Using microemulsion methods, CoO-Pt core-shell nanoparticles (NPs), with diameters of nominally 4 nm, were synthesized and characterized by high-resolution transmission electron microscopy (HRTEM) and a suite of x-ray spectroscopies,…
We present a systematic study of core-shell Au/Fe_3O_4 nanoparticles produced by thermal decomposition under mild conditions. The morphology and crystal structure of the nanoparticles revealed the presence of Au core of <d> = (6.9\pm 1.0)…
The role of particle size distribution inherently present in magnetic nanoparticles (NPs) is examined in considerable detail in relation to the measured magnetic properties of oleic acid-coated maghemite ({\gamma}-Fe$_2$O$_3$) NPs.…
Magnetic properties with 3 different sizes of Ni nanochains, synthesized by a technique of wet chemical solution, have been investigated experimentally. The sample sizes are 50 nm, 75 nm, and 150 nm with a typical length of a few microns.…
Iron oxide nano particles with nominal Fe2O3 stoichiometry were synthesized by a wet, soft chemical method with the heat treatment temperatures from 250{\deg}C to 900{\deg}C in air. The variation in the structural properties of the nano…
We report the synthesis of Co2FeGa/SiO2 nanoparticles by sol-gel method and characterization using x-ray diffraction (XRD), transmission electron microscopy (TEM) and magnetic measurements. The Rietveld refinements of XRD data with space…
Magnetic nanoparticles of La0.67Sr0.33MnO3 (LSMO) manganite with mean particle sizes of 13, 16, 18 and 21 nm were prepared by the sol-gel method. The crystal structure and mean particle size of the synthesized powders were estimated by…
Magnetic nanoparticles (NP) of magnetite (Fe3O4) coated with oleic acid (OA) and dodecanoic acid (DA) were synthesized and investigated through Transmission Electron Microscopy (TEM),magnetization M, and ac magnetic susceptibility…
In this work, the structural and magnetic properties of the gold-coated FePt nanoparticles synthesized from high-temperature solution phase are presented. The amount of gold was optimized to obtain most of the FePt particles coated. The…
Magnetic particle hyperthermia, in which colloidal nanostructures are exposed to an alternating magnetic field, is a promising approach to cancer therapy. Unfortunately, the clinical efficacy of hyperthermia has not yet been optimized.…
We carried out detailed studies of the magnetic structure, magnetoelastic coupling, and thermal properties of EuCrO$_3$ nano-powders from room temperature to liquid helium temperature. Our neutron powder diffraction and X-ray powder…
Magnetic nanoparticles of gamma-Fe2O3 coated by organic molecules and suspended in liquid and solid matrices, as well as a non-diluted magnetic fluid have been studied by electron magnetic resonance (EMR) at 77-380 K. Slightly asymmetric…
Fe2O3 nanoparticles of different sizes ranging from 22 to 56nm were synthesized chemically by a modified sol-gel method. Pure alpha phase particles as well as particles with admixture of alpha and gamma phase were obtained and identified by…
We report a systematic study on the structural and magnetic properties of Co_{x}Fe_{3-x}O_{4} magnetic nanoparticles with sizes between $5$ to $25$ nm, prepared by thermal decomposition of Fe(acac)_{3} and Co(acac)_{2}. The large…
The magnetization (M) as a function of temperature (T) from 2 to 300 K and in-plane field (H) up to 1 kOe, room temperature easy and hard direction in-plane field hysteresis loops for fields between -100 and +100 Oe, and 10 GHz…
Structural, magnetic and electronic structural properties of Ni0.2Cd0.3Fe2.5-xAlxO4 ferrites nanoparticles have been studied x-ray diffraction (XRD), transmission electron microscopy (TEM), dc magnetization, and near edge x-ray absorption…
Co2FeAl (CFA) nanoparticles (NPs) of different sizes were synthesized by chemical route. The effect of the size of NPs upon the structure and magnetization compared to its bulk counterpart was investigated. The structure and composition…
Coupling at the interface of core/shell magnetic nanoparticles is known to be responsible for the exchange bias (EB) and the relative sizes of core and shell components are supposed to influence the associated phenomenology. In this work,…
We investigate the spatial distribution of spin orientation in magnetic nanoparticles consisting of hard and soft magnetic layers. The nanoparticles are synthesized in a core / shell spherical morphology where the magnetically hard, high…
We present a study of magnetic properties of single-crystal Co3O4 nanowires with diameter about 7 nm. The nanowires expose (111) planes composed of plenty of Co3+ cations and exhibit two N\'eel temperatures at 56 K (TN of wire cores) and 73…