A polycrystalline sample of the MgB_2 superconductor was investigated by measurements of the electrical resistivity, the thermopower and the thermal conductivity in the temperature range between 1.8K and 300K in zero magnetic field. The…
The discovery of superconductivity at 39 K in magnesium diboride offers the possibility of a new class of low-cost, high-performance superconducting materials for magnets and electronic applications. With twice the critical temperature of…
Considerable excitement has been caused recently by the discovery that the binary boride system with stoichiometry MgB2 is superconducting at the remarkably high temperature of 39 K (1). This potentially opens the way to even higher Tc…
The surface resistance (Rs) and the real part (sigma_1) of the microwave complex conductivity of a ~380 nm-thick polycrystalline MgB2 film with the critical temperature (Tc) of 39.3 K were investigated at ~8.5 GHz as a function of…
Superconducting MgB2 thin films were prepared on Al2O3(0001) and MgO(100) substrates. Boron thin films were deposited by the electron-beam evaporation followed by post-annealing process with magnesium. Proper post annealing conditions were…
MgB2 thin films were deposited using Pulsed Laser Deposition (PLD) and ex-situ annealing in Mg atmosphere. The films presented critical temperatures up to 36K and turned out to be preferentially c-oriented both on Al2O3 (r-cut) and MgO(100)…
The fabrication, characterisation, and superconductivity of MgB2 thick films grown on stainless steel substrate were studied. XRD, SEM, and magnetic measurements were carried out. It was found that the MgB2 thick films can be fast formed by…
Highly smooth and c-axis oriented superconducting MgB2 thin films were prepared by pulsed laser deposition (PLD) with off-axis geometry. The films were deposited on Al2O3-C substrates perpendicularly aligned to a stoichiometric MgB2 target…
Precursor MgB2 thin films were prepared on sapphire substrates by magnetron sputtering. Influence of ex-situ annealing process on superconducting MgB2 thin films roughness is discussed. Optimized annealing process of MgB precursor thin…
The structural, electronic, optical and thermodynamic properties of Mo2Ga2C are investigated using density functional theory (DFT) within the generalized gradient approximation (GGA). The optimized crystal structure is obtained and the…
The magnetic penetration depth, $\lambda^{-2}(T)$, in the basal plane of a magnesium diboride (MgB$_2$) film was measured using a two-coil mutual inductance technique at 50 kHz. This film has $T_c\simeq 38$ K, $\Delta T_c \leq 1$ K, and…
Superconductivity has been found in RuN films obtained by reactive magnetron sputtering. This is a novel member of the metal nitride superconductors family. The critical temperature of the superconducting transition varies depending on the…
We report the fabrication of MgB2 with bulk superconducting properties by conventional solid state methods at temperatures as low as 550 C. Mg deficiencies of the type Mg1-xB2 were tested. Tc was found to decrease by about 1K at large x,…
Far-infrared reflectance of a MgB2 film has been measured by Fourier-transform spectroscopy for frequencies 10 cm^{-1}<\nu <4000 cm^{-1} above and below the superconducting transition. The data provide clear experimental evidence for the…
The in situ annealing conditions of pulsed laser deposited MgB2 films were studied. The precursor films were deposited at 250 C from a stoichiometric MgB2 target in a 120mTorr Ar atmosphere. The films were then in situ annealed at a…
Thin superconducting films of magnesium diboride (MgB2) with Tc \approx 24K were prepared on various oxide substrates by pulsed laser deposition (PLD) followed by an in-situ anneal. A systematic study of the influence of various in-situ…
Ultrathin MgB2 superconducting films with a thickness down to 7.5 nm are epitaxially grown on (0001) Al2O3 substrate by hybrid physical-chemical vapor deposition method. The films are phase-pure, oxidation-free and continuous. The 7.5 nm…
Successful replacement of B by C in the series MgB2-xCx for values of x upto 0.3 are reported. Resistivity and ac susceptibility measurements have been carried out in the samples. Solubility of carbon, inferred from the observed change in…
We measured the reflectivity of the multifold semimetal RhSi in a frequency range from 80 to 20000 cm$^{-1}$ (10 meV - 2.5 eV) at temperatures down to 10 K. The optical conductivity, calculated from the reflectivity, is dominated by the…
Magnesium diboride has many intriguing characteristics, including its relatively high critical temperature and two-band nature. Most prior studies of MgB2 thin film Josephson junctions have been conducted above 2 Kelvin. We report results…