相关论文: Growth of bulk single-crystal MnP helimagnet and i…
Bulk single crystals of manganese arsenide (MnAs) were grown from melt at 1 GPa and 1100 {\deg}C by using a cubic-anvil, high-pressure, and high-temperature technique. The as-grown black colored crystals extracted from solidified lump…
(Mn,Fe)2(P,Si) single crystals have been successfully grown by flux method. Single crystal diffraction demonstrates that Mn0.83Fe1.17P0.72Si0.28 crystallizes in a hexagonal crystal structure (space group P-62m) at both 100 and 280 K, in the…
Single crystals of MgB2 have been grown with a high-pressure cubic anvil technique. They grow via the peritectic decomposition of the MgNB9 ternary nitride. The crystals are of a size up to 2x1x0.1mm3 with a weight up to 230 micrograms.…
Transparent and colorless hexagonal boron nitride (hBN) single crystals were grown from the Mg-B-N system using high-pressure high-temperature cubic anvil technique. By varying the synthesis conditions we could determine the sequence of…
Single crystals of MgB2 with a size up to 1.5x0.9x0.2 mm3 have been grown with a high pressure cubic anvil technique. The crystal growth process is very peculiar and involves an intermediate nitride, namely MgNB9. Single crystals of BN and…
We explore strain-modulated helimagnetism in highly crystalline MnP nanorod films grown on Si(100) substrates using molecular beam epitaxy. The strained MnP film exhibits a paramagnetic to ferromagnetic (PM-FM) phase transition at TC ~ 279…
Single crystals of MgB2 have been grown at high pressure via the peritectic decomposition of MgNB9. The crystals are of a size up to 1.5x0.9x0.2 mm3 with a weight up to 0.23 mg, and typically have transition temperatures between 37 and 39…
ZrMnP and HfMnP single crystals are grown by a self-flux growth technique and structural as well as temperature dependent magnetic and transport properties are studied. Both compounds have an orthorhombic crystal structure. ZrMnP and HfMnP…
Bulk single crystals of SrPt3P have been grown for the first time by a self-flux method at 2 GPa and 1500 {\deg}C using the cubic-anvil, high-pressure and high-temperature technique. The grown black crystals were found to have either a…
We report an optimized chemical vapor transport method, which allows growing FeP single crystals up to 500 mg in mass and 80 $mm^{3}$ in volume. The high quality of the crystals obtained by this method was confirmed by means of EDX,…
We report on the crystal and magnetic structures, magnetic, and transport properties of SrMnSb$_2$ single crystals grown by the self-flux method. Magnetic susceptibility measurements reveal an antiferromagnetic (AFM) transition at $T_{\rm…
We report the growth of mm-sized Pmnb-Li2FeSiO4 single crystals by means of the optical floating-zone method at high argon pressure and describe the conditions required for a stable growth process. The crystal structure is determined and…
Mm-sized LiMn$_{1-x}$Fe$_x$PO$_4$ single crystals with $0\leq x \leq 1$ were grown by means of the traveling floating-zone technique at elevated Argon pressure of 30~bar. For the various doping levels, the growth process was optimized with…
Superconducting whisker like and bulk single crystals of PrFeAs(O,F) were grown at 3 GPa and 1500 C from NaAs flux using the cubic anvil high pressure and high temperature technique. The ribbon shaped whisker like crystals were 400-1300…
Neutron powder diffraction studies of the crystal and magnetic structures of the magnetocaloric compound Mn1.1Fe0.9(P0.8Ge0.2) have been carried out as a function of temperature, applied magnetic field, and pressure. The data reveal that…
HoFe1-xMnxO3 (0 < x < 1) single crystals have been grown by the optical floating zone technique. A structural transition from the orthorhombic to hexagonal modification has been established in the crystals in the concentration range of…
We report an optimized chemical vapor transport method to grow single crystals of (Mn$_{1-x}$Ni$_x$)$_2$P$_2$S$_6$ where x = 0, 0.3, 0.5, 0.7 & 1. Single crystals up to 4\,mm\,$\times$\,3\,mm\,$\times$\,200\,$\mu$m were obtained by this…
Millimeter size single crystals of double perovskite La2NiMnO6 (LNMO) were grown by the High Temperature Solution Growth Method. The magnetic measurements and polarized Raman spectra between 5 and 350K provide evidence that the crystals…
Compounds based on the Fe2P structure have continued to attract interest because of the interplay between itinerant and localized magnetism in a non-centrosymmetric crystal structure, and because of the recent developments of these…
By varying the parameters controlling the growth of crystals, including the thermodynamic variables, such as temperature, pressure, and reagent composition and the kinetic factors, namely reaction time and cooling rate, we found the most…