One-dimensional Ni/Ni3C core-shell nanoball chains with an average diameter by around 30 nm were synthesized by means of a mild chemical solution method using a soft template of trioctylphosphineoxide (TOPO). It was revealed that the…
Monodisperse magnetite Fe3O4 nanoparticles of controlled size within 6 and 20 nm in diameter were synthesized by thermal decomposition of an iron organic precursor in an organic medium. Particles were coated with oleic acid. For all samples…
Magnetic properties with 3 different sizes of Ni nanochains, synthesized by a technique of wet chemical solution, have been investigated experimentally. The sample sizes are 50 nm, 75 nm, and 150 nm with a typical length of a few microns.…
Herein, some magnetic nanoparticles (MNP)/clay/polymer nanocomposites have been prepared, whose saturation magnetization is higher than that of pure oleic acid coated MNP component. The existence of unique 'nano-network' structure and tight…
In the pursuit of alternative and less invasive medical treatments, magnetic nanoparticles (NPs) have gained significant relevance. Iron carbides NPs stand out for their higher saturation magnetizations compared to iron oxides, while…
In this work, Pt-Ti core-shell nanoparticles (NP) of 2 nm to 3 nm in size and 30000 u \pm 1500 u as specified single particle mass, deposited on flat silicon substrates by means of a mass-selected cluster beam source, were used for the…
Some of the synthesis methods and physical properties of iron-oxide based magnetic nanoparticles such as Fe3-xO4 and CoxFe3-xO4 are reviewed because of their interest in health, environmental applications, and ultra-high-density magnetic…
We present a microscopic model for nanoparticles, of the maghemite ($\gamma $% -Fe$_{2}$O$_{3}$) type, and perform classical Monte Carlo simulations of their magnetic properties. On account of M\"{o}ssbauer spectroscopy and high-field…
We have investigated the magnetism of the bare and graphene-covered (111) surface of a Ni single crystal employing three different magnetic imaging techniques and ab initio calculations, covering length scales from the nanometer regime up…
We have developed a simple precipitation route to synthesize magnetite (Fe3O4) nano-particles with controlled size without any requirement of calcination step at high temperatures. The study of these nano-particles indicates an enhancement…
Nanoparticles (dia ~ 5 - 7 nm) of Bi_0.5 X_0.5(X=Ca,Sr)MnO_3 are prepared by polymer assisted sol-gel method and characterized by various physico-chemical techniques. X-ray diffraction gives evidence for single phasic nature of the…
Recent experiments in approximately 10nm size electrodeposited Ni-Ni nanocontacts have shown ballistic magnetoresitance values of 700% stable during a week (Garcia et al Appl. Phys. Lett. 79, 4550(2001) and very recently up to 3000% (Chopra…
Nanoparticles (NPs) which combine several magnetic phases offer wide perspectives for cutting edge applications because of the high modularity of their magnetic properties. Besides the addition of the magnetic characteristics intrinsic to…
The synthesis of Ni filled multiwalled carbon nanotubes was performed by atmospheric pressure chemical vapor deposition with propane on Si at 850 C using a simple mixture of Ni(salen), and a conventional photoresist. Analysis of the carbon…
A combinatorial thin-film synthesis approach combined with a high throughput analysis methodology was successfully applied to synthesize TiN/Ni coatings with optimum mechanical properties. The synthesis approach consists of the deposition…
The magnetic order of La0.7Sr0.3MnO3 nanoparticles (NPs) fabricated in a SPEX D8000 mill was systematically studied. The La0.7Sr0.3MnO3 nanocrystals grow from the milled constituent oxides during the milling processes. The magnetization…
We report on the effect of organic acid capping on the behavior of magnetite nanoparticles. The nanoparticles of magnetite were obtained using microwave activated process, and the magnetic properties as well as the electron magnetic…
We combine magnetometry and magnetic small-angle neutron scattering to study the influence of the microstructure on the macroscopic magnetic properties of a nanocrystalline Ni bulk sample, which was prepared by straining via high-pressure…
The finite size and surface roughness effects on the magnetization of NiO nanoparticles is investigated. A large magnetic moment arises for an antiferromagnetic nanoparticle due to these effects. The magnetic moment without the surface…
Compacted pellets of nanocrystalline nickel (NC-Ni) of average particle size ranging from 18 to 33 nm were prepared using a variety of surfactants. They were characterized well and were studied on the influence of the surfactants on the…