The incessant technological pursuit towards a more sustainable and green future depends strongly on permanent magnets. At present, their use is widespread, making it imperative to develop new processing methods that generate highly…
The use of rare-earth-based permanent magnets is one of the critical points for the development of the current technology. On the one hand, industry of the rare-earths is highly polluting due to the negative environmental impact of their…
With an annual production amounting to 800 kilotons, ferrite magnets constitute the largest family of permanent magnets in volume, a demand that will only increase as a consequence of the rare-earth crisis. With the global goal of building…
We prepared very high-coercivity cobalt ferrite nanoparticles using short-time high-energy mechanical milling. After the milling process, the coercivity of the nanoparticles reached 3.75 kOe - a value almost five times higher than that…
In this report, the effect of the cold sintering process (CSP) on the electro-chemo-mechanical properties of 10 mol% Gd-doped ceria (GDC) is investigated. High purity nanoscale GDC powder is sintered via a cold sintering process (CSP) in…
In the search for improved permanent magnets, fueled by the geostrategic and environmental issues associated with rare-earth-based magnets, magnetically hard (high anisotropy)-soft (high magnetization) composite magnets hold promise as…
The effect of sintering temperatures (Ts) on the structural and magnetic properties of Ni0.6Zn0.4Fe2O4 (NZFO) ferrites synthesized by conventional double sintering method has been reported. The samples are sintered at 1200, 1250 and 1300…
We present the low temperature magnetic properties in Ni1.5Fe1.5O4 ferrite as the function of pH at which the material was prepared by chemical route and post annealing temperature. The material is a ferri or ferromagnet, but showed…
The changes of magnetic properties upon heat treatment of a metastable supersaturated solid solution processed by severe plastic deformation are investigated by in-situ AC-hysteresis measurements. Data are analyzed in the framework of…
Spark plasma sintering (SPS) technique is applied in combination with hydrogen decrepitation process for the recycling of SmCo5 magnets. The SmCo5 magnets for recycling were first decrepitated by hydrogen gas of a pressure of 4 bar for 3…
La-Fe-Si-based alloys are among the most application-ready magnetocaloric materials for room-temperature magnetic refrigeration. Powder metallurgy methods have been previously demonstrated to successfully produce structures with sub-mm…
Spinel Fe3O4 nanoparticles have been produced through ball milling in methyl-alcohol (CH3OH), aiming to obtain samples with similar average particle sizes <d> and different interparticle interactions. Three samples having Fe3O4/CH3(OH) mass…
We show here for the first time the use of a cold sintering process (CSP) to sinter CoSb3-based thermoelectric materials. CSP at 150 {\deg}C for 90 min under a uniaxial pressure of 750 MPa yields pieces with a relative density of 86 %,…
We report on isothermal pulsed (20 ms) field magnetization, temperature dependent AC - susceptibility, and the static low magnetic field measurements carried out on 10 nm sized Pr0.5Ca0.5MnO3 nanoparticles (PCMO10). The saturation field for…
In the last decades, to improve the CAP treatment efficiency, its biological effects in combination with other physical modalities have widely investigated. However, the physical insight into most of supposed synergistic effects remained…
We report here the realization of ferroelectricity, ferromagnetism and magnetocapacitance effect in SrFe12O19 ceramics at room temperature. The ceramics demonstrate a saturated polarization hysteresis loop, two I-V peaks and large anomaly…
In this work we report a study of the magnetic behavior of ferrimagnetic oxide CoFe2O4 treated by mechanical milling with different grinding balls. The cobalt ferrite nanoparticles were prepared using a simple hydrothermal method and…
Experimental and computational studies were performed on Co2FeGe Heusler alloy. It was found that the alloy has very high experimental magnetic moment of 6.1 muB/f.u., curie temperature of 1073K and very high spin-wave stiffness constant of…
Magnetic properties of a sigma-phase Fe60V40 intermetallic compound were studied by means of ac and dc magnetic susceptibility and magnetocaloric effect measurements. The compound is a soft magnet yet it was found to behave like a…
Polycrystalline CrTe1-xSex samples were prepared using the conventional solid-state reaction technique and characterized by x-rad diffraction, temperature- and field- dependent magnetization for possible use in magnetocaloric cooling.…