman intensities as a function of the laser wavelength above and below the phase transition…

The recently discovered layered BiS2-based superconductors have attracted a great deal of interest due to their structural similarity to cuprate and iron-pnictide superconductors. We have performed Raman scattering measurements on two…

The nonstoichiometric NaxCoO2 system exhibits extraordinary physical properties that correlate with temperature and Na concentration in its layered lattice without evident long-range structure modification when conventional crystallographic…

We present a detailed temperature dependent Raman light scattering study of optical phonons in Ba{1-x}K{x}Fe{2}As{2} (x ~ 0.28, superconducting Tc ~ 29 K), Sr{1-x}K{x}Fe{2}As{2} (x ~ 0.15, Tc ~ 29 K) and non-superconducting BaFe{2}As{2}…

We report infrared spectra of a Na$_{0.5}$CoO$_2$ single crystal which exhibits a sharp metal-insulator transition near 50 K due to the formation of charge ordering. In comparison with x=0.7 and 0.85 compounds, we found that the spectral…

We have studied the spin-Peierls (SP) transition in alpha'-Na_{1-delta}V_2O_5 (delta = 0, 0.01 and 0.1) by means of Raman scattering. At room temperature, we observe six A_1 and three A_2 phonon modes and a broad Raman band. Below…

The Raman spectra of the parent compound NaxCoO2 (x=0.75) and the superconducting oxyhydrates NaxCoO2.yH2O with different superconducting temperatures (Tc) have been measured. Five Raman active phonons around 195 cm-1 (E1g), 482 cm-1, 522…

We report a comprehensive Raman study of the phonon behaviour in PdSe$_2$ in the temperature range of 5 K to 300 K. A remarkable change in the Raman spectrum is observed at 120 K: a significant enhancement of the out-of-plane phonon…

We have performed polarized Raman scattering measurements on WTe$_2$, for which an extremely large positive magnetoresistance has been reported recently. We observe 5 A$_1$ phonon modes and 2 A$_2$ phonon modes out of 33 Raman active modes,…

Room temperature Raman scattering measurements have been carried out on well characterized samples of MgB2-xCx. The Raman line corresponding to the E2g phonon mode shows progressive hardening from 620 cm-1 in pristine MgB2 to 775 cm-1 in…

The Raman-active phonons in perovskite-like LaMn1-xCoxO3 (x = 0, 0.2, 0.3, 0.4, and 1.0) were studied by measuring Raman spectra at temperatures of 295 and 5 K. The changes in the spectra with Co doping are correlated with the decrease of…

We report inelastic light scattering studies on Ca(Fe0.97Co0.03)2As2 in a wide spectral range of 120-5200 cm-1 from 5K to 300K, covering the tetragonal to orthorhombic structural transition as well as magnetic transition at Tsm ~ 160K. The…

We report inelastic light scattering experiments on CaFe_2As_2 in the temperature range of 4 to 290 K. In in-plane polarizations two Raman-active phonon modes are observed at 189 and 211 cm-1, displaying A_1g and B_1g symmetries,…

The effect of pressure and temperature on the Raman-active phonon mode of osmium metal has been investigated for pressures up to 20 GPa and temperatures in the range 10--300 K. Under hydrostatic conditions (He pressure medium) the phonon…

Temperature-dependent (5 K to 300 K) Raman scattering study of A$_{1g}$/A'$_1$ phonon modes in mono-layer (1L), bilayer (2L), trilayer (3L), and tetralayer (4L) MoTe$_2$ is reported. The temperature evolution of the modes' intensity…