相关论文: Carbon substitution in MgB2 single crystals: struc…
Carbon-substituted MgB2 single crystals, Mg(B_1-xC_x)_2 of 0.3-1.0 mm size were grown for x=0.02-0.15 by a high-pressure technique. The doping dependence of lattice constants studied in a range of x=0.0-0.2 shows a monotonic decrease in a,…
We present details of synthesis optimization and physical properties of nearly single phase carbon doped MgB2 with a nominal stoichiometry of Mg(B{0.8}C{0.2})2 synthesized from magnesium and boron carbide (B4C) as starting materials. The…
We report data on the thermal conductivity \kappa(T,H) in the basal plane of hexagonal single-crystalline and superconducting Mg(B_{1-x}C_x)_2 (x= 0.03, 0.06) at temperatures between 0.5 and 50 K, and in external magnetic fields H between 0…
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…
The effects of high-temperature vacuum-annealing induced Mg deficiency in MgB2 single crystals grown under high pressure were investigated. As the annealing temperature was increased from 800 to 975 C, the average Mg content in the MgB2…
The DC magnetization and AC complex magnetic susceptibilities were measured for MgB2 single crystals, unsubstituted and carbon substituted with the composition of Mg(B_0.94C_0.06)2. The measurements were performed in AC and DC magnetic…
In this paper, we reported the structural properties and superconductivity of Mg(B1-xCx)2 compounds. Powder x-ray diffraction results indicate that the samples crystallize in a hexagonal AlB2-type structure. Due to the chemical activity of…
Single crystals of Mg1-xAlxB2 have been grown at a pressure of 30 kbar using the cubic anvil technique. Precipitation free crystals with x < 0.1 were obtained as a result of optimization of already developed MgB2 crystal growth procedure.…
The effect of Li substitution for Mg and of Li-C co-substitution on the superconducting properties and crystal structure of MgB2 single crystals has been investigated. It has been found that hole doping with Li decreases the superconducting…
The electronic properties of the carbon substituted MgB$_2$ single crystals are reported. The carbon substitution drops T$_c$ below 2 K. In-plane resistivity shows a remarkable increase in residual resistivity by C-substitution, while the…
We report data on the Hall coefficient (RH) of the carbon substituted Mg(B1-xCx)2 single crystals with x in the range from 0 to 0.1. The temperature dependences of RH obtained for the substituted crystals differ systematically at low…
Clarifying the impact of Fe doping on the structural and superconducting properties of MgB2 is crucial, considering that iron is commonly used as a sheath material for the fabrication of metal-clad MgB2 wires and tapes. To date the effects…
Successful replacement of B by C in the series MgB2-xCx for values of x upto 0.3 are reported. Resistivity and ac susceptibility measurements have been carried out in the samples. Solubility of carbon, inferred from the observed change in…
The upper critical field Hc2||c(0) of 85 kOe in Mg(B0.94C0.06)2 single crystals, determined from torque measurements, is more than twice as large as that one of 31 kOe in unsubstituted MgB2. Anisotropy of Hc2 increases from about 3.4 near…
Single crystals of MgB2 and Mg(B1-xCx)2 have been grown using cubic anvil technique. Tc values vary in a wide range (39-9 K) with carbon content varying from 0 up to 16%. Using SiC as the precursor leads to C and not to Si substituted…
Single crystals of MgB2 with a size up to 1.5x0.9x0.2 mm3 have been grown with a high pressure cubic anvil technique. The crystal growth process is very peculiar and involves an intermediate nitride, namely MgNB9. Single crystals of BN and…
We investigated carbon substitution effect on boron plane of superconducting MgB$_2$. MgB$_2$ and MgB$_{1.8}$C$_{0.2}$ samples are synthesized under high pressure furnace. MgB$_{1.8}$C$_{0.2}$ are characterized as AlB$_2$-type single phase…
We report that the ternary MgB2-xCx compounds adopt an isostructural AlB2-type hexagonal structure in a relatively small range of nominal carbon concentration, x<0.1. The lattice parameter a decreases almost linearly with increasing carbon…
We report on specific heat, high magnetic field transport and $ac-$susceptibility measurements on magnesium diboride single crystals. The upper critical field $H_{c2}$ for magnetic fields perpendicular and parallel to the Mg and B planes is…
The review considers bulk MgB2-based materials in terms of their structure, superconducting and mechanical properties. Superconducting transition temperatures of 34.5-39.4 K, critical current densities of 1.8-1.0 x E6 A/sq.cm in self field…