Dielectric permittivity was studied in ceramics of relaxor ferroelectric bismuth-sodium titanate Na$_{0.5}$Bi$_{0.5}$TiO$_{3}$. The measurements were performed on as sintered and heat treated in vacuum samples. The diffuse dielectric…

Multiferroic (Bi1-xLaxFeO3)0.5(PbTiO3)0.5 ceramics was prepared from mechanical synthesized nanopowders. The XRD studies revealed the tetragonal structure and the tetragonality decreased with La content. Dielectric response of the compounds…

Complex electrical permittivity measurements in (1-x)[Pb(Mg1/3 Nb2/3)O3]-xPbTiO3 ceramics for 0.10 x 0.40 were performed in the frequency and temperature range from 1 kHz to 100 kHz and from 15 to 600 K, respectively. Unexpected dielectric…

The dielectric properties of tantalum doped BaTi0.85Zr0.15O3 were investigated. The conventional solid state reaction method was used to make the ceramic samples. The composition was close to the pinch point of the three structure phase…

Dielectric study over a broadband was carried out from 10 to 70 K on ceramic Gd1-xYxMnO3 (x= 0.2, 0.3, and 0.4). For all the compositions, a prominent sharp peak about ~18K was observed in the temperature dependence of both {\epsilon}'(T)…

Advancing the functional performance of bismuth ferrite (BiFeO$_3$) requires precise control over phase stability and microstructure, challenges often complicated by secondary phase formation within the Bi$_2$O$_3$-Fe$_2$O$_3$ system. In…

We revealed the anomalous temperature behavior of the giant dielectric permittivity and unusual frequency dependences of the pyroelectric response of the fine-grained ceramics prepared by the spark plasma sintering of the ferroelectric…

Multiferroic bismuth ferrite Bi_2Fe_4O_9 (BFO) ceramic was synthesized by conventional solid state reaction route. X-ray diffraction and Rietveld refinement show formation of single phase ceramic with orthorhombic crystal structure (space…

Frequency dependence of the dielectric constant of complex perovskite oxide Ba(1-x)La(x)Ti(1-x)Cr(x)O3 (BLTC) ceramics with the composition ratio 0.4<= x <= 0.7 is precisely measured in the temperature range from 20 K to 300 K, and the…

Temperature-dependent dielectric permittivity of lead-free (LixNa1-x)NbO3 for nominal x = 0.04-0.20, prepared by solid state reaction followed by sintering, was studied to resolve often debated issue pertaining to exactness of morphotropic…

Room temperature dielectric and magnetic properties of BiFeO$_3$ samples, co-doped with magnetic Gd and non-magnetic Ti in place of Bi and Fe, respectively, were reported. The nominal compositions of…

The model discussion focused on links between the unique properties of relaxor ceramics and the basics of critical phenomena physics and glass transition physics. It indicates the significance of uniaxiality for appearing mean-field…

The temperature dependence of elastic, dielectric, and piezoelectric properties of (65-x)Pb(Mg1/3Nb2/3)O3-xBaTiO335-PbTiO3 ceramics with x=0, 1, 2, 3, and 4 was investigated. Compound with x=2 was found to exhibit a large piezoelectric…

In contrast to ordinary ferroelectrics where the temperature, Tm, of the permittivity maximum monotonically increases with bias field, E, in (1-x)PbMg1/3Nb2/3O3-(x)PbTiO3 (0<x<0.35) single crystals, Tm was found to remain constant or…

AFe$_{1 / 2}$B$_{1 / 2}$O$_{3}$(A- Ba, Sr, Ca; B-Nb, Ta, Sb) ceramics were synthesized and temperature dependencies of the dielectric permittivity were measured at different frequencies. The experimental data obtained show very high values…

We investigate the low temperature behaviour of Pb(In$_{1/2}$Nb$_{1/2}$)O$_{3}$-Pb(Mg$_{1/3}$Nb$_{2/3}$)O$_{3}$-PbTiO$_{3}$ using dielectric permittivity measurements. We compare single crystal plates measured in the [001] and [111]…

(1-x)Li0.12Na0.88NbO3-xBaTiO3 (0 to x to 0.40) ferroelectric ceramics were prepared using conventional ceramics route and their phase transitional behavior is investigated by using dielectric spectroscopy. The temperature-dependent…

High-frequency dielectric studies of Bi_0.85Nd_0.15FeO_3 ceramics performed betweeen 100 and 900 K reveal hardening of most polar phonons on cooling below antiferroelectric phase transition, which occurs near 600 K. Moreover, a strong THz…

In-plane temperature dependent dielectric behavior of BiFeO3 (BFO) as-grown thin films show diffuse but prominent phase transitions near 450 (+/-10) K and 550 K with dielectric loss temperature dependences that suggest skin layer effects.…

Dielectric nonlinear response of (PbMg$_{1/3}$Nb$_{2/3}$O$_3$)$_{0.9}$(PbTiO$_3$)$_{0.1}$ (0.9PMN-0.1PT) relaxor ceramics was investigated under different ac drive voltages. It was observed that: (i) the dielectric permittivity is…