Fatigue failure is ubiquitous in engineering applications. While the total fatigue life is critical to understanding a component's operational life, for safety, regulatory compliance, and predictive maintenance, the characterization of…
In this work we propose a stochastic model for estimating the occurrence of crack initiations on the surface of metallic specimens in fatigue problems that can be applied to a general class of geometries. The stochastic model is based on…
The following study investigates the statistical nature of crack jumps during fatigue of Inconel 718. In-situ measurement in atmospheric air of the crack length at several loading and temperature conditions was conducted using a direct…
Fatigue crack growth is decisive for the design of thin-walled structures such as fuselage shells of air planes. The cold rolling process, used to produce the aluminium sheets this structure is made of, leads to anisotropic mechanical…
Aluminum alloy A356-T6 was subjected to fully reversed cyclic loading under tension, torsion and combined loading. Results indicate that endurance limits are governed by maximum principal stress. Fractography demonstrates long shear mode…
Recent improvements in additive manufacturing and high-throughput material synthesis have enabled the discovery of novel metallic materials for extreme environments. However, high-fidelity testing of advanced mechanical properties such as…
In this work a novel methodology for fracture toughness characterization by means of the small punch test (SPT) is presented. Notched specimens are employed and fracture resistance is assessed through a critical value of the notch mouth…
In this paper the problem of a plane strain hydraulic fracture in elasto-plastic material is analyzed. The analysis is based on Finite Element Method computations of crack propagation and closure to simulate the Mini-Frac calibration test.…
Clay, the major ingredient of natural soils, is often used as a rheological modifier while formulating paints and coatings. When subjected to desiccation, colloidal clay suspensions and clayey soils crack due to the accumulation of…
In this work, the crack nucleation under fretting loading is investigated experimentally with a damage tolerant 2024 aluminium alloy. A new method is introduced to determine its condition with respect to all loading parameters including the…
This paper presents an experimental study of the fretting crack nucleation threshold, expressed in terms of loading conditions, with a cylinder/plane contact. The studied material is a damage tolerant aluminium alloy widely used in the…
A new model is presented to predict hydrogen-assisted fatigue. The model combines a phase field description of fracture and fatigue, stress-assisted hydrogen diffusion, and a toughness degradation formulation with cyclic and hydrogen…
Cast and HIP'ed \textgamma-TiAl 4522XD is being developed for use in jet engine low pressure turbine blades, where temperature variations occur through the flight cycle. The effects of temperature variations on fatigue cracking were…
An estimate of the effective toughness of heterogeneous materials is proposed based on the Phase Field Fracture model implemented in an FFT homogenization solver. The estimate is based on the simulation of the deformation of representative…
An accurate risk assessment for fatigue damage is of vital importance for the design and service of today's turbomachinery components. We present an approach for quantifying the probability of crack initiation due to surface driven…
Fatigue failure of crystalline materials is a difficult problem in science and engineering, and recent results have shown that fatigue crack growth can occur in intermittent jumps which have fat-tailed distributions. As fatigue crack…
The accumulation of residual stress during welding and additive manufacturing is an important effect that can significantly anticipate the workpiece failure. In this work we exploit the physical and analytical transparency of a 1.5D model…
A novel FFT-based phase-field fracture framework for modelling fatigue crack initiation and propagation at the microscale is presented. A damage driving force is defined based on the stored energy and dislocation density, relating…
We propose a decomposition of constitutive relations into crack-driving and persistent portions, specifically designed for materials with anisotropic/orthotropic behavior in the phase field approach to fracture to account for the…
A micromechanical model at the microscale within a crystal plasticity self-consistent model, is used to analyse loading histories in Type 316H stainless steel, common to structural components in high-temperature power plants. The study…