相关论文: Kondo behavior, ferromagnetic correlations, and cr…
The compound Ce3Co4Sn13 is an extremely heavy cubic heavy fermion system with a low temperature electronic specific heat of order ~4 J/mol-K2. If the compound is nonmagnetic, it would be one of the heaviest nonmagnetic Ce-based heavy…
Inelastic neutron scattering experiments have been carried out to determine the crystal field states of the Kondo lattice heavy fermions CeRuSn3 and CeRhSn3. Both the compounds crystallize in LaRuSn3-type cubic structure (space group Pm-3n)…
We have grown the single crystals of CeMg$_3$ and its non-magnetic analogue LaMg$_3$, which crystallize in the cubic crystal structure with the space group \textit{Fm\rm{\={3}}m}, and studied their magnetic properties on well oriented…
We have performed an inelastic neutron scattering study of the low energy spin dynamics of the heavy fermion compound Ce0.8La0.2Al3 as a function of temperature and external pressure up to 5 kbar. At temperatures below 3 K, the magnetic…
We have performed magnetic susceptibility, specific heat, resistivity, and inelastic neutron scattering measurements on a single crystal of the heavy Fermion compound Ce(Ni$_{0.935}$Pd$_{0.065}$)$_2$Ge$_2$, which is believed to be close to…
In this study we report the results of study of novel ternary $Np_2PtGa_3$ compound. The x-ray-powder diffraction analysis reveals that the compound crystallizes in the orthorhombic CeCu$_2$-type crystal structure (space group Imma) with…
We have measured the crystalline electric field (CEF) excitations of the CeMIn5 (M = Co, Rh, Ir) series of heavy fermion superconductors by means of inelastic neutron scattering. Fits to a CEF model reproduce the inelastic neutron…
The microscopic theory of interaction between the heavy fermions and the crystal field excitations in Kondo lattices is presented. It is shown that the heavy-fermion spectrum scaled by the Kondo temperature $T_K$ can be modified by the…
Magnetization, heat capacity, electrical resistivity, thermoelectric power, and Hall effect have been investigated on single-crystalline Ce_2PdSi_3. This compound is shown to order antiferromagnetically below N'eel temperature (T_N) \~3 K.…
Physical properties of polycrystalline CeCrGe$_{3}$ and LaCrGe$_{3}$ have been investigated by x-ray absorption spectroscopy, magnetic susceptibility $\chi(T)$, isothermal magnetization M(H), electrical resistivity $\rho(T)$, specific heat…
We report the thermodynamic, magnetic, and electronic transport properties of the new ternary intermetallic system (Ce,La)3Pt4In13. Ce3Pt4In13 orders antiferromagnetically at 0.95 K while the non-magnetic compound La3Pt4In13 is a…
Inelastic neutron scattering investigation on ferromagnetic Kondo lattice compounds belonging to CeSi_{2-x}Ga_{x}, x = 0.7, 1.0 and 1.3, system is reported. The thermal evolution of the quasielastic response shows that the Kondo…
Inelastic neutron scattering experiments were performed on single crystals of the heavy-fermion compound CeIn$_{3}$ for temperatures below and above the N\'eel temperature, $T_N$. In the antiferromagnetically ordered phase, well-defined…
Heavy fermions represent an archetypal example of strongly correlated electron systems which, due to entanglement among different interactions, often exhibit exotic and fascinating physics involving Kondo screening, magnetism and…
We report inelastic neutron scattering experiments on a single crystal of the intermediate valence compound CePd3. At 300 K the magnetic scattering is quasielastic, with halfwidth of 23 meV, and is independent of momentum transfer Q. At low…
We have measured the electrical resistivity of cerium monochalcogenices, CeS, CeSe, and CeTe, under high pressures up to 8 GPa. Pressure dependences of the antiferromagnetic ordering temperature $T_{N}$, crystal field splitting, and the…
Inelastic neutron scattering experiment has been performed on a new heavy fermion compound YbAgGe for a polycrystalline sample at zero magnetic field. A quasielastic scattering and a crystal field excitation at 12 meV was observed. Both of…
A large, strongly temperature-dependent Nernst coefficient, $\nu$, is observed between $T$ = 2 K and 300 K for CeCu$_2$Si$_2$ and Ce$_{0.8}$La$_{0.2}$Cu$_2$Si$_2$. The enhanced $\nu(T)$ is determined by the asymmetry of the on-site Kondo…
The filled skutterudite compound SmOs_{4}Sb_{12} was prepared in single crystal form and characterized. The SmOs_{4}Sb_{12} crystals have the LaFe_{4}P_{12}-type structure with lattice parameter a = 9.3085 Angstroms. Specific heat…
We report systematic studies of CeCu$_9$In$_2$, which appears to be a new Kondo lattice system. Electrical resistivity exhibits a logarithmic law characteristic of Kondo systems with a broad maximum at $T_{coh}\approx$45 K and it obeys the…