A C14 Nb0.975Fe2.025 Laves phase compound was investigated aimed at determining the H-T magnetic phase diagram. Magnetization, M, and AC magnetic susceptibility measurements were performed. Concerning the former field-cooled and…
C14 Laves phase Nb0.975Fe2.025 compound was investigated by means of the M\"ossbauer spectroscopy. Spectra were recorded in the temperature range of 5-300K. Their analysis in terms of three sub spectra yielded information on magnetic and…
Magnetization measurements were carried out in the in field-cooled (FC) and in zero-field-cooled (ZFC) conditions versus temperature, T, and external magnetic field, H, on a sigma-phase Fe47Mo53 compound. Analysis of the measured M_FC and…
Magnetization measurements have been performed on single-crystalline Fe$_{1.1}$Te in pulsed magnetic fields $\mathbf{H}\perp\mathbf{c}$ up to 53 T and temperatures from 4.2 to 65 K. At $T=4.2$ K, a non-reversible reorientation of the…
The magnetic properties and magnetocaloric effect of an intermetallic compound $\mathrm{Er_2Rh_3Si}$ was investigated by performing temperature dependence of dc- and ac-magnetic susceptibility and isothermal magnetizations. Polycrystalline…
Magnetic properties of $M_{c}$Ta$_{2}$S$_{2}$C ($M$ = Fe, Co, Ni, Cu) have been studied using SQUID DC and AC magnetic susceptibility. In these systems magnetic $M^{2+}$ ions are intercalated into van der Waals gaps between adjacent S…
Sigma-phase intermetallic compound of Fe54Cr46 was investigated using DC and AC magnetic susceptibility techniques. A clear-cut evidence was found that the sample orders magnetically at Tc=23.5 K and its ground magnetic state is constituted…
Sigma-phase Fe47Re53 compound was investigated by means of in-field DC and AC magnetization measurements. Field cooled, MFC, and zero-field cooled, MZFC, DC magnetization curves were recorded in the magnetic field, H, up to 1000 Oe. AC…
The measurements of the magnetic susceptibility, magnetization, electrical resistivity and magnetoresistance have been performed for the Fe intercalated compound Fe0.5TiS2. According to X-ray diffraction measurements the Fe0.5TiS2 compound…
We have performed magnetization measurements at high magnetic fields of up to 53 T on single crystals of a uranium heavy-fermion compound U$_2$Zn$_{17}$ grown by the Bridgman method. In the antiferromagnetic state below the N\'{e}el…
In-field DC and AC magnetization measurements were carried out on a sigma-phase Fe55Re45 intermetallic compound aimed at determination of the magnetic phase diagram in the H-T plane. Field cooled, M_FC, and zero-field cooled, M_ZFC, DC…
Magnetic response of uranium dioxide (UO2) has been investigated through temperature and magnetic field dependent dc magnetization measurements. UO2 is a paramagnet at room temperature. The magnetic susceptibility, however, deviates from…
Zero-field-cooled (ZFC) and field-cooled (FC) magnetization along with ac-magnetization vs. temperature and m-h loop measurements are reported for two series of ion-beam sputtered Fe-Cr GMR multilayers where the interface roughness is…
We have measured the magnetization and specific heat of multiferroic CoCr2O4 in magnetic fields up to 14 T. The high-field magnetization measurements indicate a new phase transition at T* = 5 - 6 K. The phase between T* and the lock-in…
We report magnetization and specific heat measurements in the 2D frustrated spin-1/2 Heisenberg antiferromagnet Cs2CuCl4 at temperatures down to 0.05 K and high magnetic fields up to 11.5 T applied along a, b and c-axes. The low-field…
The intermetallic compound SmMn$_2$Ge$_2$, displaying multiple magnetic phase transitions, is being investigated in detail for its magnetization behavior near the 145 K first order ferromagnetic to antiferromagnetic transition occuring on…
We have studied the magnetization and magnetoresistance of CeRu2Al10 in the applied magnetic field H along the c-axis up to ~ 55 T. The magnetization M at low temperatures shows an H-linear increase with a small slope of M/H than that for H…
We report the magnetization, specific heat and transport measurements of high quality Na$_{0.85}$CoO$_2$ single crystals in applied magnetic fields up to 14T. In high temperatures, the system is in a paramagnetic phase. It undergoes a…
Detailed magneto-transport data on dense wires of $MgB_2$ are reported for applied magnetic fields up to 18 T. The temperature and field dependencies of the electrical resistivity are consistent with $MgB_2$ behaving like a simple metal and…
Magnetic phases for the intermetallic compound NdMn1.4Co0.6Si2 have been investigated at various temperatures by dc magnetization, neutron diffraction and neutron depolarization. Our study shows multiple magnetic phase transitions with…