A racetrack coil using MgB2/Cu strand has been fabricated and tested for transport current density at 4.2 K in self field. The monofilamentary strand was 1.0 mm OD and insulated with S-glass braid. Eighty turns of strand (42 m) were wound…

The critical current densities of MgB2 monofilamentary strands with and without SiC additions were measured at 4.2 K. Additionally, magnetic Jc at B = 1 T was measured from 4.2 K to 40 K. Various heat treatment times and temperatures were…

In this letter, we report the results of transport Jc of solenoid coils upto 100 turns fabricated with Cu-sheathed MgB2 wires using a wind-reaction in-situ technique. Despite the low density of single core and some reaction between Mg and…

Transport critical current densities and n-values were measured at 4.2 K in fields up to 15 T on 7, 19, and 37-stack multifilamentary MgB2 strands made using an in-situ route. Some strands included SiC additions (particle size 30 nm), while…

Transport current values of 7.5 x 104 A/cm2 at 4.2 K and self-field are reported for MbB2-based tapes. MgB2 strands were formed by directly filling commercially available MgB2 powder into Nb-lined, monel tubes and wire drawing. The wires…

We present the fabrication and test results of Hot-Isostatic-Pressed (HIPed) Powder-in-Tube (PIT) MgB$_2$ coils. The coils properties were measured by transport and magnetization at different applied fields ($H$) and temperatures ($T$). The…

Thrust measurements were performed on a coil made of YBa2Cu3O7-d coated conductor acting as the excitation system of a single-sided linear synchronous motor. The superconducting coil was a single pancake in the shape of a racetrack with 100…

We report on the test of a small scale, non-planar coil using non-insulated ReBCO tape wound on a 3D-printed aluminum support structure. A 3D-scan of the winding frame which was printed out of AlSi10Mg using selective laser melting, showed…

We prepared and characterized monofilamentary MgB2 wires with a mechanically reinforced composite sheath of Ta(Nb)/Cu/steel, which leads to dense filaments and correspondingly high transport currents up to Jc = 10^5 A/cm^2 at 4.2 K, self…

Monocore powder-in-tube MgB2 strands were cold-drawn and heat-treated at 600C and 700C for times of up to 71 hours and structure-property relationships examined. Drawing-induced elongation of the Mg particles led, after HT, to a textured…

In this article, a novel hot wire oxidation-sublimation deposition (HWOSD) technique was developed to prepare molybdenum oxide (MoOx) thin films with high quality. Silicon heterojunction (SHJ) solar cells with the HWOSD MoOx as a hole…

The recently discovered iron-based superconductors with very high upper critical field and small anisotropy have been regarded as a potential candidate material for high field applications. However, enhancements of superconducting…

Copper sheath is the first choice for manufacturing high-Tc superconducting wires and tapes because of its high electrical and thermal conductivities, low cost and good mechanical properties. However, Cu can easily react with…

We report the temperature dependence of the transport critical current density (Jc) in textured Sr1-xKxFe2As2/Fe (Sr122) tapes fabricated by an ex situ powder-in-tube process. Critical currents were measured in magnetic fields up to 0-15 T…

Roebel cables made of HTS coated conductors can carry high currents with a compact design and reduced AC losses. They are therefore good candidates for manufacturing coils for HTS applications such as motors and generators. In this paper we…

MgB2 monofilamentary nickel-sheated tapes and wires were fabricated by means of the ex-situ powder-in-tube method using either high-energy ball milled and low temperature synthesized powders. All sample were sintered at 920 C in Ar flow.…

Transport measurements of critical current density, Jct, in monocore powder-in-tube MgB2 strands have been carried out at temperatures, T, of from 4.2 K to 40 K, and in transverse fields, B, of up to 14 T. Processing methods used were…

MgB2 hollow wires have been produced with a new technique which uses a conventional wire manufacturing process but is applied to composite billets containing the elemental B and Mg precursors in an appropriate shape. The technique has been…

Seven-core Ag/Fe sheathed Sr0.6K0.4Fe2As2 (Sr-122) superconducting wires were produced by the ex situ powder-in-tube (PIT) method. The relationship between the cold-work deformation process and the superconducting properties of wires were…

Iron-pnictides are hotly studied since 2008 in the superconducting materials research area, due to their special properties and unclear mechanism. Big achievement has been made in the pnictide research during the past years. For practical…