相关论文: Large barocaloric effect with high pressure-drivin…
We report magnetization and differential thermal analysis measurements as a function of pressure accross the martensitic transition in magnetically superelastic Ni-Mn-In alloys. It is found that the properties of the martensitic…
A remarkable decrease of the structural transition temperature of MnNiSi from 1200 K to <300 K by chemically alloying it with MnFeGe results in a coupling of the magnetic and structural transitions, leading to a large magnetocaloric effect…
The effect of pressure on the magnetic and the magnetocaloric properties around the martensitic transformation temperature in NiCoMnSb Heusler alloy has been studied. The martensitic transition temperature has significantly shifted to…
The isostructural alloying of two compounds with extremely different magnetic and thermo-structural properties has resulted in a new system, (MnNiSi)1-x(FeCoGe)x, that exhibits extraordinary magnetocaloric properties with an acute…
Magnetic and magneto-functional behavior of a Fe-doped MnNiGe alloy with nominal composition Mn$_{0.85}$Fe$_{0.15}$NiGe have been investigated in ambient as well as in high pressure condition. The alloy undergoes first order martensitic…
Giant magnetocaloric effect is widely achieved in hexagonal MnMX-based (M = Co or Ni, X = Si or Ge) ferromagnets at their first-order magnetostructural transition. However, the thermal hysteresis and the low sensitivity of the…
Ni-Mn-In magnetic shape-memory Heusler alloys exhibit generally a large thermal hysteresis at their first-order martensitic phase transition which hinder a technological application in magnetic refrigeration. By optimizing the Cu content in…
A coupling of the first-order paramagnetic-to-induced-ferromagnetic martensitic and the second-order antiferromagnetic-to-ferromagnetic metamagnetic transitions was found in MnNi0.8Fe0.2Ge alloy. Based on the coupling, a magneto-volume…
Structural and magnetic properties of the CoMn$_{0.88}$Cu$_{0.12}$Ge compound have been investigated using X-ray diffraction (XRD) and differential scanning calorimetry (DSC) accompanied with investigation of magnetic properties under…
The magnetic and thermodynamic properties of a Ni2.19Mn0.81Ga alloy with coupled magnetic and structural (martensitic) phase transitions were studied experimentally and theoretically. The magnetocaloric effect was measured by a direct…
The magnetostructural coupling between the structural and the magnetic transition plays a crucial role in magnetoresponsive effects in a martensitic-transition system. A combination of various magnetoresponsive effects based on this…
We have studied the effect of magnetic field on a non-stoichiometric Heusler alloy Ni$_{50}$Mn$_{35}$In$_{15}$ that undergoes a martensitic as well as a magnetic transition near room temperature. Temperature dependent magnetization…
We report the effect of hydrostatic pressure on the magnetic and structural properties of the shape-memory Heusler alloy Ni50Mn35In15. Magnetization and x-ray diffraction experiments were performed at hydrostatic pressures up to 5 GPa using…
Magnetic properties of a polycrystalline alloy Ni$_{2.19}$Mn$_{0.81}$Ga, which undergoes a first-order magnetostructural phase transition from cubic paramagnetic to tetragonal ferromagnetic phase, are studied. Hysteretic behavior of…
Novel Ni-Co-Mn-Ti all-d-metal Heusler alloys are exciting due to large multicaloric effects combined with enhanced mechanical properties. An optimized heat treatment for a series of these compounds leads to very sharp phase transitions in…
We report a systematic study on the magneto-structural transition in Mn-rich Fe-doped Mn-Fe-Ni-Sn(Sb/In) Heusler alloys by keeping the total valence electron concentration (e/a ratio) fixed. The martensitic transition (MT) temperature is…
Polycrystalline samples of Co$_{1-x}$Cu$_x$MnGe ($x=0.05, 0.10, 0.15, 0.22$ and 0.35), prepared by arc melting under argon atmosphere, have been annealed at 1123 K with final furnace cooling. The samples have been investigated by powder…
An effective scheme of isostructural alloying was applied to establish a Curie-temperature window in isostructural MnNiGe-CoNiGe system. With the simultaneous accomplishment of decreasing structural-transition temperature and converting…
Ferromagnetic solids acquire nontrivial magnetic and caloric properties when the temperature of the structural phase transition approaches the Curie point. Deciphering magneto-structural transitions, i.e. determining their characteristic…
We report on measurements of the adiabatic temperature change in the inverse magnetocaloric Ni$_{50}$Mn$_{34}$In$_{16}$ alloy. It is shown that this alloy heats up with the application of a magnetic field around the Curie point due to the…