The in-plane resistivity $\rho$ and thermal conductivity $\kappa$ of extremely overdoped KFe$_2$As$_2$ ($T_c$ = 3.0 K) single crystal were studied. It is found that $\rho \sim T^{1.5}$ at low temperature, a typical non-Fermi liquid behavior…

The thermal conductivity of iron-based superconductor CsFe$_2$As$_2$ single crystal ($T_c =$ 1.81 K) was measured down to 50 mK. A significant residual linear term $\kappa_0/T$ = 1.27 mW K$^{-2}$ cm$^{-1}$ is observed in zero magnetic…

The in-plane thermal conductivity of iron-based superconductor RbFe$_2$As$_2$ single crystal ($T_c \approx$ 2.1 K) was measured down to 100 mK. In zero field, the observation of a significant residual linear term $\kappa_0/T$ = 0.65 mW…

In a recent Letter [J. K. Dong et al., Phys. Rev. Lett. 104, 087005 (2010)], Dong \textit{et al}. have observed a $T^{1.5}$ dependence of resistivity $\rho$ in KFe$_2$As$_2$ at the upper critical field $B_{c2}$ = 5 T parallel to the c axis…

The thermal conductivity $\kappa$ of the iron-arsenide superconductor Ba$_{1-x}$K$_x$Fe$_2$As$_2$ ($T_c \simeq$ 30 K) was measured in single crystals at temperatures down to $T \simeq 50$ mK ($\simeq T_c$/600) and in magnetic fields up to…

75As-zero-field nuclear magnetic resonance (NMR) and nuclear quadrupole resonance (NQR) measurements are performed on CaFe2As2 under pressure. At P = 4.7 and 10.8 kbar, the temperature dependences of nuclear-spin-lattice relaxation rate…

The in-plane thermal conductivity $\kappa$ of overdoped FeAs-based superconductor BaFe$_{1.73}$Co$_{0.27}$As$_2$ ($T_c$ = 8.1 K) single crystal was measured down to 80 mK. In zero field, the residual linear term $\kappa_0/T$ is negligible,…

The normal state and superconducting properties are investigated in the phase diagram of K_xSr_{1-x}Fe_2As_2 for 0<x<1. The ground state upper critical field, H_{c2}(0), is extrapolated from magnetic field dependent resistivity…

We report resistivity measurements performed on KFe$_2$As$_2$ single crystals down to $T$ = 0.3 K and in magnetic fields up to 17.5 T. The in-plane resistivity vs. $T$ curve has a convex shape down to $\sim$50 K and shows a $T^2$ dependence…

High-quality KFe2As2 single crystals have been studied by transport, magnetization and low-T specific heat measurements. Their analysis shows that superconductivity occurs (in some cases coexists) in the vicinity of disordered magnetic…

From the measurement and analysis of the specific heat of high-quality K_(1-x)Na_xFe_2As_2 single crystals we establish the presence of large T^2 contributions with coefficients alpha_sc ~ 30 mJ/mol K^3 at low-T for both x=0 and 0.1.…

The optical properties of KFe$_2$As$_2$ have been measured for light polarized in the a-b planes over a wide temperature and frequency range. Below $T^\ast\simeq 155$ K, where this material undergoes an incoherent-coherent crossover, we…

We report pressure-induced superconductivity in a single crystal of CaFe2As2. At atmospheric pressure, this material is antiferromagnetic below 170 K but under an applied pressure of 0.69 GPa becomes superconducting, with a transition…

The electrical transport and thermoelectric properties of K_xSr_{1-x}Fe_2As_2 are investigated for 0<x<1. The resistivity rho(T) shows a crossover from Fermi liquid-like temperature dependence at small x to linear rho~T dependence at…

Single crystals of Tl0.58Rb0.42Fe1.72Se2 are successfully grown with the superconducting transition temperatures Tconset=32K and Tczero=31.4K. The Hall coefficient exhibits a multi-band behavior, which is very similar to that of all other…

We have determined the resistive upper critical field Hc2 for single crystals of the superconductor Fe1.11Te0.6Se0.4 using pulsed magnetic fields of up to 60T. A rather high zero-temperature upper critical field of mu0Hc2(0) approx 47T is…

The specific heat down to 0.08 K of the iron pnictide superconductor KFe2As2 was measured on a single crystal sample with a residual resistivity ratio of ~650, with an onset Tc determined by specific heat of 3.7 K. The zero field normal…

Among the iron-based pnictide superconductors the material KFe$_2$As$_2$ is unusual in that its Fermi surface does not consist of quasi-nested electron and hole pockets. Here we report measurements of the temperature dependent London…

Measurements of temperature-dependent in-plane resistivity, $\rho(T)$, were used to determine the upper critical field and its anisotropy in high quality single crystals of stoichiometric iron arsenide superconductor KFe$_2$As$_2$. The…

Millimeter sized single crystals of KCa_2Fe_4As_4F_2 were grown using a self-flux method. The chemical compositions and crystal structure were characterized carefully. Superconductivity with the critical transition T_c = 33.5 K was…