We present electrical transport, magnetization, and specific heat measurements on bulk MgB2 samples (T_{c} = 38.5 K) synthesized under 200 MPa pressure using a process based on hot isostatic pressing with cooling under pressure. The samples are fully dense and display excellent superconducting properties, including a narrow superconducting transition width (\Delta T_{c} = 0.75 K), a high upper critical field H_{c2} (H_{c2}(0) ~ 155 kOe), and a critical current density J_{c} that is the largest yet measured for bulk samples of MgB2 (J_{c}(0) ~ 1.4 MA/cm^{2}). Specific heat measurements yielded a jump \Delta C at T_{c} of 92 mJ/mol K. These superconducting properties are comparable to those obtained with techniques that are not so well suited to industrial scale fabrication.
@article{arxiv.cond-mat/0106518,
title = {Improved superconducting properties of MgB2},
author = {N. A. Frederick and Shi Li and M. B. Maple and V. F. Nesterenko and S. S. Indrakanti},
journal= {arXiv preprint arXiv:cond-mat/0106518},
year = {2009}
}