相关论文: Superconducting properties of MgB$_2$ probed by ra…
The effect of radiation-induced disordering in a nuclear reactor (fast neutrons fluence \Phi = 5\cdot10^{19} cm^2, T_{\text{irr}} = 340 K) on resistivity \rho, superconducting transition temperature T_C and upper critical field H_{C_2} of…
We studied the effect of disorder on the superconducting properties of polycrystalline MgB_2 by specific-heat measurements. In the pristine state, these measurements give a bulk confirmation of the presence of two superconducting gaps with…
We have studied the evolution of superconducting and normal state properties of neutron irradiated Mg(B$_{.962}$C$_{.038}$)$_2$ wire segments as a function of post exposure annealing time and temperature. The initial fluence fully…
The behavior of electrical resistivity rho(T), temperature of superconducting transition Tc, and upper critical field Hc2(T) of polycrystalline YNi2B2C after irradiation with thermal neutron and subsequent high-temperature isochronous…
Far-infrared reflectivity studies on the polycrystalline intermetallic compound MgB_2 with a superconducting transition temperature T_c=39 K were performed at temperatures 20 K to 300 K. We observe a significant raise of the…
In this letter we present the effect of neutron irradiation up to fluences of 3.9 1019 n/cm2 on the superconducting properties of MgB2. In order to obtain a disorder structure homogeneously distributed, the experiment was carried out on…
NMR line shift and nuclear spin-lattice relaxation rate T_1^{-1} of 11B and 25Mg were measured in superconducting MgB_2 (T_c^{ons}=38K) structurally disordered by nuclear reactor neutrons up to the fluence of thermal neutrons $\Phi=1…
We report synthesis, structure/micro-structure, resistivity under magnetic field [R(T)H], Raman spectra, thermoelectric power S(T), thermal conductivity K(T), and magnetization of ambient pressure argon annealed polycrystalline bulk samples…
Considerable excitement has been caused recently by the discovery that the binary boride system with stoichiometry MgB2 is superconducting at the remarkably high temperature of 39 K (1). This potentially opens the way to even higher Tc…
We have performed a systematic study of the evolution of the superconducting and normal state properties of neutron irradiated MgB$_2$ wire segments as a function of fluence and post exposure annealing temperature and time. All fluences…
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…
A polycrystalline sample of the MgB_2 superconductor was investigated by measurements of the electrical resistivity, the thermopower and the thermal conductivity in the temperature range between 1.8K and 300K in zero magnetic field. The…
The review considers bulk MgB2-based materials in terms of their structure, superconducting and mechanical properties. Superconducting transition temperatures of 34.5-39.4 K, critical current densities of 1.8-1.0 x E6 A/sq.cm in self field…
We synthesized single crystalline and policrystalline MgB_2 under ambient pressures. The single crystals of MgB_2 were of good quality, where the crystal structure refinements were successfully converged with R = 0.020. The specific heat of…
A single crystal of isovalently substituted Ba(Fe$_{1-x}$Ru$_{x}$)$_2$As$_2$ ($x=0.24$) was sequentially irradiated with 2.5 MeV electrons up to a maximum dose of $2.1 \times 10^{19}$ electrons/cm^2. The electrical resistivity was measured…
The superconducting phase diagram of MgB2 was determined from magnetization, magneto-transport and the first single-crystal specific heat measurements. A zero-temperature in-plane coherence length of 8 nm is determined. The superconducting…
The effects of neutron irradiation on normal state and superconducting properties of epitaxial magnesium diboride thin films are studied up to fluences of 1020 cm-2. All the properties of the films change systematically upon irradiation.…
Growth of carbon substituted magnesium diboride Mg(B1-xCx)2 single crystals with 0<x<0.15 is reported and the structural, transport, and magnetization data are presented. The superconducting transition temperature decreases monotonically…
We report specific heat measurements in neutron irradiated MgB2 samples, for which the critical temperature has been suppressed down to 8.5 K, but the superconducting transition remains extremely sharp, indicative of a defect structure…
A relatively high critical temperature, Tc, approaching 40 K, places the recently-discovered superconductor magnesium diboride (MgB2) intermediate between the families of low- and copper-oxide-based high-temperature superconductors (HTS).…