In this study, a preparation route of Co-Cu alloys with soft magnetic properties by high-pressure torsion deformation is introduced. Nanocrystalline, supersaturated single-phase microstructures are obtained after deformation of Co-Cu…
A Cu-Fe nanocomposite containing 50 nm thick iron filaments dispersed in a copper matrix was processed by torsion under high pressure at various strain rates and temperatures. The resulting nanostructures were characterized by transmission…
A filamentary composite elaborated by cold drawing was processed by High Pressure Torsion (HPT). The nanostructure resulting from this severe plastic deformation (SPD) was investigated thanks to scanning electron microscopy, transmission…
In this study, severe plastic deformation by high pressure torsion is used as a fabrication method for nanocrystalline magnetic CuCo alloys in bulk quantities. By subsequent isothermal annealing, phase separation of the supersaturated solid…
Samples consisting of one ferromagnetic and one diamagnetic component which are immiscible at the thermodynamic equilibrium (Co-Cu, Fe-Cu, Fe-Ag) are processed by high-pressure torsion at various compositions. The received microstructures…
Mixtures of Fe and Cu powders are cold-compacted and subsequently deformed with severe plastic deformation by high-pressure torsion, leading to bulk samples. The dilution of Fe in the Cu matrix is investigated with SQUID-magnetometry,…
Severe plastic deformation using high-pressure torsion of ternary Cu-based materials (CuFeCo and CuFeNi) was used to fabricate bulk samples with a nanocrystalline microstructure. The goal was to produce materials featuring the granular…
The processing of binary alloys consisting of ferromagnetic Fe and antiferromagnetic Cr by severe plastic deformation (SPD) with different chemical compositions has been investigated. Although the phase diagram exhibits a large gap in the…
Bulk metallic samples were synthesized from different binary powder mixtures consisting of elemental Cu, Co, and Fe using severe plastic deformation. Small particles of the ferromagnetic phase originate in the conductive Cu phase, either by…
This work gives insights into processing and characterisation of bulk nanocrystalline FeCr materials. The investigated FeCr alloys, consisting of 30, 50 and 70 at.% ferromagnetic Fe and remaining anti-ferromagnetic Cr, are processed by arc…
Exchange-coupling between soft- and hard-magnetic phases plays an important role in the engineering of novel magnetic materials. To achieve exchange coupling, a two-phase microstructure is necessary. This interface effect is further…
During the past decade, CoFe2O4 (hard)/Co-Fe alloy (soft) magnetic nanocomposites have been routinely prepared by partial reduction of CoFe2O4 nanoparticles. Monoxide (i.e., FeO or CoO) has often been detected as a byproduct of the…
A Cu-Cr composite was processed by severe plastic deformation to investigate the role of interphase boundaries on the grain size reduction mechanisms. The as-deformed material exhibits a grain size of only 20nm. This gives rise to a…
We report an experimental study of the CoFe2O4/CoFe2 nanocomposite, a nanostructured material formed by hard (CoFe2O4) and soft (CoFe2) magnetic materials. The precursor material, cobalt ferrite (CoFe2O4), was prepared using the…
Ultrafine-grained aluminum alloys offer interesting multifunctional properties with a combination of high strength, low electrical resistivity, and low density. However, due to thermally induced grain coarsening, they typically suffer from…
A complex study of aging kinetics for both coarse-grained and nanostructured by severe plastic deformation Cu -- 2 wt% Be alloy is reported. It is shown that aging of a coarse-grained alloy leads to continuous formation of nanosized CuBe…
Ferromagnetic (Fe or Fe20Ni80) and antiferromagnetic (NiO) phases were deformed by high pressure torsion, a severe plastic deformation technique, to manufacture bulk sized nanocomposites and demonstrate an exchange bias, which has been…
Nano-structured molybdenum-copper composites have been produced through severe plastic deformation of liquid-metal infiltrated Cu30Mo70 and Cu50Mo50 (wt.%) starting materials. Processing was carried out using high pressure torsion at room…
Severe plastic deformation of powder blends consisting of SmCo5-Cu results in magnetically hardened nanocomposite bulk materials. The microstructure is continuously refined with increasing torsional deformation, yet, coercivity saturates at…
The thermal decomposition behavior, the microstructural evolution and its influence on the mechanical properties of a supersaturated Cu Co solid solution with ~100 nm average grain size prepared by severe plastic deformation is investigated…