相关论文: Structure and physical properties of NaxCoO2.yH2O …
A systematic study of NaxCoO2 (x=0.50 - 0.90) and NaxCoO2 yH(D)2O (x=0.26 - 0.42, y=1.3) has been performed to determine phase stability and the effect of hydration on the structural and superconducting properties of this system. We show…
Neutron scattering has been used to investigate the crystal structure and lattice dynamics of superconducting Na0.3CoO2 1.4(H/D)2O, and the parent Na0.3CoO2 material. The structure of Na0.3CoO2 consists of alternate layers of CoO2 and Na…
The nonstoichiometric NaxCoO2 system exhibits extraordinary physical properties that correlate with temperature and Na concentration in its layered lattice without evident long-range structure modification when conventional crystallographic…
A series of CaxCoO2 (0.15 <= x <= 0.40) materials have been prepared by means of ion exchange reaction from NaxCoO2. Transmission electron microscopy (TEM) measurements revealed a rich variety of structural phenomena resulting from cation…
We report the synthesis and superconducting properties of a metastable form of the known superconductor NaxCoO2*yH2O (x ~ 1/3, y ~ 4x). Instead of using the conventional bromine-acetonitrile mixture for sodium deintercalation, we use an…
The observation of superconductivity at 4.3 K in a new crystalline form of Na0.3CoO2*1.3H2O is reported. The new superconductor has three layers of CoO6 octahedra per crystallographic unit cell, in contrast to the previously reported…
Two series of alpha and beta-NaxCoO2 materials have been prepared by means of Na deintercalation from the parent alpha-NaCoO2 and beta-Na0.6CoO2 phases, respectively. The alpha-NaxCoO2 materials undergo a…
We synthesized Nax(H3O)zCoO2yH2O samples with various Na/H3O ratios but with the constant Co valence of s = +3.40, and measured their magnetic properties to draw phase diagrams of the system. The superconductivity is very sensitive to the…
We synthesized powder samples of Na$_{x}$CoO$_{2}\cdot y$H$_{2}$O changing the volume of the water in the hydration process, then investigated their superconducting properties,. It was proved that the volume of water is one of key…
We report a complete analysis of the formal oxidation state of Co in NaxCoO2, in the interval 0.31<x<0.67. Iodometric titration and thermoelectric power confirm that a direct relationship between the Na content and the amount of Co 3 +…
The layered sodium cobalt oxyhydrate superconductor Na0.3CoO2*1.4H2O is shown through X-ray diffraction and thermogravimetric studies to be one of a series of hydrated phases of Na0.3CoO2. Further, it is shown that the material is…
Various samples of sodium cobalt oxyhydrate with relatively large amounts of Na$^{+}$ ions were synthesized by a modified soft-chemical process in which a NaOH aqueous solution was added in the final step of the procedure. From these…
Poly- and single-crystalline Na$_x$CoO$_2$ has been successfully intercalated with H$_2$O and D$_2$O as confirmed by X-ray diffraction and thermogravimetric analysis. Resistivity, magnetic susceptibility, and specific heat measurements show…
The crystal structures of the NaxCoO2 phases based on three-layer NaCoO2, with x=0.32, x=0.51, x=0.60, x=0.75 and x=0.92, determined by powder neutron diffraction, are reported. The structures have triangular CoO2 layers interleaved by…
We succeeded in synthesizing the powder samples of bilayer-hydrate sodium cobalt oxide superconductors NaxCoO2-yH2O with Tc = 0 ~ 4.6 K by systematically changing the keeping duration in a 75 % relative humidity atmosphere after…
We report the electrical, magnetic and thermal measurements on a layered cobalt oxyhydrate Na$_{0.31}$CoO$_{2}\cdot$1.3H$_{2}$O. Bulk superconductivity at 4.3 K has been confirmed, however, the measured superconducting fraction is…
The electronic properties of Co in bulk Na0.7CoO2 and the superconducting hydrated compound Na0.35CoO2 - y H2O have been investigated by x-ray absorption spectroscopy (XAS) and resonant inelastic x-ray scattering (RIXS) using hard x-rays.…
Results of thermo-electric power (S) and electrical resistivity (r) measurements are reported on NaxCoO2 compounds with x = 1.0, 0.7 and 0.6. These are single-phase compounds crystallizing in the hexagonal structure (space group P63/mmc) at…
Layered Co oxide NaxCoO2.yH2O with a superconducting transition temperature Tc =4.5 K has been studied by 59Co NQR. The nuclear spin relaxation rate 1/59T1 is nearly proportional to temperature T in the normal state. In the superconducting…
Transmission-electron-microscopy investigation reveals the presence of a superstructure with a doubled period of 2d110 in the NaxCoO2 materials for x ranging from 0.75 to 1.0. Systematic analyses suggest that this superstructure in general…