相关论文: Discovery of Li2(Pd,Pt)3B superconductors

Magnetization in DC magnetic fields and at different temperatures have been measured on the Li2Pd3B compound. This material was recently found to show superconductivity at 7-8K. Critical fields Hc1(0) and Hc2(0) have been determined to be…

We discovered the enhancement of superconducting transition temperature, Tc, in yttrium sesquicarbide system with the maximum Tc of Tc=18K and their superconducting properties were discussed. The crystal structure of Y2C3 is the…

LiB, a predicted layered compound analogous to the MgB$_2$ superconductor, has been recently synthesized via cold compression and quenched to ambient pressure, yet its superconducting properties have not been measured. According to prior…

We report on the properties of new ruthenocuprates Ru(1-x)Sr2GdCu(2+x)O(8-y) (x=0, 0.1, 0.2, 0.3, 0.4, 0.75) that extend the superconductivity found previously in RuSr2GdCu2O8 (Tc=45 K) to the solid solution with varied Ru/Cu ratios. The…

We report on the synthesis and on basic superconducting properties of a completely new Mo_2Re_3B ternary boride. The crystal structure of the Mo_2Re_3B compound is characterised by Pmmm space group and the cell parameters: a=11.626 A,…

Magnetization studies have been carried out on superconducting MgB$_2$ (T$_c$=37K) in the temperature range of 2-50K and in magnetic field up to 5 Tesla. From these measurements, values of the lower critical field H$_c1$(0), upper critical…

In the present work, we report the synthesis of Pb-Bi alloy with enhanced Tc of up to 9K, which is higher than that of Pb. The alloy is synthesized via a solid-state reaction route in the vacuum-encapsulated quartz tube at 7000C in an…

We have discovered that samples of a new material produced by special processing of crystals of Sr2RuO4 (which is known to be a triplet superconductor with Tc values ~1.0-1.5K) exhibit signatures of superconductivity (zero DC resistance and…

The results of electrical resistance (1.4 - 300 K), magnetization (2-300 K) and heat-capacity (2 - 50 K) measurements in Y$_2$PdGe$_3$, found to crystallize in a AlB$_2$-derived hexagonalstructure, are reported. The results establish that…

REBCO coated conductor is a high temperature superconductor that has a wide range of applications, one of which is the current leads of magnet systems. In the design of current leads, it is crucial to minimize their thermal conduction while…

The single crystal of ThCr2Si2-type BaPd2As2 was successfully prepared by a self-flux method, and the crystal structure was characterized by X-ray diffraction method with the lattice parameters a = 4.489(2) {\AA} and c = 10.322(3) {\AA}.…

We report on magnetization data obtained as a function of temperature and magnetic field in Li2 (Pd0.8Pt0.2)3B and Li2Pd3B non-centro-symmetric superconductors. Reversible magnetization curves were plotted as M1/2 vs. T. This allows study…

Superconductivity was found for a rhenium boride Re3B at Tc=4.7 K and for ReB2 with Tc in the range from 4.5 to 6.3 K depending on the boron concentrations. Both compounds have the structure different from that of the simple layered…

Following the recent theoretical prediction of superconductivity in hole doped LiBC by Rosner et al [1], we have attempted to synthesise Li deficient LixBC (x = 1, 0.8, 0.6 and 0.4) and look for superconductivity in this system. Our…

The results of micro-structural and detailed magnetization studies are reported here for our recently published TbSr2Cu2.7Mo0.3O7+d superconductor with a transition temperature (Tc) at as high as 80 K [1]. From XRD and EDX the sample was…

In this paper we present a penetration depth study on the newly discovered superconductors Li$_2$Pd$_3$B and Li$_2$Pt$_3$B. Surprisingly, the low-temperature penetration depth $f(T)$ demonstrates distinct behavior in these two isostructural…

We have investigated the superconducting properties in a single crystal of a new superconductor Pb$_{2}$Pd via various techniques including magnetization, AC transport, transverse field muon spin rotation and relaxation (TF-$\mu$SR), and…

Magneto-resistive and magneto-caloric properties of polycrystalline Pr2/3Sr1/3MnO3 have been studied as a function of sintering temperature (Ts) between 1260-1450{\deg}C. Reitveld refinement of their X-ray diffraction (XRD) patterns…

Far-infrared reflectivity studies on the polycrystalline intermetallic compound MgB_2 with a superconducting transition temperature T_c=39 K were performed at temperatures 20 K to 300 K. We observe a significant raise of the…

Superconductivity with Tc above 9 K was found in metal-deficient NbB2 prepared under 5 GPa, while no clear superconductivity was observed down to 3 K in stoichiometric NbB2. The superconductivity was observed above x = 0.04 in Nb1-xB2. and…