To elucidate the mechanism as to why alcoholic beverages can induce superconductivity in Fe_{1+d}Te_{1-x}S_x samples, we performed component analysis and found that weak acid such as organic acid has the ability to induce superconductivity.…
The red wine dependence of superconductivity in FeTe0.8S0.2 was investigated. Samples with a higher shielding volume fraction had a tendency to show a higher concentration of tartaric acid in red wine. We found the tartaric acid is one of…
Superconductivity in polycrystalline Fe1+dTe0.9Se0.1 was enhanced by heating in alcoholic beverages. We found that part of the excess Fe was deintercalated from the interlayer sites by the treatment and the shielding volume fractions were…
Superconductivity in FeTe0.8S0.2 is successfully induced by an electrochemical reaction using an ionic liquid solution. A clear correlation between the Fe concentration in the solution and the manifestation of superconductivity was…
We have systematically investigated and compared different methods to induce superconductivity in iron chalcogenide Fe1+yTe0.6Se0.4 including annealing in vacuum, N2, O2, I2 atmosphere, and immersing samples into acid and alcoholic…
Moisture-induced superconductivity was observed in FeTe0.8S0.2. With exposing the sample to the air, the zero resistivity temperature and the superconducting volume fraction were enhanced up to 7.2 K and 48.5 %, respectively, while the…
Superconductivity is successfully induced by utilizing a battery-like reaction found in a typical Li-ion battery. Excess Fe in FeTe0.8S0.2 is electrochemically de-intercalated by applying a voltage in a citric acid solution. The…
We report superconductivity induced in films of the non-superconducting, antiferromagnetic parent material FeTe by low temperature oxygen incorporation in a reversible manner. X-ray absorption shows that oxygen doping changes the nominal Fe…
Superconductivity with zero resistance transition temperature (Tc) up to 8.4 K and 8.3 K can be obtained by doping cobalt and sodium in alfa-FeSe with the nominal composition of Fe0.92Co0.08Se and Na0.1FeSe, respectively. The electrical…
A new hight Tc Fe-based compound system, AFe2As2 with A = K, Cs, K/Sr and Cs/Sr has been found. Through electron-doping, Tc of the A = K and Cs compounds rises to ~37 K, and finally enter a spin-density-wave state (SDW) through further…
CaFe$_2$As$_2$ has been found to be exceptionally sensitive to the application of hydrostatic pressure and superconductivity has been found to exist in a narrow pressure region that appears to be at the interface between two different phase…
Superconductivity of Fe0.95Te0.85S0.15 was induced and enhanced by immersing the as-grown (non-superconducting) sample into sulfuric acid. Dissolved Fe was detected in the sulfuric acid treatment, indicating that excess Fe was removed from…
We report the study of the cocktail effect on superconductivity in high-entropy alloys (HEAs),using hexagonal close-packed HEAs as a prototype system. Compared with the compositional averages of the constituent elements, the superconducting…
We report protonation in several compounds by an ionic-liquid-gating method, with optimized gating conditions. This leads to single superconducting phases for several compounds. Non-volatility of protons allow post-gating magnetization and…
By using solid state reaction method, we have synthesized the Pd-doped superconductor SrFe2-xPdxAs2. The systematic evolution of the lattice constants indicated that the Fe ions were successfully replaced by the Pd. By increasing the doping…
Co-doping of lanthanum and phosphorus in CaFe2As2 induces superconductivity at 45 K. This superconducting transition temperature is higher than the 38 K transition in Ba1-xKxFe2As2, which is the maximum found thus far among the 122 phases.…
The bulk polycrystalline sample FeSe1/2Te1/2 is synthesized by solid state reaction route in an evacuated sealed quartz tube at 750 oC. The presence of superconductivity is confirmed through magnetization/thermoelectric/resistivity studies.…
It has been considered that FeAs-based high transition temperature (high-Tc) superconductors need electron or hole doping by aliovalent ion substitution or large off-stoichiometry in order to induce superconductivity. We report that…
We report the interplay between charge-density-wave (CDW) and superconductivity of 1$T$-Fe$_{x}$Ta$_{1-x}$S$_{2}$ ($0\leq x \leq 0.05$) single crystals. The CDW order is gradually suppressed by Fe-doping, accompanied by the disappearance of…
We investigate the possibility of achieving high-temperature superconductivity in hydrides under pressure by inducing metallization of otherwise insulating phases through doping, a path previously used to render standard semiconductors…