相关论文: Electrochemical synthesis of iron-based supercondu…
Superconductivity is successfully induced by utilizing a battery-like reaction found in a typical Li-ion battery. Excess Fe in FeTe0.8S0.2 is electrochemically de-intercalated by applying a voltage in a citric acid solution. The…
We demonstrate the successful fabrication on CaF$_2$ substrates of FeSe$_{1-x}$Te$_{x}$ films with $0 \le x \le 1$, including the region of $0.1 \le x \le 0.4$, which is well known to be the "phase-separation region", via pulsed laser…
(NaxKy)FezSe2 crystals are prepared by Na, Fe, and Se as starting materials in NaCl/KCl flux at low temperatures~720 {\deg}C. It is found that K is more preferred than Na to enter in between FeSe layers and forms the phase. Thus-obtained…
This work reports studies performed in the superconducting compound FeSe0:5Te0:5 under high pressure. Changes were observed in the transition temperature, superconducting critical fields,anomalous variations in the Meissner fraction, and in…
High-quality FeSe tapes have been prepared by using a diffusion method. By adjusting the reaction temperature and the thickness systematically, a transport critical current density as high as 600 A/cm2 at 4.2 K under self field is achieved.…
Superconducting FeSe0.8Te0.2 thin films on SrTiO3, LaAlO3 and CaF2 substrates were electrochemically etched in an ionic liquid DEME-TFSI electrolyte with a gate bias of 5 V. Superconductivity at 38 K was commonly observed on all substrates…
We report here that a new superconducting phase with much higher Tc has been found in K intercalated FeSe compound with excess Fe. We successfully grew crystals by precisely controlling the starting amount of Fe. Besides the superconducting…
We have fabricated thin films of FeTe$_{1-x}$Se$_x$ using a scotch-tape method. The superconductivities of the thin films are different from each other although these films were fabricated from the same bulk sample. The result clearly…
Single-layer FeSe films with extremely expanded in-plane lattice constant of 3.99A are fabricated by epitaxially growing FeSe/Nb:SrTiO3/KTaO3 heterostructures, and studied by in situ angle-resolved photoemission spectroscopy. Two elliptical…
We fabricated single- and 3-core superconducting Fe-Se wires using a novel process based on a chemical transformation from hexagonal FeSe1+d (non-superconducting) to tetragonal FeSe (superconducting) via an optimal supply of Fe from the Fe…
Epitaxial Fe(Se,Te) thin films were prepared by pulsed laser deposition on (La0.18Sr0.82)(Al0.59Ta0.41)O3 (LSAT), CaF2-buffered LSAT and bare CaF2 substrates, which exhibit an almost identical in-plane lattice parameter. The composition of…
The transition from insulator to superconductor was achieved in the non-superconducting FeSe ultrathin film via simple Mg coating technique in present work. It was found that in non-superconducting FeSe ultrathin film without Mg coating,…
This article reviews recent experimental investigations on two binary Fe-chalcogenides: FeSe and Fe$_{1+y}$Te. The main focus is on synthesis, single crystal growth, chemical composition, as well as on the effect of excess iron on…
The FeSe samples in the form of polycrystals, single crystals and thin films have been prepared and characterized. The synthesized material has been hot isostatically pressed under pressure of 0.45 GPa of 5N purity argon with the use of the…
We have fabricated the Fe(Se, Te) superconducting wire by a special process based on a powder-in-tube method. The pure Fe tube plays the role of not only the sheath but also the raw material for synthesizing the superconducting phases. We…
Hydrothermal synthesis is described of layered lithium iron selenide hydroxides Li1-xFex(OH)Fe1-ySe (x ~ 0.2; 0.02 < y < 0.15) with a wide range of iron site vacancy concentrations in the iron selenide layers. This iron vacancy…
In this study, we investigated the gate voltage dependence of $T_{\mathrm c}$ in electrochemically etched FeSe films with an electric-double layer transistor structure. The $T_{\mathrm c}^{\mathrm {zero}}$ value of the etched FeSe films…
The beta-modification of FeSe, which has an anti-PbO type structure, achieves superconductivity at 8 K without external doping or pressure and exhibits a nematic phase, which has been crucial for studies of unconventional pairing…
Solvothermal intercalation of ethylenediamine molecules into FeSe separates the layers by 1078 pm and creates a different stacking. FeSe(en)0.3 is not superconducting although each layer exhibits the stripe-type crystal structure and the…
The presumably unconventional superconductor Beta-FeSe was deposited by radio frequency sputtering and molecular beam epitaxy (MBE) from two elementary sources. Superconducting thin films were grown in (001)-orientation on MgO(100) and…