Thin films of MgB2 superconductor were prepared by three different procedures on sapphire and silicon substrates. Boron thin films, ex-situ annealed in magnesium vapour, resulted in textured polycrystalline films with crystal dimensions…
Ultrathin MgB2 superconducting films with a thickness down to 7.5 nm are epitaxially grown on (0001) Al2O3 substrate by hybrid physical-chemical vapor deposition method. The films are phase-pure, oxidation-free and continuous. The 7.5 nm…
We report magnetic field dependent magnetization and microwave impedance measurements on a MgB2 superconductor prepared by high pressure synthesis. We find that the upper critical field is linearly dependent on temperature near Tc and the…
Very thick, ~ 40 $\mu$m, clean, and highly textured MgB2 film was effectively grown on an Al2O3 substrate. The fabrication technique is by the hybrid physical-chemical vapor deposition (HPCVD) using B2H6 gas and Mg ingot as the sources. The…
Superconducting MgB(2) films with Tc = 38.6 K were prepared using a precursor-deposition, ex-situ post-processing approach. Precursor films of boron, ~0.5 micrometer thick, were deposited onto Al(2)O(3) (102) substrates by e-beam…
The improvement in the fabrication techniques of iron-based superconductors have made these materials real competitors of high temperature superconductors and MgB$_2$. In particular, iron-chalcogenides have proved to be the most promising…
High-pressure electrical resistivity measurements reveal that the mechanical deformation of ultra-hard WB2 during compression induces superconductivity above 50 GPa with a maximum superconducting critical temperature, Tc of 17 K at 90 GPa.…
The in-situ growth of superconducting MgB2 thin films was examined from various perspectives. The paper discusses (1) growth temperature, (2) the effect of excess Mg, (3) the effect of residual gas during growth, (4) the effect of in-situ…
Mechanical stress causes motion of defects in solids. We show that in a type-II superconductor a moving dislocation generates a pattern of current that exerts the depinning force on the surrounding vortex lattice. Concentration of…
For technical application in windings of coils, transformers or motors, a reinforcement of MgB2 wires and tapes is necessary to withstand applied stresses and strains and to avoid cracks in the filaments. Therefore, the response of the…
Superconductivity has been found in RuN films obtained by reactive magnetron sputtering. This is a novel member of the metal nitride superconductors family. The critical temperature of the superconducting transition varies depending on the…
We prepared and characterized monofilamentary MgB2 wires with a mechanically reinforced composite sheath of Ta(Nb)/Cu/steel, which leads to dense filaments and correspondingly high transport currents up to Jc = 10^5 A/cm^2 at 4.2 K, self…
We report on the observation of dendritic flux avalanches in a large Niobium single crystal. In contrast to avalanches observed in thin films, they appear only in a very narrow temperature interval of about a tenth of a Kelvin near the…
We predict a novel buckling instability in the critical state of thin type-II superconductors with strong pinning. This elastic instability appears in high perpendicular magnetic fields and may cause an almost periodic series of flux jumps…
We report synthesis, structure/micro-structure, resistivity under magnetic field [R(T)H], Raman spectra, thermoelectric power S(T), thermal conductivity K(T), and magnetization of ambient pressure argon annealed polycrystalline bulk samples…
The stability of superconducting films with respect to oscillatory precursor modes for thermomag- netic avalanches is investigated theoretically. The results for the onset threshold show that previous treatments of non-oscillatory modes…
In this paper we develop a theory of mesoscopic fluctuations in disordered thin superconducting films in a parallel magnetic field. At zero temperature and sufficiently strong magnetic field the system undergoes a phase transition into a…
In this paper, we analyze the upper critical field of four MgB2 thin films, with different resistivity (between 5 to 50 mWcm) and critical temperature (between 29.5 to 38.8 K), measured up to 28 Tesla. In the perpendicular direction the…
We present electrical transport, magnetization, and specific heat measurements on bulk MgB2 samples (T_{c} = 38.5 K) synthesized under 200 MPa pressure using a process based on hot isostatic pressing with cooling under pressure. The samples…
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…