An improved nanopatterning procedure has been developed to obtain YBCO nanowires with cross sections as small as 50x50 nm^2, protected by an Au capping layer. To probe the effective role of the Au protecting layer, we have measured the…
Significant progress has been made in the development of superconducting quantum circuits, however new quantum devices that have longer decoherence times at higher temperatures are urgently required for quantum technologies. Superconducting…
We present results on ultra low noise YBa$_2$Cu$_3$O$_{7-\delta}$ nano Superconducting QUantum Interference Devices (nanoSQUIDs). To realize such devices, we implemented high quality YBCO nanowires, working as weak links between two…
We have grown and characterized 30 nm thick YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) films, deposited by pulsed laser deposition on both MgO (110) and SrTiO$_3$ (001) substrates, which induce opposite strain to the superconducting layer. By…
Materials of the Y-Ba-Cu-O (melt-textured YBa2Cu3O7-d-based materials or MT-YBCO) and Mg-B-O (MgB2-based materials) systems with high superconducting performance, which can be attained due to the formation of regularly distributed…
The fabrication of free-standing ultra-thin films from high-temperature (high-Tc) superconductors is of great interest for the development of superconducting nanowire single-photon detectors with high operating temperatures. We successfully…
The influence of adding 23 nm NiO nanoparticles on the magnetic hysteresis loops and critical current density of the high-temperature superconductor YBa2Cu3O7-d has been investigated. The samples were prepared using a fast annealing method…
High-temperature superconducting YBa2Cu3O7-d (YBCO) thin-film detectors with improved responsivities were developed for fast time-domain measurements in the THz frequency range. YBCO thin films of 30 nm thickness were patterned to micro-…
Superconducting nanowires undergoing quantum phase-slips have potential for impact in electronic devices, with a high-accuracy quantum current standard among a possible toolbox of novel components. A key element of developing such…
Continuous Nb wires, 7-15 nm in diameter, have been fabricated by sputter-coating single fluorinated carbon nanotubes. Transmission electron microscopy revealed that the wires are polycrystalline, having grain sizes of about 5 nm. The…
Superconducting nanowires are very important due to their applications ranging from quantum technology to astronomy. In this work, we implement a non-invasive process to fabricate nanowires of high-$T_\text{c}$ superconductor…
Much smoother surfaces and significantly improved superconducting properties of relatively thick YBa2Cu3O7 (YBCO) films have been achieved by introducing a multilayered structure with alternating main YBCO and additional NdBCO layers. The…
We report a simple and easily controllable method where a nano-undulated surface morphology of Nd1/3Eu1/3Gd1/3Ba2Cu3Ox (NEG) films leads to a substantial increase in the critical current density in superconducting YBa2Cu3Ox (YBCO) films…
Cuprate high-temperature superconductors, such as Yttrium Barium Copper Oxide (YBCO), are extremely promising for emerging technologies such as low-power computing, data storage, quantum sensors and superconducting electronics. However, the…
The critical current density of epitaxial YBCO films grown on vicinal SrTiO3 substrates was investigated by electrical transport measurements along and across the steps of the SrTiO3 surface for a range of temperatures of 10 K to 85 K and…
We report on the growth and characterization of ultrathin YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) films on MgO (110) substrates, which exhibit superconducting properties at thicknesses down to 3 nm. YBCO nanowires, with thicknesses down to 10 nm…
We present a detailed report of microwave irradiation of ultra-narrow superconducting nanowires. In our nanofabricated circuits containing a superconducting NbSi nanowire, a dc blockade of current flow was observed at low temperatures below…
Superconducting thick films (200$\mu$m-300$\mu$m) of YBCO have been fabricated successfully on MgO substrates by a new approach. The precursor powders (YBa2Cu3O7-$\delta$(Y123)+0.1molY2BaCuO5(Y211)) are placed between two MgO (10mm x 10mm)…
Dissipation-free current transport in high-temperature superconductors is one of the most crucial properties of this class of materials which is directly related to the effective inhibition of flux line movement by defect structures. In…
The observation that the thermal conductivity of single-crystalline silicon nanowires with diameter on the length scale of 25 nm is lower than that of bulk material by two orders of magnitude has attracted the interest onto silicon as a…