In recent decades, the growth of ultrathin epitaxial bismuth (Bi) films on various substrates has garnered interest due to their unique electronic properties. We report upon the growth and electrical transport properties of epitaxial Bi…

Single crystals of the Ni-doped FeAs-based superconductor SrFe2-xNixAs2 were grown using a self-flux solution method and characterized via x-ray measurements and low temperature transport, magnetization, and specific heat studies. A doping…

Over the last decade advances in high temperature superconducting (HTS) materials have generated a renewed optimism in the use of this technology in future high-power applications including motors, generators, and power transmission. The…

Single-layer FeSe films grown on (001) SrTiO3 substrates have shown a significant increase in superconducting transition temperature compared to bulk FeSe. Several mechanisms have been proposed to explain such enhancement, including…

We report comprehensive resistivity measurements of single crystalline samples of the Ba(Fe(1-x)Co(x))2As2 high Tc superconductor under hydrostatic pressure up to 2.75 GPa and over a broad concentration range, 0 < x < 0.099. We show that…

In-situ epitaxial growth of FeSe$_{0.5}$Te$_{0.5}$ thin films is demonstrated on a non-oxide substrate CaF$_2$. Structural analysis reveals that compressive stress is moderately added to 36-nm thick FeSe$_{0.5}$Te$_{0.5}$, which pushes up…

We have successfully synthesized a new superconducting phase of FeTe1-xSx with a PbO-type structure. It has the simplest crystal structure in iron-based superconductors. Superconducting transition temperature is about 10 K at x = 0.2. The…

We use Ar-ion milling to thin Bi2212 single crystals down to a few nanometers or one-to-two (CuO2)2 layers. With decreasing the thickness, superconducting transition temperature gradually decreases to zero and the in-plane resistivity…

Superconducting thin films have been prepared on Si-substrates, using pulsed laser deposition from a target composed of a mixture of Mg and MgB2 powders. The films were deposited at room temperature and post-annealed at 600 degrees C. The…

We report the realization of superconductivity by 5d element Ir doping in LaFeAsO, a prototype parent compound of high-temperature iron based superconductors. X-ray diffraction patterns indicate that the material has formed the…

Localized high frequency (several GHz) electrodynamic properties of a high quality epitaxial, single-crystal Iron-Pnicitde Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$ thin film near optimal doping (x=0.08) are measured under a localized and strong RF…

We report single-crystal growth of La$_{0.34}$Na$_{0.66}$Fe$_2$As$_2$ iron-based superconductor with the size of several millimeters. The samples were accidentally obtained in trying to grow LaFeAsO$_{1-y}$F$_y$ ( $y \geq$ 0.8 ) single…

The recently discovered LaFe2As2 superconducting compound, member of the 122 family of iron pnictide superconductors, becomes superconducting below Tc=13K, yet its nominal doping apparently places it in the extreme overdoped limit, where…

The industrial manufacturing of the long-length iron-pnictide wires and tapes requires simple and low-cost technology. Although the transport critical current density of the FeAs-122 tapes has already achieved the practical application…

High pressure electrical resistance and x-ray diffraction measurements have been performed on ruthenium-doped Ba(Fe0.9Ru0.1)2As2, up to pressures of 32 GPa and down to temperatures of 10 K, using designer diamond anvils under…

Titanium nitride is a material of interest for many superconducting devices such as nanowire microwave resonators and photon detectors. Thus, controlling the growth of TiN thin films with desirable properties is of high importance. In…

Nb-doped SrTiO$_{3}$ epitaxial thin films have been prepared on (001) SrTiO$_{3}$ substrates using pulsed laser deposition. A high substrate temperature ($>1000^{\circ}{C}$) was found to be necessary to achieve 2-dimensional growth. Atomic…

We report strain engineering of superconductivity in RuO$_2$ singlecrystalline films, which are epitaxially grown on rutile TiO$_2$ and MgF$_2$ substrates with various crystal orientations. Systematic mappings between the superconducting…

We report on the electrical properties of polycrystalline NbO2 thin film vertical devices grown on TiN coated SiO2/Si substrates using pulsed laser deposition. First, we analyzed the thickness and contact size dependences of threshold…

Single crystals of Ba_{1-x}Rb_{x}Fe_2As_2 with x=0.05-0.1 have been grown from Sn flux and are bulk superconductors with T_c up to 23 K. The crystal structure was determined by X-ray diffraction analysis, and Sn is found to be incorporated…