相关论文: Effects of Iodine Annealing on Fe1+yTe0.6Se0.4
It has been clarified that bulk superconductivity in Fe$_{1+y}$Te$_{0.6}$Se$_{0.4}$ can be induced by annealing in an appropriate atmosphere to remove the harmful effects of excess iron. In order to clarify the details of the annealing…
Iron chalcogenide Fe(Te,Se) attracted much attention due to its simple structure, which is favorable for probing the superconducting mechanism. Its less toxic nature compared with iron arsenides is also advantageous for applications of…
Superconductivity in anti-PbO-type iron chalcogenides Fe1-xTe1-ySey (x = 0, 0.1, y = 0.1 0.4) depends on the amount (x) of interstitial iron atoms located between the FeTe1-ySey layers. Non-superconducting samples of nominal Fe1.1Te1-ySey…
We report a detailed study of the Te vapor annealing effect in Fe$_{1+y}$Te$_{0.6}$Se$_{0.4}$ single crystals. Bulk superconductivity can be gradually induced by annealing with increasing amount of Te, until the molar ratio of Te to the…
We have systematically investigated and compared different methods to induce superconductivity in iron chalcogenide Fe1+yTe0.6Se0.4 including annealing in vacuum, N2, O2, I2 atmosphere, and immersing samples into acid and alcoholic…
For the Fe-based superconductor Fe{1+y}Te{1-x}S{x}, superconductivity is induced by annealing treatment in oxygen atmosphere, whereas as-grown samples do not show superconductivity. We have investigated the sample-size dependence of…
Experimental evidences from transport, magnetic, and magneto-optical (MO) image measurements confirmed that arsenic (As) vapor annealing was another effective way to induce bulk superconductivity with isotropic, large, and homogenous…
We reported a controllable way of removing excess Fe in Fe1+yTe0.6Se0.4 by annealing in a fixed amount of O2. Compared with the weak superconductivity induced by dilute acids, O2 annealing can successfully induce bulk superconductivity.…
In the layered iron-based superconductor YFe2Ge2, a high Sommerfeld ratio of ~100 mJ/molK^2 and a T^(3/2) temperature dependence of the electrical resistivity at low temperature T indicate strong electronic correlations and point towards an…
The effect of vacuum annealing on superconductivity is investigated in Fe(Se,Te) single crystals. It is found that superconductivity is not enhanced by annealing under high vacuum (~ 10^(-3) Pa) or by annealing in a sealed evacuated quartz…
Superconductivity with zero resistance transition temperature (Tc) up to 8.4 K and 8.3 K can be obtained by doping cobalt and sodium in alfa-FeSe with the nominal composition of Fe0.92Co0.08Se and Na0.1FeSe, respectively. The electrical…
Single crystalline FeTe$_{0.61}$Se$_{0.39}$ with a sharp superconducting transition at $T_{\textrm{c}} \sim$ 14 K is synthesized via slow furnace cooling followed by low-temperature annealing. The effect of annealing on the chemical and…
Thermal conductivity measurements in magnetic fields have been carried out for FeSe$_{0.3}$Te$_{0.7}$ single crystals as-grown and annealed at 400 {\degree}C for 100 h in vacuum ($\sim$ 10$^{-4}$ Pa). It has been found that the thermal…
We have systematically investigated the annealing effect on the superconductivity of iron chalcogenide Fe1+y(Te1-xSex). The atmospheres used for annealing include O2, N2, I2 vapor, air and vacuum. We observed that annealing in O2, I2 and…
Superconductivity has been explored in single crystals of the Ni-doped FeAs-compound SrFe2-xNixAs2 grown by self-flux solution method. The antiferromagnetic order associated with the magnetostructural transition of the parent compound…
We have successfully grown single crystalline NaFeAs with cobalt or phosphor doping. Bulk superconductivity occurs in NaFe$_{0.95}$Co$_{0.05}$As at 19 K while much higher transition temperature is observed in NaFeAs$_{0.8}$P$_{0.2}$, in…
We reported that bulk superconductivity in Fe$_{1+y}$Te$_{1-x}$Se$_{x}$ can be induced by annealing in Se and S vapor. The well-annealed samples show a large critical current density, emph{J}$_c$ $\sim$ 2 - 4 $\times$ 10$^5$ A/cm$^2$.…
The superconducting properties of polycrystalline Sr0.6K0.4Fe2As2 were strongly influenced by Ag doping (Supercond. Sci. Technol. 23 (2010) 025027). Ag addition is mainly dominated by silver diffusing, so the annealing process is one of the…
Co-doped BaFe2As2 has been previously shown to have an unusually significant improvement of Tc (up to 2 K, or almost 10%) with annealing 1-2 weeks at 700 or 800 C, where such annealing conditions are insufficient to allow significant atomic…
Since the discovery of superconductivity at 26 K in oxy-pnictide LaFeAsO1-xFx, enormous interests have been stimulated in the field of condensed matter physics and material sciences. Among the many kind of structures in the iron pnictide…