相关论文: Development of Powder-in-Tube Processed Iron Pnict…

Iron-based superconductors, with Tc values up to 55 K, are of great interest for applications, due to their lower anisotropies and ultrahigh upper critical fields. In the past 4 years, great progress has been made in the fabrication of…

Conventional powder-in-tube (PIT) method has been the most effective technique for fabricating iron-based superconducting wires and tapes. Tremendous advances have been made during the last few years, especially for 122 family pnictide…

We report significant transport critical currents firstly achieved in Sr0.6K0.4Fe2As2 wires and tapes with a Tc = 34 K, which were fabricated through an in-situ powder-in-tube process. Silver was used as a chemical addition as well as a…

We report large transport critical current densities observed in Ag-added (Ba,K)Fe2As2 superconducting wires prepared by an ex-situ powder-in-tube (PIT) process. The wire has a simple composite structure sheathed only by Ag. A precursor…

The recent discovery of superconductivity in the iron based superconductors with very high upper critical fields presents a new possibility for practical applications, but fabricating fine-wire is a challenge because of mechanically hard…

Improving transport current has been the primary issue for practical application of superconducting wires and tapes. However, the porous nature of powder-in-tube (PIT) processed iron-based superconducting tapes is thought to be one of the…

We found that the transport Jc of the ex-situ PIT processed (Ba,K)Fe2As2 (Ba-122) wire with single Ag sheath can be significantly enhanced by repeating the combined process of rolling and heat treatment. The transport Jc (4.2 K and 10 T) of…

Seven-core Ag/Fe sheathed Sr0.6K0.4Fe2As2 (Sr-122) superconducting wires were produced by the ex situ powder-in-tube (PIT) method. The relationship between the cold-work deformation process and the superconducting properties of wires were…

In this work, the feasibility condition of Powder-In-Tube (PIT) processed wires of Fe(Se,Te) superconductor has been investigated. We faced several technical issues that are extensively described and discussed. In particular, we tested…

We report that high transport critical current density exceeding 104 A/cm2 at 4.2 K and 10 T can be obtained with good reproducibility for Ag sheathed (Ba,K)Fe2As2 (Ba 122) tapes by modifying the ex-situ powder-in-tube (PIT) method. The…

122 type pnictide superconductors are of particular interest for high-field applications because of their large upper critical fields Hc2 (> 100 T), low Hc2 anisotropy r (< 2), and high thin-film critical current densities Jc (> 1 MA/cm2 at…

Copper sheath is the first choice for manufacturing high-Tc superconducting wires and tapes because of its high electrical and thermal conductivities, low cost and good mechanical properties. However, Cu can easily react with…

Among the recently discovered Fe-based superconducting compounds, the (K,Ba)Fe2As2 phase is attracting large interest within the scientific community interested in conductor developments. In fact, after some years of development, critical…

We have fabricated (Ba,K)Fe2As2 superconducting wires through ex-situ powder-in-tube method. Silver was used as a chemical addition to improve the performance of these superconducting wires. The transport critical current densities (Jc)…

Nb-sheathed Sr0.6K0.4Fe2As2 superconducting wires have been fabricated using the powder-in-tube (PIT) method for the first time and the superconducting properties of the wires have been investigated. The transition temperature (Tc) of the…

The Powder-In-Tube process has been employed to fabricate tape-like conductors with a strong metallic sheath and based on the newly discovered MgB2 superconducting phase. Long superconducting tapes have been prepared by packing reacted MgB2…

FeTe0.5Se0.5 superconducting wires have been fabricated using ex-situ PIT method with an Fe sheath. Among the other FeAs-based superconductor, FeTe0.5Se0.5 has great advantage for application due to binary composition and less toxic.…

We demonstrate that Fe sheathed LaO0.9F0.1FeAs wires with Ti as a buffer layer were successfully fabricated by the powder-in-tube (PIT) method. Comparing to the common two-step vacuum quartz tube synthesis method, the PIT method is more…

The industrial manufacturing of the long-length iron-pnictide wires and tapes requires simple and low-cost technology. Although the transport critical current density of the FeAs-122 tapes has already achieved the practical application…

Mono- and multifilamentary MgB2/Fe tapes and wires with high transport critical current densities have been prepared using the powder-in-tube (PIT) process. The fabrication details are described. The effect of powder grain sizes and…