相关论文: Evidence for multiple gaps in specific heat of LiF…

Low-temperature specific heat (SH) is measured on the 1111-type CaFe_{0.88}Co_{0.12}AsF single crystals under different magnetic fields. A clear SH jump with the height \Delta C/T|_Tc = 10.4 mJ/mol K^2 was observed at the superconducting…

We present specific heat, c_P, and ARPES data on single crystals of the stoichiometric superconductor LiFeAs. A pronounced anomaly is found in c_P at the superconducting transition. The electronic contribution can be described by two s-type…

Low-temperature specific heat was measured on the BaFe1.9Ni0.1As2 single crystals with critical transi-tion temperature Tc = 20.1 K. A clear specific heat jump with the value \DeltaC/T|Tc \approx 23 mJ/mol K^2 has been observed. In…

We report specific heat capacity measurements on a LiFeAs single crystal at temperatures down to 400 mK and magnetic fields up to 9 Tesla. A small specific heat jump at Tc and finite residual density of states at T=0 K in the…

The specific heat of high-purity $\rm Ba_{0.68}K_{0.32}Fe_2As_2$ single crystals with the highest reported superconducting $T_c$ = 38.5 K was studied. The electronic specific heat, $C_p$, below $T_c$ shows two gap features, with $\Delta_1…

Using a differential technique, we have measured the specific heats of polycrystalline Ba1-xKxFe2As2 samples with x=0, 0.1 and 0.3, between 2K and 380K and in magnetic fields 0 to 13 Tesla. From this data we have determined the electronic…

We report low-temperature specific heat measurements for high-quality single crystalline KFe2As2 (T_c about 3.5 K). The investigated zero-field specific heat data yields an unusually large nominal Sommerfeld coefficient gamma_n of 94(3)…

LiFeAs is one of the new class of iron superconductors with a bulk onset Tc in the 15-17 K range. We report on the specific heat characterization of single crystal material prepared from self-flux growth techniques with significantly…

The specific heat $C(T)$ of BaFe$_2$As$_2$ single crystal, electron-doped Ba$_{0.7}$La$_{0.3}$Fe$_2$As$_2$ and hole-doped Ba$_{0.5}$K$_{0.5}$Fe$_2$As$_2$ polycrystals were measured. For undoped BaFe$_2$As$_2$ single crystal, a very sharp…

We present detailed heat capacity measurements for Ba(Fe(1-x)Cox)2As2 and Ba(Fe(1-x)Nix)2As2 single crystals in the vicinity of the superconducting transitions. The specific heat jump at the superconducting transition temperature (Tc),…

The pairing symmetry in the iron-based superconductor Ba1-xKxFe2As2 may change from nodeless s-wave near x~0.4 and Tc>30 K, to nodal (either d-wave or s-wave) at x=1 and Tc<4 K. Theoretical interest has been focused on this possibility,…

The heat capacity of a 2H-NbS2 single crystal has been measured by a highly sensitive ac technique down to 0.6 K and in magnetic fields up to 14 T. At very low temperatures data show excitations over an energy gap (2DS/kBTc \approx 2.1)…

The specific heat of single crystal hole-doped Ca0.33Na0.67Fe2As2, Tc(onset)=33.7 K, was measured from 0.4 to 40 K. The discontinuity in the specific heat at Tc, deltaC, divided by Tc is 105 +- 5 mJ/molK2, consistent with values found…

We investigate the electronic properties and the superconducting gap characteristics of a single crystal of hole-doped 122 Fe-pnictide Ba$_{0.65}$Na$_{0.35}$Fe$_2$As$_2$ by means of specific heat measurements. The specific heat exhibits a…

Low-temperature specific heat is measured on the overdoped Ba(Fe_{1-x}Co_x)_2As_2 (x = 0.13) single crystal under magnetic fields along three different directions. A clear anisotropy is observed on the field dependent electronic specific…

Low temperature specific heat (SH) was measured on the FeAs-based superconducting single crystals Ba$_{0.6}$K$_{0.4}$Fe$_2$As$_2$ and high pressure synthesized polycrystalline samples SmFeAsO$_{0.9}$F$_{0.1}$. It is found that the sharp SH…

The in- and out-of-plane lower critical fields and magnetic penetration depths for LiFeAs were examined. The anisotropy ratio $\gamma_{H_{c1}}(0)$ is smaller than the expected theoretical value, and increased slightly with increasing…

The in-plane thermal conductivity $\kappa$ of overdoped FeAs-based superconductor BaFe$_{1.73}$Co$_{0.27}$As$_2$ ($T_c$ = 8.1 K) single crystal was measured down to 80 mK. In zero field, the residual linear term $\kappa_0/T$ is negligible,…

We report the specific heat measurements on the newly discovered Fe-based layered superconductor LaO_0.9F_{0.1-delta}FeAs with the onset transition temperature T_c \approx 28 K. A nonlinear magnetic field dependence of the electronic…

We report on specific heat measurements on clean overdoped $\mathrm{BaFe_{2}(As_{1-x}P_x)_2}$ single crystals performed with a high resolution membrane-based nanocalorimeter. A nonzero residual electronic specific heat coefficient at zero…