相关论文: Magnetism of monomer MnO and heterodimer FePt@MnO …
Zero field cooled (ZFC)/Field Cooled (FC) magnetization curves of a bulk MnO single crystal show a peculiar peak at low temperatures (~40K) similar to the low temperature peak observed in MnO nanoparticles. In order to investigate the…
We report studies on temperature, field and time dependence of magnetization on cupric oxide nanoparticles of sizes 9 nm, 13 nm and 16 nm. The nanoparticles show unusual features in comparison to other antiferromagnetic nanoparticle…
We report studies on temperature, field and time dependence of magnetization on cupric oxide nanoparticles of sizes 9 nm, 13 nm and 16 nm. The nanoparticles show unusual features in comparison to other antiferromagnetic nanoparticle…
We have performed unpolarized and polarized neutron diffraction experiments on monodisperse 8 nm and 13 nm antiferromagnetic MnO nanoparticles. For the 8 nm sample, the antiferromagnetic transition temperature $T_N$ (114 K) is suppressed…
We report nanoscale inter-particle magnetic orderings in self-assemblies of Fe3O4 nanoparticles (NPs), and the emergence of inter-particle antiferromagnetic (AF) (super-antiferromagnetic) correlations near the coercive field at low…
Magnetism of a very thin antiferromagnetic (AFM) surface CuO has been investigated with the partially oxidized nanocomposites of Cu-CuCl, ~ 200 nm. The samples are characterized by X-ray diffraction, X-ray photoelectron spectroscopy,…
We report detailed studies on non-equilibrium magnetic behavior of antiferromagnetic Co_3O_4 nanoparticles. Temperature and field dependence of magnetization, wait time dependence of magnetic relaxation (aging), memory effects and…
We report detailed studies on magnetic properties of Co3O4 nanoparticles of average size 12.5 nm. Temperature and field dependence of magnetization, wait time dependence of magnetic relaxation (aging), memory effects and temperature…
The structural and magnetic properties of ZnFe2O4 nanoparticles embedded in a non-magnetic ZnO matrix are presented. X-ray diffractograms and Transmission Electron Microscopy (TEM) images showed that the resulting samples are composed of…
Multiferroic BaMnF$_4$ powder were prepared by hydrothermal method. Hysteretic field dependent magnetization curve at 5 K confirms the weak ferromagnetism aroused from the canted antiferromagnetic spins by magnetoelectric coupling. The…
Magnetic nanoparticles (NP) of magnetite (Fe3O4) coated with oleic acid (OA) and dodecanoic acid (DA) were synthesized and investigated through Transmission Electron Microscopy (TEM),magnetization M, and ac magnetic susceptibility…
Using microemulsion methods, CoO-Pt core-shell nanoparticles (NPs), with diameters of nominally 4 nm, were synthesized and characterized by high-resolution transmission electron microscopy (HRTEM) and a suite of x-ray spectroscopies,…
ZnO nanoparticles with Wurtzite structure were prepared by chemical methods at low temperature in aqueous solution. Nanoparticles are in the range from about 10 to 30 nm. Ferromagnetic properties were observed from 2 K to room temperature…
Temperature and field-dependent magnetization $M(H,T)$ measurements and neutron scattering study of a single crystal CeSb$_2$ are presented. Several anomalies in the magnetization curves have been confirmed at low magnetic field, i.e., 15.6…
Nd_0.5 Ca_0.5 MnO_3 (NCMO) nanoparticles (average diameter ~ 20 and 40 nm) are synthesized by polymeric precursor sol-gel method and characterized by X- ray diffraction, transmission electron microscopy (TEM), selective area electron…
Magnetic relaxation in antiferromagnetic CoRh$_2$O$_4$ nanoparticles is investigated at 2 K by cooling the sample from a temperature (70 K) well above the antiferromagnetic ordering temperature at 27 K, following zero field cooled (ZFC) and…
We report the magnetic properties of magnetic nano-composite, consisting of different quantity of NiFe2O4 nanoparticles in polymer matrix. The nanoparticles exhibited a typical magnetization blocking, which is sensitive on the variation of…
Magnetic properties with 3 different sizes of Ni nanochains, synthesized by a technique of wet chemical solution, have been investigated experimentally. The sample sizes are 50 nm, 75 nm, and 150 nm with a typical length of a few microns.…
The origin of room temperature (RT) ferromagneticlike behavior in ZnO-based diluted magnetic semiconductors is still an unclear topic. The present work concentrates on the appearance of RT magnetic moments in just mixed ZnO/Co3O4 mixtures…
A neutron scattering investigation of the magnetoelectric coupling in PbFe_{1/2}Nb_{1/2}O_{3} (PFN) has been undertaken. Ferroelectric order occurs below 400 K, as evidenced by the softening with temperature and subsequent recovery of the…