We have synthesized a quaternary fluoroarsenide SrFeAsF with the ZrCuSiAs-type structure (P4/nmm, a = 0.3999 and c = 0.8973 nm), which is composed of an alternately stacked (FeAs)- and (SrF)+ layers, analogous to the FeAs-based…
We report the synthesis and physical property characterization of PrFe1-xCoxAsO with x = 0.0 to 1.0. The studied samples are synthesized by solid state reaction route via vacuum encapsulation method. The pristine compound PrFeAsO does not…
Polycrystalline Sr1-xNdxFeAsF samples were prepared at various Nd-doping levels using both a stoichiometric mixture of the starting materials and in slight excess amounts of FeAs. Susceptibility and resistivity of the samples were studied…
A huge enhancement of the superconducting transition temperature Tc was observed in tetragonal FeSe superconductor under high pressure. The onset temperature became as high as 27 K at 1.48 GPa and the pressure coefficient showed a huge…
The bulk polycrystalline sample FeSe1/2Te1/2 is synthesized by solid state reaction route in an evacuated sealed quartz tube at 750 oC. The presence of superconductivity is confirmed through magnetization/thermoelectric/resistivity studies.…
Polycrystalline sample of the new layered superconductor Bi4O4S3 is successfully synthesized by solid-state reaction method by using Bi, S and Bi2O3 powders with one step reaction. The superconducting transition temperature (Tconset=4.5 K),…
A new iron arsenide superconducting system LiFeAs was found that crystallizes into a tetragonal structure with space group P4/nmm. The superconductivity with Tc up to 18 K was observed in the compounds. This simple 111 type layered iron…
The layered compound LaOBiSSe was successfully synthesized by a two-step solid-state reaction method, which is isostructural with the quaternary compound LaOBiS2 indicated by the powder X-ray diffraction characterization, and the crystal…
"F-free" CeOBiS$_2$ single crystals have successfully grown, thoroughly eliminating a concern about F-contamination by using a high-purity CsCl flux. The obtained crystals have a plate-like shape with a size of 1.0-3.0 mm in the…
We report superconductivity in single crystals of the new iron-pnictide system BaFe1.9Pt0.1As2 grown by a self-flux solution method and characterized via x-ray, transport, magnetic and thermodynamic measurements. The magnetic ordering…
CaFe$_2$As$_2$ has been found to be exceptionally sensitive to the application of hydrostatic pressure and superconductivity has been found to exist in a narrow pressure region that appears to be at the interface between two different phase…
Muon spin relaxation ($\mu$SR) measurements on the new layered cobalt oxide superconductor Na$_{0.35}$CoO$_{2}\cdot$1.3H$_{2}$O and its parent, non-superconducting compounds, have revealed unconventional nature of superconductivity through:…
A polycrystalline sample of YNiGe3, being a non-magnetic isostructural counterpart to the unconventional pressure-induced superconductor CeNiGe3, was studied by means of specific heat and electrical resistivity measurements at temperatures…
We report the discovery of superconductivity at high pressure in SrFe2As2 and BaFe2As2. The superconducting transition temperatures are up to 27 K in SrFe2As2 and 29 K in BaFe2As2, making these the highest pressure-induced superconducting…
High-quality single crystals of K0.8Fe2Se1.4S0.4 are successfully synthesized by self-flux method with the superconducting transition temperatures Tconset = 32.8 K and Tczero = 31.2 K. In contrast to external pressure effect on…
The Ca10(PtnAs8)(Fe2As2)5 (n=3,4) compounds are a new type of iron pnictide superconductors whose structures consist of stacking Ca-PtnAs8-Ca-Fe2As2 layers in a unit cell. When n=3 (the 10-3-8 phase), the undoped compound is an…
DyRh4B4 has been known to crystallize in the primitive tetragonal (pt)-structure and to exhibit a ferromagnetic transition at 12 K, the highest magnetic transition temperature in the entire series of the RRh4B4 materials [1]. We show here…
Studied 100-atm O2-annealed RuSr2Gd1.5Ce0.5Cu2O10 (Ru-1222) compound crystallized in a tetragonal I4/mmm space group crystal structure. Thermo-gravemetric (TG) analysis of the compound showed the release of oxygen and breaking to metallic…
In this article we review our studies of the K0.80Fe1.76Se2 superconductor, with an attempt to elucidate the crystal growth details and basic physical properties over a wide range of temperatures and applied magnetic field, including…
The single crystal of ThCr2Si2-type BaPd2As2 was successfully prepared by a self-flux method, and the crystal structure was characterized by X-ray diffraction method with the lattice parameters a = 4.489(2) {\AA} and c = 10.322(3) {\AA}.…