Magnetic relaxation in antiferromagnetic CoRh$_2$O$_4$ nanoparticles is investigated at 2 K by cooling the sample from a temperature (70 K) well above the antiferromagnetic ordering temperature at 27 K, following zero field cooled (ZFC) and…
The magnetic properties of Fe$_3$O$_4$ nanoparticle assemblies have been investigated in detail through a combination of vibrating sample magnetometry and muon spin relaxation ($\mu$SR) techniques. Two samples with average particle sizes of…
We report detailed studies on magnetic properties of Co3O4 nanoparticles of average size 12.5 nm. Temperature and field dependence of magnetization, wait time dependence of magnetic relaxation (aging), memory effects and temperature…
We report on the low-temperature magnetic ac-susceptibility of antiferromagnetic DyPO4 nanoparticles with a very high surface to volume ratio. The results are interpreted in terms of superparamagnetic relaxation of the Neel vector arising…
In this work, a successful synthesis of magnetic cobalt ferrite (CoFe2O4) nanoparticles is presented. The synthesized CoFe2O4 nanoparticles have a spherical shape and highly monodisperse in the selected solvent. The effect of different…
We report a systematic study on the structural and magnetic properties of Co_{x}Fe_{3-x}O_{4} magnetic nanoparticles with sizes between $5$ to $25$ nm, prepared by thermal decomposition of Fe(acac)_{3} and Co(acac)_{2}. The large…
We report studies on temperature, field and time dependence of magnetization on cupric oxide nanoparticles of sizes 9 nm, 13 nm and 16 nm. The nanoparticles show unusual features in comparison to other antiferromagnetic nanoparticle…
The role of particle size distribution inherently present in magnetic nanoparticles (NPs) is examined in considerable detail in relation to the measured magnetic properties of oleic acid-coated maghemite ({\gamma}-Fe$_2$O$_3$) NPs.…
We present X-ray diffraction (XRD), M\"ossbauer spectroscopy (MS) and d.c. magnetization measurements performed on ball-milled CuFe2O4 samples. The average particle size <d> was found to decrease to the nanometer range after t=15 min of…
We report studies on temperature, field and time dependence of magnetization on cupric oxide nanoparticles of sizes 9 nm, 13 nm and 16 nm. The nanoparticles show unusual features in comparison to other antiferromagnetic nanoparticle…
Single-phase Mg-doped ZnFe$_2$O$_4$ nanoparticles with x= 0, 0.3, 0.5, 0.7 have been prepared by the glycol-thermal method without any subsequent calcination. The crystallite size, microstructure and magnetic properties of the prepared…
Copper ferrite nanoparticles have catalytic activity for hydrogen peroxide, which can be used in many fields. This characteristic comes from the physical properties of matters at nanometer scale. Thus, controlling the size and aggregation…
The magnetization processes in binary magnetic/nonmagnetic amorphous alloy Hf_{57}Fe_{43} are investigated by the detailed measurements of magnetic hysteresis loops, temperature dependence of magnetization, relaxation of magnetization and…
We have studied the magnetic and power absorption properties of three samples of CoFe2O4 nanoparticles with sizes from 5 to 12 nm prepared by thermal decomposition of Fe (acac)3 and Co(acac)2 at high temperatures. The blocking temperatures…
A new class of superparamagnetism was found in relaxor ferroelectric 2/3BiFeO$_{3}$-1/3BaTiO$_{3}$. The size of the magnetic particle, estimated from the superparamagnetic magnetization curve, coincides with the size of the polar nanoregion…
The magnetic behavior of $Fe_{3-x}O_4$ nanoparticles synthesized either by high-temperature decomposition of an organic iron precursor or low-temperature co-precipitation in aqueous conditions, is compared. Transmission electron microscopy,…
Structural, magnetic and electronic structural properties of Ni0.2Cd0.3Fe2.5-xAlxO4 ferrites nanoparticles have been studied x-ray diffraction (XRD), transmission electron microscopy (TEM), dc magnetization, and near edge x-ray absorption…
A one-step synthesis of Ca$_x$Zn$_{1-x}$Fe$_2$O$_4$ (x=0, 0.5 and 1) nanoferrites and nanocomposites by the glycol-thermal method is reported. The structural, morphological and magnetic properties were studied using XRD, HRTEM, HRSEM,…
We report on isothermal magnetization, M\"ossbauer spectroscopy, and magnetostriction as well as temperature-dependent alternating-current (ac) susceptibility, specific heat, and thermal expansion of single crystalline and polycrstalline…
In this work we report a study of the magnetic behavior of ferrimagnetic oxide CoFe2O4 and ferrimagnetic oxide/ferromagnetic metal CoFe2O4/CoFe2 nanocomposites. The latter compound is a good system to study hard ferrimagnet/soft ferromagnet…