Related papers: FeCuNbSiB thin films with sub-Oersted coercivity
Compositionally graded Fe-Pt thin films were prepared on stationary 100 mm Si substrates by magnetron sputtering a base target of Fe on which a piece of Pt is asymmetrically positioned. Energy Dispersive X-Ray analysis was used to map the…
In this work we elaborated and characterized nanocomposite thin films using a preselected multiferroic matrix Bi$_{0.9}$Gd$_{0.1}$Fe$_{0.9}$Mn$_{0.1}$O$_3$ (BGFMO) in the aim to enhance their basic ferroelectric and magnetic properties. The…
Nanostructured Pd-Fe thin films with varied Fe content were prepared by electrodeposition technique from organic electrolytes on Cu and brass substrates. The structure and the magnetic properties of the films were investigated prior to…
Flexible NbC nanocomposite thin films with carbon content ranging from 0 to 99 at.% were deposited at room temperature on Si (100) and polystyrene substrates by non-reactive magnetron sputtering from pure Nb and C targets without applying…
We demonstrate that low concentrations of a secondary magnetic phase in (Ga,Mn)As thin films can enhance the coercivity by factors up to ~100 without significantly degrading the Curie temperature or saturation magnetisation. Magnetic…
We report pulsed laser deposition synthesis and characterization of polycrystalline Fe1-xCox Si thin films on Si (111). X-ray diffraction, transmission electron, and atomic force microscopies reveal films to be dense, very smooth, and…
Thickness uniformity is regarded as an important parameter in designing thin film devices. However, some applications based on films with non-uniform thickness have recently emerged, such as gas sensors and optimized materials based on the…
Although nanoscale deformation, such as nanostrain in iron chalcogenide (FeSexTe1-x, FST) thin films, has attracted attention owing to the enhancement of general superconducting properties, including critical current density (Jc) and…
The magnetization (M) as a function of temperature (T) from 2 to 300 K and in-plane field (H) up to 1 kOe, room temperature easy and hard direction in-plane field hysteresis loops for fields between -100 and +100 Oe, and 10 GHz…
A detailed nanoscale structural characterization was performed on high-quality La0.66Sr0.33MnO3 (LSMO) thin films of different thicknesses and deposited by pulsed laser deposition onto buffered Si (100) substrates. A multilayered structure…
Different thicknesses of cobalt thin films were growth by magnetron sputtering deposition techniques. The films thicknesses were determinated with X ray Photoelectron Spectroscopy (XPS) and Quartz Crystal Monitoring (QCM). XPS is also used…
Here, we report wafer scale fabrication of densely packed Fe nanostripe-based magnetic thin films on a flexible substrate and their magnetic anisotropy properties. We find that Fe nanostripes exhibit large in-plane uniaxial anisotropy and…
Mechanical strain can be used to control physical properties in materials. The experimental investigation of strain-induced effects at the nanoscale is of importance not only for its fundamental aspects, but also for the development of…
We present a universal nanomechanical sensing platform for the investigation of magnetostriction in thin films. It is based on a doubly-clamped silicon nitride nanobeam resonator covered with a thin magnetostrictive film. Changing the…
Scaling superconducting digital circuits requires fundamental changes in the current material set and fabrication process. The transition to 300 mm wafers and the implementation of advanced lithography are instrumental in facilitating…
We report magnetostatic measurements for granulated films (CoFeB)$_{x}$-(SiO$_{2}$)$_{1-x}$ with fabrication induced intraplanar anisotropy. The measurements have been performed in the film plane in the wide temperature interval…
Severe plastic deformation using high-pressure torsion of ternary Cu-based materials (CuFeCo and CuFeNi) was used to fabricate bulk samples with a nanocrystalline microstructure. The goal was to produce materials featuring the granular…
MnGe has been grown as a thin film on Si(111) substrates by molecular beam epitaxy. A 10 \AA\ layer of MnSi was used as seedlayer in order to establish the B20 crystal structure. Films of a thickness between 45 and 135 \AA\ have been…
5$\mu$m thick NdFeB films have been sputtered onto 100 mm Si substrates using high rate sputtering (18 $\mu$m/h). Films were deposited at ≤ 500 C and then annealed at 750 C for 10 minutes. While films deposited at temperatures up to…
We studied the ferroelectric and ferromagnetic properties of compressive strained and unstrained BiMnO3 thin films grown by rf-magnetron sputtering. BiMnO3 samples exhibit a 2D cube-on-cube growth mode and a pseudo-cubic struc-ture up to a…