We report the first study of the optical conductivity of MgB2 covering the range of its superconducting energy gap. Terahertz time-domain spectroscopy is utilized to determine the complex, frequency-dependent conductivity of thin films. The…

Far-infrared reflectivity studies on the polycrystalline intermetallic compound MgB_2 with a superconducting transition temperature T_c=39 K were performed at temperatures 20 K to 300 K. We observe a significant raise of the…

Far-infrared reflectance of a MgB2 film has been measured by Fourier-transform spectroscopy for frequencies 10 cm^{-1}<\nu <4000 cm^{-1} above and below the superconducting transition. The data provide clear experimental evidence for the…

The complex conductivity of a MgB2 film has been investigated in the frequency range 4 cm^{-1}< nu < 30 cm^{-1} and for temperatures 2.7 K < T <300 K. The overall temperature dependence of both components of the complex conductivity is…

Temperature dependence of far-infrared transmission of NbN thin films deposited on MgO and Si substrates was measured at several frequencies from 0.4 up to 4.3 THz. Exponential increase of relative penetration depth at low temperatures and…

We have performed flux noise and AC-susceptibility measurements on two 400 nm thick MgB$_2$ films. Both measurement techniques give information about the vortex dynamics in the sample, and hence the superconducting transition, and can be…

Using mm-wave transmission we obtain information about both the real and imaginary part of the dielectric function of superconducting thin films. This is done by fitting the Fabry-Perot resonance spectrum for the film plus substrate over a…

Measurements of the far infrared magnetotransmission of YBa2(ZnxCu(1-x))3O(7-d) thin film (x = 0.025) deposited on a wedged MgO substrate are reported. The application of magnetic field perpendicular to the ab plane produces at low…

We investigate the influence of carbon-ion irradiation on the superconducting critical properties of MgB$_2$ thin films. MgB$_2$ films of two thicknesses viz. 400 nm (MB400nm) and 800 nm (MB800nm) were irradiated by 350 keV C ions having a…

We report measurements of the far infrared transmission of superconducting YBa$_2$Cu$_3$O$_{7-\delta }$ thin films from 5 cm$^{-1}$ to 200 cm$^{-1}$ in fields up to 14$T$. A Kramers-Kronig analysis of the magneto-transmission spectrum…

We present the technical details of a broadband microwave spectrometer for measuring the complex conductance of thin films covering the range from 50 MHz up to 16 GHz in the temperature range 300 mK to 6 K and at applied magnetic fields up…

We report the growth of high-quality c-axis-oriented epitaxial MgB2 thin films by using a pulsed laser deposition technique. The thin films grown on (1`1 0 2) Al2O3 substrates show a Tc of 39 K. The critical current density in zero field is…

Here we report an optical investigation in the terahertz region of a 40 nm ultrathin BaFe$_{1.84}$Co$_{0.16}$As$_2$ superconducting film with superconducting transition temperature T$_c$ = 17.5 K. A detailed analysis of the combined…

We studied the far-infrared reflectance of superconducting MgB2 in and out of equilibrium using pulsed synchrotron radiation. The equilibrium data can be described by a single energy gap at 2 Delta / hc = 43 cm-1. The fit improves slightly…

The effects of Al substitution and neutron irradiation on the conduction regime (clean or dirty) of the $\pi$- and $\sigma$-band of MgB$_{2}$ have been investigated by means of far-infrared spectroscopy. The intensity reflected by well…

Infrared absorption measurements in the range of 125 to 700 cm^(-1) have been carried out as a function of temperature upto 5 K in MgB2. The absorption spectrum is characterised by a broad band centred at 485 cm^{-1}, with shoulders at 333…

In high-quality c-axis-oriented MgB2 thin films, we observed high critical current densities (Jc) of 16 MA/cm^2 at 15 K under self fields comparable to those of cuprate high-temperature superconductors. The extrapolated value of Jc at 5 K…

We have analyzed about 100 voltage-dependent differential resistance dV/dI(V) curves of metallic point contacts between c-axis oriented MgB$_2$ thin film and Ag, which exhibit clear Andreev reflection features connected with the…

A MgB2 superconducting tape has been successfully prepared by a new way of boron diffusion into Mg tape. This tape superconductor has a Tc of 39 K with a sharp transition width of 0.4 K, high bulk critical current density jc of 6.7*10^5…

Temperature dependent optical conductivities and DC resistivity of c-axis oriented superconducting (Tc = 39.6 K) MgB2 films (~ 450 nm) have been measured. The normal state ab-plane optical conductivities can be described by the Drude model…