We report a direct current transport study of the local intergrain connections in a polycrystalline SmFeAsO0.85 (Sm1111) bulk, for which we earlier estimated significant intergranular critical current density Jc. Our combined low…
Early studies have found quasi-reversible magnetization curves in polycrystalline bulk rare-earth iron oxypnictides that suggest either wide-spread obstacles to intergranular current or very weak vortex pinning. In the present study of…
A series of polycrystalline SmFeAs1-xOx bulks was prepared to systematically investigate the influence of sample density on flux pinning properties. Different sample densities were achieved by controlling the pelletizing pressure. The…
In order to understand why the inter- and intra-granular current densities of polycrystalline superconducting oxypnictides differ by three orders of magnitude, we have conducted combined magneto-optical and microstructural examinations of…
We report enhancement in the magnetic critical current density of indium added polycrystalline SmFeAsO1-xFx. The value of magnetic Jc is around 25 kA/cm2 at 4.2 K under self-magnetic field. Polycrystalline SmFeAsO1-xFx is mainly composed of…
Superconducting technology provides most sensitive field detectors, promising implementations of qubits and high field magnets for medical imaging and for most powerful particle accelerators. Thus, with the discovery of new superconducting…
SmFeAsO and the isostructural superconducting SmFeAs(O0.93F0.07) samples were prepared. Characterization by means of Rietveld refinement of X-ray powder diffraction data, scanning electron microscope observation, transmission electron…
Hot Isostatic Pressing was applied to synthesize bulk samples with diameter up to 30 mm starting with Alfa Aesar magnesium diboride powder. HIPing at 2 kbar, 1000 C with cooling under pressure (DMCUP cycle) resulted in a fully dense (or low…
A series of polycrystalline SmO1-xFxFeAs bulks (x=0.15, 0.2, 0.3 and 0.4) were prepared by the conventional solid state reaction. Resistivity, susceptibility, magnetic hysteresis, critical current density and microstructure of these samples…
SmFeAsO1-xFx (Sm1111) tapes were prepared by an ex-situ powder-in-tube method with a Sn-presintering process. Scanning electron microscopy revealed apparent difference in microstructure between Sn-presintered tapes and the previously…
The new rare-earth arsenate superconductors are layered, low carrier density compounds with many similarities to the high-Tc cuprates. An important question is whether they also exhibit weak-coupling across randomly oriented…
In this study, the impurity concentration and magnetic response of nine highly oriented pyrolytic graphite (HOPG) samples with different grades and from different providers were determined using ion beam microscopy and SQUID magnetometry.…
We report about muSR measurements on SmFeAsO1-xFx which helped us to identify the signature of diluted ferromagnetic inclusions, ubiquitous in the iron pnictides. These impurities are characterized by a Curie temperature close to room…
We present a set of experimental results concerning the power spectrum of current noise, detected on a granular high Tc superconductor submitted either to a slowly varying magnetic field or to a varying current intensity. Experiments were…
This work studies the influence of microstructures and crystalline defects on the superconductivity of MgB2, with the objective to improve its flux pinning. A MgB2 sample pellet that was hot isostatic pressed (HIPed) was found to have…
The distribution of magnetic field in single-phase polycrystalline bulk MgB2 has been measured using a Magneto-Optical (MO) technique for an external magnetic field applied perpendicular to the sample surface. The MO studies indicate that…
In a wide variety of materials, such as copper oxides, heavy fermions, organic salts, and the recently discovered iron pnictides, superconductivity is found in close proximity to a magnetically ordered state. The character of the proximate…
The magnetization of the PrFeAsO$_{0.60}$F$_{0.12}$ polycrystalline sample has been measured as functions of temperature and magnetic field $(H)$. The observed total magnetization is the sum of a superconducting irreversible magnetization…
Polycrystalline samples and single crystals of SmFeAs1-xPxO1-y were synthesized and grown employing different synthesis methods and annealing conditions. Depending on the phosphorus and oxygen content, the samples are either magnetic or…
BaFe2As2 (Ba-122) and (Ba0.6K0.4)Fe2As2 (K-doped Ba-122) powders were successfully synthesized from the elements using a reaction method, which incorporates a mechanochemical reaction using high-impact ball milling. Mechanically-activated,…