相关论文: A 57Fe M\"ossbauer Study Of Local Structure And Sp…
Detailed 57Fe Mossbauer spectroscopy measurements on superconducting NaFeAs powder samples have been performed in the temperature range 13 K < T < 300 K. The 57Fe spectra recorded in the paramagnetic range (T > TN ~ 46 K) were discussed…
We report new results of a 57Fe M\"ossbauer study of multiferroic 3R-AgFeO2 powder samples performed in a wide temperature range, including two points, TN1 ~ 14 K and TN2 ~ 9 K, of magnetic phase transitions. At the intermediate temperature…
57Fe Moessbauer spectroscopy was applied to investigate the superconductor parent compound Fe(1+x)Te for x=0.06, 0.10, 0.14, 0.18 within the temperature range 4.2 K - 300 K. A spin density wave (SDW) within the iron atoms occupying regular…
The paper reports new results of the 57Fe M\"ossbauer measurements on Fe3PO4O3 powder sample recorded at various temperatures including the point of magnetic phase transition TN ~ 163K. The spectra measured above TN consist of quadrupole…
57Fe-M\"ossbauer studies of superconducting Rb0.8Fe1.6Se2.0 with TC = 32.4 K were performed on single-crystalline and polycrystalline samples in the temperature range 4.2 K to 295 K. They reveal the presence of 88% magnetic and 12%…
The structural and magnetic phase transitions of the ternary iron arsenides SrFe2As2 and EuFe2As2 were studied by temperature-dependent x-ray powder diffraction and 57-Fe Moessbauer spectroscopy. Both compounds crystallize in the tetragonal…
We report results of 57Fe Mossbauer and 31P NMR studies of a phosphide FeP powder sample performed in a wide temperature range including the point (TN ~ 120 K) of magnetic phase transitions. The 57Fe Mossbauer spectra at low temperatures T…
With the advent of Fe-As based superconductivity it has become important to study how superconductivity manifests itself in details of 57Fe Mossbauer spectroscopy of conventional, Fe - bearing superconductors. To this end, the iron-based…
$^{57}$Fe M\"ossbauer spectroscopy can probe several \emph{local} structural, electronic and magnetic properties of Fe-containing systems. However, to establish a direct relationship between these properties and a system's geometric…
The EuFe(2-x)Ni(x)As2 compounds exhibiting 3d and/or 4f magnetic order were investigated by means of 57Fe and 151Eu M\"ossbauer spectroscopy. Additionally, results for the end members of this system, i.e. EuFe2As2 and EuNi2As2, are reported…
$^{57}$Fe M\"ossbauer spectra at different temperatures between $\sim 5$ K and $\sim 300$ K were measured on an oriented mosaic of single crystals of CaKFe$_4$As$_4$ . The data indicate that CaKFe$_4$As$_4$ is a well formed compound with…
57Fe Mossbauer spectroscopy was used to perform a microscopic study on the extremely pressure and strain sensitive compound, CaFe2As2, with different degrees of strain introduced by grinding and annealing. At the base temperature, in the…
We report measurements of 57Fe Mossbauer spectra for RFe2Zn20 ( R = Lu, Yb, Gd) from ~ 4.5 K to room temperature. The obtained isomer shift values are very similar for all three compounds, their temperature dependence was analyzed within…
Iron-titanium sulfides FeTi2S4 and Fe2TiS4 have been structurally and magnetically characterized using powder X Ray Diffraction with Rietveld refinement method and 57Fe M\"ossbauer spectroscopy at variable temperature. Both sulfides have…
The chromium arsenides BaCr2As2 and BaCrFeAs2 with ThCr2Si2 type structure (space group I4/mmm; also adopted by '122' iron arsenide superconductors) have been suggested as mother compounds for possible new superconductors. DFT-based…
Two iron-chalcogenide superconductors Li(x)[C5H5N](y)Fe(2-z)Se2 and Cs(x)Fe(2-z)Se2 in the as-prepared and annealed state have been investigated by means of the Moessbauer spectroscopy versus temperature. Multi-component spectra are…
A new oxide, sodium iron antimonate, Na2FeSbO5, was synthesized and structurally characterized, and its static and dynamic magnetic properties were comprehensively studied both experimentally by dc and ac magnetic susceptibility,…
The new quaternary iron arsenide-fluoride SrFeAsF with the tetragonal ZrCuSiAs-type structure was synthesized and the crystal structure was determined by X-ray powder diffraction (P4/nmm, a = 399.30(1), c = 895.46(1) pm). SrFeAsF undergoes…
We present results from a detailed experimental investigation of LaFeAsO, the parent material in the series of "FeAs" based oxypnictide superconductors. Upon cooling this material undergoes a tetragonal-orthorhombic crystallographic phase…
Iron-based superconductors Ba0.7Rb0.3Fe2As2 and CaFe1.92Co0.08As2 of the '122' family have been investigated by means of the 14.41-keV Moessbauer transition in 57Fe versus temperature ranging from the room temperature till 4.2 K. A…