Related papers: MOD derived pyrochlore films as buffer layer for a…
In the reported low-fluorine MOD-YBCO studies, the lowest F/Ba mole ratio of the precursor solution was 4.5. However, further lowering the F/Ba ratio is important according to the researches of YBCO thick film. On the other hand, the F/Ba…
The integration of high-temperature superconducting YBa2Cu3O6+x (YBCO) into flexible electronic devices has the potential to revolutionize the technology industry. The effective preparation of high-quality flexible YBCO films therefore…
In the present work we study the growth by pulsed laser deposition of YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) films on the r-cut sapphire substrates. To improve the matching of the lattice parameters between the substrate and the film we use…
Superconducting thick films (200$\mu$m-300$\mu$m) of YBCO have been fabricated successfully on MgO substrates by a new approach. The precursor powders (YBa2Cu3O7-$\delta$(Y123)+0.1molY2BaCuO5(Y211)) are placed between two MgO (10mm x 10mm)…
Most commercial high-temperature superconducting coated conductors based on ion beam assisted MgO deposited templates use $\mathrm{LaMnO_3}$ (LMO) films as the terminating buffer layer. In contrast, coated conductors based on inclined…
Solution derived La2Zr2O7 films have drawn much attention for potential applications as thermal barriers or low-cost buffer layers for coated conductor technology. Annealing and coating parameters strongly affect the microstructure of…
It is known that solid-state reaction in high-pressure oxygen can stabilize high-oxidation phases of Y-Ba-Cu-O superconductors in powder form. We extend this superoxygenation concept of synthesis to thin films which, due to their large…
YBCO films were successfully prepared on biaxially textured Ag{110}<211> substrates by using pulsed laser deposition. X-ray diffraction results showed that the degree of preferential orientation of Ag{110}<211> substrates varied with…
Over the last decade advances in high temperature superconducting (HTS) materials have generated a renewed optimism in the use of this technology in future high-power applications including motors, generators, and power transmission. The…
We have grown and characterized 30 nm thick YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) films, deposited by pulsed laser deposition on both MgO (110) and SrTiO$_3$ (001) substrates, which induce opposite strain to the superconducting layer. By…
Homogeneous highly epitaxial LaSrMnO3 (LSMO) thin films have been grown on Yttria-stabilized-Zirconia (YsZ) / CeO2 buffer layers on technological relevant 4" silicon wafers using a Twente Solid State Technology B.V. (TSST) developed large…
A rapid decrease in the critical current density (Jc) of YBa2Cu3O7-x (YBCO) films with increasing film thickness has been observed for multiple YBCO growth processes. While such behavior is predicted from 2D collective pinning models under…
Epitaxial bilayers of the high-temperature-superconductor YBa2Cu3O7-d (YBCO) and the ferromagnetic metal La0.67Ca0.33MnO3 (LCMO) were prepared by pulsed laser deposition on (110)-oriented SrTiO3 substrates, such that the CuO2 planes of YBCO…
High-temperature superconducting YBa2Cu3O7-d (YBCO) thin-film detectors with improved responsivities were developed for fast time-domain measurements in the THz frequency range. YBCO thin films of 30 nm thickness were patterned to micro-…
We report a synthetic route to achieve high electron mobility at room temperature in epitaxial La:BaSnO$_3$/SrZrO$_3$ heterostructures prepared on several oxide substrates. Room-temperature mobilities of 157, 145, and 143…
The oxygen deficiency $\delta$ in YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) plays a crucial role for affecting high-temperature superconductivity. We applied (coincident) Doppler broadening spectroscopy of the electron-positron annihilation line…
We study the growth and electronic properties of a high temperature superconductor, YBa$_2$Cu$_3$O$_7$ (YBCO) in proximity of a magnetic material, La$_{0.67}$Sr$_{0.33}$MnO$_3$ (LSMO). High quality single crystalline films of YBCO and…
By inserting a SrZrO$_3$ buffer layer between the film and the substrate, we demonstrate a significant reduction of the threading dislocation density with an associated improvement of the electron mobility in La:BaSnO$_3$ films. A room…
La2Zr2O7 (LZO) formation of bulk powders and of films by Chemical Solution Deposition (CSD) process have been studied using propionates. The treatment involved a one step cycle in the reducing forming gas (Ar-5%H2) to be compatible with…
La1-xCaxMnO3 (x = 0.3; LCMO) films of different thickness were sputter-deposited on SrTiO3(100) (STO) single crystal substrates with and without YBa2Cu3O7-d (YBCO) as template layer. The electric and magnetic properties and the…