相关论文: Large magnetic anisotropy in Ferrihydrite nanopart…
Nanoparticles (size 20, 40 and 60 nm) of Pr_0.5Sr_0.5MnO_3 are prepared by sol-gel technique and their magnetic properties are studied using ferromagnetic resonance and magnetization measurements. A comparison with the properties of the…
CoFe2O4 nanoparticles were synthesized using gelatin as a polymerizing agent. Structural, morphological and magnetic properties of samples treated at different temperatures were investigated by X-ray diffraction, scanning electron…
We show that the magnetic anisotropy energy of antiferromagnetic ferrihydrite depends on the square root of the nanoparticles volume, using a method based on the analysis of statistical distributions. The size distribution was obtained by…
A potassium alumina borosilicate glass with the composition 13K2O*13Al2O3*16B2O3*43SiO2*15Fe2O3-x was melted using Fe2O3 as raw material. The melt was dumped from a Pt-crucible with a downpipe in water which resulted in the formation of…
We report a systematic study on the structural and magnetic properties of Co_{x}Fe_{3-x}O_{4} magnetic nanoparticles with sizes between $5$ to $25$ nm, prepared by thermal decomposition of Fe(acac)_{3} and Co(acac)_{2}. The large…
The magnetic behavior of $Fe_{3-x}O_4$ nanoparticles synthesized either by high-temperature decomposition of an organic iron precursor or low-temperature co-precipitation in aqueous conditions, is compared. Transmission electron microscopy,…
Magnetic properties with 3 different sizes of Ni nanochains, synthesized by a technique of wet chemical solution, have been investigated experimentally. The sample sizes are 50 nm, 75 nm, and 150 nm with a typical length of a few microns.…
Magnetic nanoparticles of cobalt ferrite have been synthesized by wet chemical method using stable ferric and cobalt salts with oleic acid as the surfactant. X-ray Diffraction (XRD) and Transmission Electron Microscope (TEM) confirmed the…
We have studied the magnetic behavior of dextran-coated magnetite (Fe$_3$O$_4$) nanoparticles with median particle size $\left<d\right>=8$ $nm$. Magnetization curves and in-field M\"ossbauer spectroscopy measurements showed that the…
Here, we report wafer scale fabrication of densely packed Fe nanostripe-based magnetic thin films on a flexible substrate and their magnetic anisotropy properties. We find that Fe nanostripes exhibit large in-plane uniaxial anisotropy and…
The dynamic magnetic properties of Ni nanoparticles diluted in an amorphous SiO2 matrix prepared from a modified sol-gel method have been studied by the frequency f dependence of the ac magnetic susceptibility \c{hi}(T). For samples with…
Nanosheets of nickel with thickness equal to 0.6 nm have been grown within the interlayer spaces of Na-4 mica. The sheets are made up of percolative clusters of nanodisks. Magnetization characteristics indicate a superparamagnetic behavior…
The magnetic behaviour of nanoparticles of antiferromagnetic ferritin has been investigated by 57Fe Mossbauer absorption spectroscopy and magnetisation measurements, in the temperature range 2.5K-250K and with magnetic fields up to 7T.…
Bulk samples of carbon multilayer nanotubes with the structure of nested cones (fishbone structure) suitable for transport measurements, were prepared by compressing under high pressure (~25 kbar) a nanotube precursor synthesized through…
Magnetization reversal of individual, isolated high-aspect-ratio Fe nanoparticles with diameters comparable to the magnetic exchange length is studied by high-sensitivity submicron Hall magnetometry. For a Fe nanoparticle with diameter of 5…
Nanocrystalline Al-doped nickel ferrite powders have been synthesized by sol-gel auto-ignition method and the effect of non-magnetic aluminum content on the structural and magnetic properties has been studied. The X-ray diffraction (XRD)…
Mn-Zn ferrite nanoparticles have been subject of increasing research due to their desired properties for a wide range of applications. These properties include nanometer particle size control, tunable magnetic properties and low toxicity,…
We have studied the magnetic and power absorption properties of three samples of CoFe2O4 nanoparticles with sizes from 5 to 12 nm prepared by thermal decomposition of Fe (acac)3 and Co(acac)2 at high temperatures. The blocking temperatures…
Temperature dependent Ferromagnetic Resonance measurements performed as a function of diameter on Nickel nanowire arrays reveal several interesting features in these systems. With diameter decrease from 100 nm to 15 nm, a transition induced…
Spinel Fe3O4 nanoparticles have been produced through ball milling in methyl-alcohol (CH3OH), aiming to obtain samples with similar average particle sizes <d> and different interparticle interactions. Three samples having Fe3O4/CH3(OH) mass…