Improving transport current has been the primary issue for practical application of superconducting wires and tapes. However, the porous nature of powder-in-tube (PIT) processed iron-based superconducting tapes is thought to be one of the…
The high upper critical field and low anisotropy of iron-based superconductors make them being particularly attractive for high-field applications. However, the current carrying capability needs to be enhanced by overcoming the weak-link…
From the application point of view, large critical current densities Jc (H) for superconducting wires are required, preferably for magnetic fields higher than 5 T. Here we show that strong c-axis textured Sr1-xKxFe2As2 tapes with nearly…
We report the realization of grain alignment in Sn-added Sr1-xKxFe2As2 superconducting tapes prepared by ex-situ powder-in-tube method. At 4.2 K, high transport critical current densities Jc of 2.5x10^4 A/cm^2 (Ic = 180 A) in self-field and…
We report significant transport critical currents firstly achieved in Sr0.6K0.4Fe2As2 wires and tapes with a Tc = 34 K, which were fabricated through an in-situ powder-in-tube process. Silver was used as a chemical addition as well as a…
We found that transport critical current density (Jc) of the Ba1-xKxFe2As2/Ag tapes is significantly enhanced by the combination process of cold flat rolling and uniaxial pressing. At 4.2 K, the Jc reaches a high value of 9.1x104 A/cm2 in 4…
Iron-based superconductors have been considered to be very promising in high-field applications, for which multifilamentary wire and tape conductors with high mechanical strength are essential. In this work, 7-,19- and 114-filament…
High-performance Sr0.6K0.4Fe2As2 (Sr-122) tapes have been successfully fabricated using hot pressing (HP) process. The effect of HP temperatures (850-925 C) on the c-axis texture, resistivity, Vickers micro-hardness, microstructure and…
We report the temperature dependence of the transport critical current density (Jc) in textured Sr1-xKxFe2As2/Fe (Sr122) tapes fabricated by an ex situ powder-in-tube process. Critical currents were measured in magnetic fields up to 0-15 T…
(Ba,K)Fe2As2 superconducting wires and tapes are fabricated by using hot isostatic pressing (HIP) technique, and their superconducting properties are studied. In the HIP round wire, transport critical current density (Jc) at 4.2 K has…
We found that the transport Jc of the ex-situ PIT processed (Ba,K)Fe2As2 (Ba-122) wire with single Ag sheath can be significantly enhanced by repeating the combined process of rolling and heat treatment. The transport Jc (4.2 K and 10 T) of…
The industrial manufacturing of the long-length iron-pnictide wires and tapes requires simple and low-cost technology. Although the transport critical current density of the FeAs-122 tapes has already achieved the practical application…
The paper reports the first successful fabrication of MgB2 superconducting tape using a flexible metallic substrate as well as its strong pinning force, which was verified by direct measurement of transport critical current density. The…
Copper sheath is the first choice for manufacturing high-Tc superconducting wires and tapes because of its high electrical and thermal conductivities, low cost and good mechanical properties. However, Cu can easily react with…
Conventional powder-in-tube (PIT) method has been the most effective technique for fabricating iron-based superconducting wires and tapes. Tremendous advances have been made during the last few years, especially for 122 family pnictide…
High temperature (high-Tc) superconductors like cuprates have superior critical current properties in magnetic fields over other superconductors. However, superconducting wires for high-field-magnet applications are still dominated by…
Iron-pnictides are hotly studied since 2008 in the superconducting materials research area, due to their special properties and unclear mechanism. Big achievement has been made in the pnictide research during the past years. For practical…
We report on the preparation of dense monofilamentary MgB2/Ni and MgB2/Fe tapes with high critical current densities. In annealed MgB2/Ni tapes, we obtained transport critical current densities as high as 2.3*105 A/cm2 at 4.2 K and 1.5 T,…
Nowadays the development of high-field magnets strongly relies on the performance of superconducting materials. Iron-based superconductors exhibit high upper critical fields and low electromagnetic anisotropy, making them particularly…
Iron-based superconductors, with Tc values up to 55 K, are of great interest for applications, due to their lower anisotropies and ultrahigh upper critical fields. In the past 4 years, great progress has been made in the fabrication of…