相关论文: Synthesis and Bulk Properties of Oxychloride Super…
Ca2-xNaxCuO2Cl2 is a structural analogue to the La2-xSrxCuO4 superconductor. By substituting Na+ for Ca2+ mobile holes are introduced into the CuO2 planes. A series of experiments shows that the Na content x depends not only on the pressure…
Using the apical oxygen doping mechanism, i.e. a partial substitution of divalence O for the monovalence Cl, a p-type oxychloride cuprate superconductor, Sr2CuO2+xCl2-y, was synthesized at high pressure high temperature. The x-ray…
Dense pure and doped (Mg1-xAx)B2 samples with A = Na, Ca, Cu, Ag, Zn and Al were synthesized at high pressure - high temperature in a multi anvils press (3.5-6 GPa, 900-1000C) for x up to 0.20. They were studied by x-ray diffraction,…
We report the synthesis and superconducting properties of a metastable form of the known superconductor NaxCoO2*yH2O (x ~ 1/3, y ~ 4x). Instead of using the conventional bromine-acetonitrile mixture for sodium deintercalation, we use an…
We synthesized powder samples of Na$_{x}$CoO$_{2}\cdot y$H$_{2}$O changing the volume of the water in the hydration process, then investigated their superconducting properties,. It was proved that the volume of water is one of key…
The effect of hydrostatic pressure on the superconducting transition temperature of Na{0.35}CoO{2}.yH{2}O was investigated by ac susceptibility measurements up to 1.6 GPa. The pressure coefficient of T{c} is negative and the dependence…
Muon spin relaxation ($\mu$SR) measurements on the new layered cobalt oxide superconductor Na$_{0.35}$CoO$_{2}\cdot$1.3H$_{2}$O and its parent, non-superconducting compounds, have revealed unconventional nature of superconductivity through:…
Neutron scattering has been used to investigate the crystal structure and lattice dynamics of superconducting Na0.3CoO2 1.4(H/D)2O, and the parent Na0.3CoO2 material. The structure of Na0.3CoO2 consists of alternate layers of CoO2 and Na…
Cu2O nanorods have been deposited on soda-lime glass (SLG) substrates by the modified SILAR technique by varying the concentration of NaCl electrolyte into the precursor complex solution. The structural, electrical, and optical properties…
We have prepared powder samples of NaxCoO2 x yH2O using a new synthesis route. Superconductivity was observed in Na0.3CoO2 x 1.3H2O between 4 and 5K as indicated by the magnetic susceptibility. The bulk compressibilities of Na0.3CoO2 x…
The effect of the 16O-->18O substitution on the superconducting transition temperatures Tc of NaxCoO2.yH2O has been studied for several sets of samples. Each set has two kinds of samples, one with the oxygen sites in the CoO2 layers filled…
A study of the in-plane magnetic penetration depth \lambda_ab in a series of the cuprate superconductors Ca_2-xNa_xCuO_2Cl_2 (Na-CCOC) with Na content x=0.11, 0.12, 0.15, 0.18, and 0.19 is reported. The zero temperature values of…
Various samples of sodium cobalt oxyhydrate with relatively large amounts of Na$^{+}$ ions were synthesized by a modified soft-chemical process in which a NaOH aqueous solution was added in the final step of the procedure. From these…
Here we study the effect of Ca doping on charge transfer mechanism of polycrystalline YBa2Cu3O7-{\delta} compound. The samples of composition Y1-xCaxBa2Cu3O7-{\delta} (x = 0.00, 0.05, 0.10, 0.20 and 0.30) are synthesized through standard…
The observation of superconductivity at 4.3 K in a new crystalline form of Na0.3CoO2*1.3H2O is reported. The new superconductor has three layers of CoO6 octahedra per crystallographic unit cell, in contrast to the previously reported…
Poly- and single-crystalline Na$_x$CoO$_2$ has been successfully intercalated with H$_2$O and D$_2$O as confirmed by X-ray diffraction and thermogravimetric analysis. Resistivity, magnetic susceptibility, and specific heat measurements show…
High-transition-temperature (high-Tc) superconductivity is ubiquitous in the cuprates containing CuO2 planes but each cuprate has its own character. The study of the material dependence of the d-wave superconducting gap (SG) should provide…
Experiments under hydrostatic and uniaxial pressure serve not only as a guide in the synthesis of materials with superior superconducting properties but also allow a quantitative test of theoretical models. In this chapter the pressure…
The structural properties of NaxCoO2 and NaxCoO2yH2O have been investigated. The NaxCoO2yH2O samples in general show up the superconducting transitions at around 3.5K. EDAX analyses suggest our samples have the average composition of…
The effects of pressure on the superconducting properties of a Bi-based layered superconductor La2O2Bi3Ag0.6Sn0.4S6, which possesses a four-layer-type conducting layer, have been studied through the electrical resistance and magnetic…