相关论文: Preparation of YBCO superconducting thick films On…
We have grown and characterized 30 nm thick YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) films, deposited by pulsed laser deposition on both MgO (110) and SrTiO$_3$ (001) substrates, which induce opposite strain to the superconducting layer. By…
Superconducting MgB(2) films with Tc = 38.6 K were prepared using a precursor-deposition, ex-situ post-processing approach. Precursor films of boron, ~0.5 micrometer thick, were deposited onto Al(2)O(3) (102) substrates by e-beam…
In this work, we report a strengthened superheating effect caused by a buffering YBa2Cu3Oy (Y123 or YBCO) layer in the Nd1+xBa2-xCu3O7-y (Nd123 or NdBCO) thin film with MgO substrate (i.e., NdBCO/YBCO/MgO thin film). In the cold-seeding…
The integration of high-temperature superconducting YBa2Cu3O6+x (YBCO) into flexible electronic devices has the potential to revolutionize the technology industry. The effective preparation of high-quality flexible YBCO films therefore…
We have studied a three-unit-cell-thick YBa2Cu3O7-x (YBCO) superconducting film grown on a slightly vicinal SrTiO3 substrate that was polished from the (001) plane by a small miscut angle (less than 0.5 degrees). This produced, on its…
Thin films of MgB2 superconductor were prepared by three different procedures on sapphire and silicon substrates. Boron thin films, ex-situ annealed in magnesium vapour, resulted in textured polycrystalline films with crystal dimensions…
Over the last decade advances in high temperature superconducting (HTS) materials have generated a renewed optimism in the use of this technology in future high-power applications including motors, generators, and power transmission. The…
A rapid decrease in the critical current density (Jc) of YBa2Cu3O7-x (YBCO) films with increasing film thickness has been observed for multiple YBCO growth processes. While such behavior is predicted from 2D collective pinning models under…
We have grown untwinned YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) films on (110) MgO substrates that were pre-annealed at high temperature in oxygen atmosphere. The annealing results in surface reconstruction with shallow facets, which induce the…
The fabrication of free-standing ultra-thin films from high-temperature (high-Tc) superconductors is of great interest for the development of superconducting nanowire single-photon detectors with high operating temperatures. We successfully…
Superconducting MgB2 thin films were prepared on 50-micrometer-thick, flexible polyamide Kapton-E foils by vacuum co-deposition of Mg and B precursors with nominal thickness of about 100 nm and a special ex-situ rapid annealing process in…
Materials of the Y-Ba-Cu-O (melt-textured YBa2Cu3O7-d-based materials or MT-YBCO) and Mg-B-O (MgB2-based materials) systems with high superconducting performance, which can be attained due to the formation of regularly distributed…
Superconducting MgB2 thin films were fabricated on Al2O3(0001) substrates under an ex-situ processing conditions. Boron thin films were deposited by pulsed laser deposition followed by a post-annealing process. Resistance measurements of…
We fabricated superconducting MgB2 thin films on (001) MgO substrates. The samples were prepared by magnetron rf and dc co-sputtering on heated substrates. They were annealed ex-situ for one hour at temperatures between 450{\deg}C and…
Superconducting MgB2 thin films were prepared on Al2O3(0001) and MgO(100) substrates. Boron thin films were deposited by the electron-beam evaporation followed by post-annealing process with magnesium. Proper post annealing conditions were…
Precursor MgB2 thin films were prepared on sapphire substrates by magnetron sputtering. Influence of ex-situ annealing process on superconducting MgB2 thin films roughness is discussed. Optimized annealing process of MgB precursor thin…
The competition of superconductivity and magnetism in superlattices composed of alternating YBa$_2$Cu$_3$O$_{7-d}$ and La$_{0.67}$Ca$_{0.33}$MnO$_{3}$ thin films is investigated using low-energy optical spectroscopy. The thickness of the…
We report on the growth and characterization of ultrathin YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) films on MgO (110) substrates, which exhibit superconducting properties at thicknesses down to 3 nm. YBCO nanowires, with thicknesses down to 10 nm…
YBCO films were successfully prepared on biaxially textured Ag{110}<211> substrates by using pulsed laser deposition. X-ray diffraction results showed that the degree of preferential orientation of Ag{110}<211> substrates varied with…
We report a detailed study performed on La2Zr2O7 (LZO) pyrochlore material grown by Metal-Organic Decomposition (MOD) method as buffer layers for YBa2Cu3O7-x (YBCO) coated conductors. High quality epitaxial LZO thin films have been obtained…