Edge-TCT and charge collection measurements with passive test structures made in LFoundry 150 nm CMOS process on p-type substrate with initial resistivity of over 3 k$\Omega$cm are presented. Measurements were made before and after…
In this paper results of Edge-TCT and I-V measurements with passive test structures made in LFoundry 150 nm HV-CMOS process on p-type substrates with different initial resistivities ranging from 0.5 to 3 k$\Omega$cm are presented. Samples…
The unique electrical and material properties of 4H-silicon-carbide (4H-SiC) make it a promising candidate material for high rate particle detectors. In contrast to the ubiquitously used silicon (Si), 4H-SiC offers a higher carrier…
Several thin Low Gain Avalanche Detectors from Hamamatsu Photonics were irradiated with neutrons to different equivalent fluences up to $\Phi_{eq}=3\cdot10^{15}$ cm$^{-2}$. After the irradiation they were annealed at 60$^\circ$C in steps to…
Charge multiplication (CM) in p$^+$n epitaxial silicon pad diodes of 75, 100 and 150 $\upmu$m thickness at high voltages after proton irradiation with 1 MeV neutron equivalent fluences in the order of $10^{16}$ cm$^{-2}$ was studied as an…
Silicon carbide (SiC) is a wide band gap semiconductor and an attractive candidate for applications in harsh environments such as space, fusion, or future high luminosity colliders. Due to the large band gap, the leakage currents in SiC…
Due to the increased commercial availability, wide-bandgap semiconductors and their radiation hardness have recently received increased interest from the particle physics community. 4H-Silicon Carbide (SiC), especially, is an attractive…
To face the higher levels of radiation due to the 10-fold increase in integrated luminosity during the High-Luminosity LHC, the CMS detector will replace the current Calorimeter Endcap (CE) using the High-Granularity Calorimeter (HGCAL)…
A monolithic silicon pixel prototype produced for the MONOLITH ERC Advanced project was irradiated with 70 MeV protons up to a fluence of 1 x 10^16 1 MeV n_eq/cm^2. The ASIC contains a matrix of hexagonal pixels with 100 {\mu}m pitch,…
The quadrant silicon detector, a kind of passivated implanted planar silicon detector with quadrant structure on the junction side, gained its wide application in charged particle detection. In this paper, the manufacturing procedure,…
Samples of the monolithic silicon pixel ASIC prototype produced in 2022 within the framework of the Horizon 2020 MONOLITH ERC Advanced project were irradiated with 70 MeV protons up to a fluence of 1 x 1016 neq/cm2, and then tested using a…
This paper presents the possibility of using very thin Low Gain Avalanche Diodes (LGAD) ($25 - 50\mu$m thick) as tracking detector at future hadron colliders, where particle fluence will be above $10^{16}\; n_{eq}/cm^2$. In the present…
Low Gain Avalanche Detectors (LGADs) are silicon sensors with a built-in charge multiplication layer providing a gain of typically 10 to 50. Due to the combination of high signal-to-noise ratio and short rise time, thin LGADs provide good…
A method is presented which allows to obtain the position-dependent electric field and charge density by fits to velocity profiles from edge-TCT data from silicon strip-detectors. The validity and the limitations of the method are…
Charge collection properties of depleted CMOS pixel detector prototypes produced on p-type substrate of 2 k$\Omega$cm initial resistivity (by LFoundry 150 nm process) were studied using Edge-TCT method before and after neutron irradiation.…
Neutron bombardments with equivalent fluence (1$\times$10$^{10}$ cm$^{-2}$) and different fluxes ($2.5\times$10$^5$ cm$^{-2}$s$^{-1}$ to $1\times$10$^7$ cm$^{-2}$s$^{-1}$) have been performed on three kinds of bipolar devices with n-type…
Low Gain Avalanche Detectors (LGAD) are based on a n++-p+-p-p++ structure where an appropriate doping of the multiplication layer (p+) leads to high enough electric fields for impact ionization. Gain factors of few tens in charge…
Using multi-channel time-resolved current measurements (multi TCT), the charge collection of p+n silicon strip sensors for electron-hole pairs produced close to the Si-SiO2 interface by a focussed sub-nanosecond laser with a wavelength of…
The degradation of signal in silicon sensors is studied under conditions expected at the CERN High-Luminosity LHC. 200 $\mu$m thick n-type silicon sensors are irradiated with protons of different energies to fluences of up to $3 \cdot…
The collection of charge carriers generated in p+n strip sensors close to the Si-SiO2 interface before and after 1 MGy of X-ray irradiation has been investigated using the transient current technique with sub-nanosecond focused light pulses…