In this paper, two fatigue lifetime prediction models are tested on TiAl intermetallic using results from uniaxial low-cycle fatigue tests. Both assessments are based on dissipated energy but one of them considers a hydrostatic pressure…
Magnetron sputtered titanium nitride (TiN) thin films are widely used as protective coatings due to their high hardness, but suffer from inherent brittleness and low fracture toughness, limiting their applicability. The multilayering of TiN…
The brittleness of an aluminide diffusion coating protecting a Ren\'e 125 Ni-based polycrystalline superalloy was investigated over a wide range of temperatures in its as-received and thermally aged form. Isothermal and thermal cycled aging…
Strain-controlled fatigue of Mg-1Mn-0.5Nd (wt.\%) alloy were studied by experiment and simulation. The microstructure was made up of a dispersion of strongly texture grains (13\%) embedded in a matrix of grains with a random texture. The…
The damage mechanisms and load redistribution of high strength TC17 titanium alloy/unidirectional SiC fibre composite (fibre diameter = 100 $\mu$m) under high temperature (350 {\deg}C) fatigue cycling have been investigated in situ using…
The deformation mechanisms governing the cyclic stress-strain behaviour of a TiNi shape memory alloy were investigated in this work. To understand the development of these mechanisms during cyclic loading, three low-cycle fatigue tests were…
Crack initiation governs high cycle fatigue life and is susceptible to microstructural details. While corresponding microstructure-sensitive models are available, their validation is difficult. We propose a validation framework where a…
The fatigue properties of 930 nm-thick Au films and 1 {\mu}m-thick Au film with a Ti interlayer are systematically investigated. The dominant damage behaviors of 930 nm-thick Au films under dynamic bending cyclic loading changed from…
There is a long-standing technological problem in which a stress dwell during cyclic loading at room temperature in Ti causes a significant fatigue life reduction. It is thought that localised time dependent plasticity in soft grains…
A series of density functional theory (DFT) simulations was performed to investigate the approach, contact, and subsequent separation of two atomically flat surfaces consisting of different materials. Aluminum (Al) and titanium nitride…
A microstructure-based model that accounts for the effect of grain size has been developed to study the effect of grain size on the fatigue life of Inconel 718 alloys. The fatigue behavior of two alloys with different grain size was…
When considering grinding of minerals, scaling effect induces competition between plastic deformation and fracture in brittle solids. The competition can be sketched by a critical size of the material, which characterizes the…
We study the fatigue fracture of disordered materials by means of computer simulations of a discrete element model. We extend a two-dimensional fracture model to capture the microscopic mechanisms relevant for fatigue, and we simulate the…
This paper presents a multi-scale modelling approach to investigate the underpinning mechanisms of microstructure-sensitive damage of single crystal Sn-3Ag-0.5Cu (wt%, SAC305) solder joints of a Ball Grid Array (BGA) board assembly subject…
The main purpose of this study is to determine, via a three dimensions Finite Element analysis (FE), the stress and strain fields at the inner surface of a tubular specimen submitted to thermo-mechanical fatigue. To investigate the surface…
Solids subjected to repeated cycles of stress or deformation can fail after several cycles, a phenomenon termed fatigue failure. Although intensely investigated for a wide range of materials owing to its obvious practical importance, a…
In recent years, interfacial fracture becomes one of the most important problems in the assessment of reliability of electronics packaging. Especially, underfill resin is used with solder joints in flip chip packaging for preventing the…
There is a long standing technological problem in which a stress dwell during cyclic loading at room temperature in Ti causes a significant fatigue life reduction. It is thought that localised time dependent plasticity in soft grains…
Lifecycle assessment of wind turbines is essential to improve their design and to optimum maintenance plans for preventing failures during the design life. A critical element of wind turbines is the composite blade due to uncertain cyclic…
An accurate assessment for fatigue damage as a function of activation and deactivation cycles is vital for the design of many engineering parts. In this paper we extend the probabilistic and local approach to this problem proposed in [1,2]…