We succeeded in the synthesis of high-Jc MgB2 bulks via high energy ball-milling of elemental Mg and B powder at ambient temperatures. Alternatively to longtime mechanical alloying technique, the mixed powder was ball-milled for only 1h and…
We report the magnetic-field dependence of the irreversible magnetization of the recently discovered binary superconductor MgB$_{2}$. For the temperature region of $T< 0.9T_c$, the contribution of the bulk pinning to the magnetization…
The MgB2 bulks were prepared by high energy milling of Mg and B powder. The correlations among milling times, microstructure and superconducting properties were investigated in MgB2 bulks. Samples were characterized by x-ray diffraction…
Highly dense MgB2 policrystalline bulk materials, obtained by reactive liquid infiltration, have been characterized in their superconducting transport and magnetic properties in magnetic field and in a temperature range of interest for the…
Highly dense nanocrystalline MgB_2 bulk superconductors with distinctly improved pinning were prepared by mechanical alloying of Mg and B powders and hot compaction at ambient temperatures. The nanocrystalline samples reveal high critical…
High-density bulk materials of a newly discovered 40K intermetallic MgB2 superconductor were prepared by high pressure sintering. Superconducting transition with the onset temperature of 39K was confirmed by both magnetic and resistive…
We report on the results of a comparative investigation of highly dense bulk MgB$_2$ samples prepared by three methods: (i) hot deformation; (ii) high pressure sintering; and (iii) mechanical alloying of Mg and B powders with subsequent hot…
We have successfully prepared the MgB2 superconducting bulk and powdered materials by the method of combustion synthesis. The starting materials used in this study were powders of Mg and B. X-ray powder diffraction pattern was well assigned…
The magnetic field dependent critical current density $j_c(B)$ of a MgB$_2$ bulk sample has been obtained by means of magnetization hysteresis measurements. The $j_c(B)$ curves at different temperatures demonstrate a crossover from single…
We report results of dc magnetic and ac linear low-frequency study of a polycrystalline MgB$_2$ sample. AC susceptibility measurements at low frequencies, performed under dc fields parallel to the sample surface, provide a clear evidence…
We have developed disk-shaped MgB2 bulk superconducting magnets (20, 30 mm in diameter, 10 mm in thickness) using the in-situ process from Mg and B powders and evaluated the temperature dependence of trapped magnetic field. A pair of two…
The review considers bulk MgB2-based materials in terms of their structure, superconducting and mechanical properties. Superconducting transition temperatures of 34.5-39.4 K, critical current densities of 1.8-1.0 x E6 A/sq.cm in self field…
Superconducting $MgB_2$ wires in Cu, GlidCop or Monel sheath with Nb or Fe barrier are prepared. Wires vary by sheath material, number of superconducting cores and their chemical composition. Wires are HIP-ed (Hot Isostatic Pressing) at…
Superconducting MgB2 was synthesized in a stainless steel tube which compressed by pulsed magnetic field. The temperature dependence of diamagnetic moment m(T) was investigated and the pinning potential was determined
Holes drilled in a type-II superconductor trap the magnetic flux. Following Clem's flux pinning model, we consider surface pinning as a mechanism for compressing the magnetic flux in the holes. Estimations of the trapped magnetic flux…
Seven years after the discovery of superconductivity in magnesium diboride, the fundamental superconducting properties of this compound are well known and the peculiar current transport in polycrystalline materials is essentially…
High-resolution magneto-optical technique was used to analyze flux patterns in the intermediate state of bulk Pb samples of various shapes - cones, hemispheres and discs. Combined with the measurements of macroscopic magnetization these…
Two different hot isostatic pressing cycles (HIPing) were investigated to synthesize bulk MgB2 samples: a "standard" cycle where a low vessel pressure is maintained while heating to the process temperature with a subsequent simultaneous…
A slab in parallel field is submitted to a step-like magnetic-field excitation, of amplitude 1--10 G, in the same direction as the applied field. The slab has been rolled or spark cut, without special care, from a conventional…
We present electrical transport, magnetization, and specific heat measurements on bulk MgB2 samples (T_{c} = 38.5 K) synthesized under 200 MPa pressure using a process based on hot isostatic pressing with cooling under pressure. The samples…