Magnetic dc susceptibility between 1.5 and 800 K, ac susceptibility and magnetization, thermodynamic properties, temperature dependence of radio and audio-wave dielectric constants and conductivity, contact-free dielectric constants at…
Nanoparticles of the ferrimagnetic epsilon-Fe2O3 oxide have been synthesized by sol-gel method. Here, we report on the measurements of the dielectric permittivity as a function of temperature, frequency and magnetic field. It is found that,…
Dielectric and magnetic properties of Eu0.5Ba0.25Sr0.25TiO3 are investigated between 10 K and 300 K in the frequency range from 10 Hz to 100 THz. A peak in permittivity revealed near 130 K and observed ferroelectric hysteresis loops prove…
Our measured dielectric constant and mechanical response of multiferroic BiFeO3 indicate four phase transitions below room temperature. Features correlate with those reported at 50K (from a peak in the zero-field-cooled magnetic…
We have investigated the effect of temperature on magnetic properties of Bi$_{0.9}$Gd$_{0.1}$Fe$_{1-x}$Ti$_x$O$_3$ (x = 0.00-0.20) multiferroic system. Unexpectedly, the coercive fields ($H_{c}$) of this multiferroic system increased with…
A single-phase polycrystalline La0.5Ba0.5CoO3-d sample was synthesized by microwave irradiation within 20 minutes of processing time and its structural, magnetic, electrical, and magnetostrictive properties were investigated. While the…
We report on the lattice evolution of BiFeO3 as function of temperature using far infrared emissivity, reflectivity, and X-ray absorption local structure. A power law fit to the lowest frequency soft phonon in the magnetic ordered phase…
We synthesized a series of GdFe$_{1-x}$Co$_x$AsO polycrystalline samples ($0 \leq x \leq 1$) by using a solid state reaction method and present a systematic study on the physical properties by means of electrical resistivity $\rho(T)$,…
The magnetic susceptibility between 1.5 and 800 K, the infrared reflectivity at room temperature and the temperature dependence of the dielectric constant at mm-wavelengths are reported for single crystalline BiFeO3. A well developed…
We report the response of electrical resistivity $\rho$ to the application of magnetic fields (H) up to 140 kOe in the temperature interval 1.8-300 K for the compound, Gd7Rh3, ordering antiferromagnetically below 150 K. We find that there…
The linear magnetoelectric effect was measured in 500 nm Cr2O3 films grown by rf sputtering on Al2O3 substrates between top and bottom thin film Pt electrodes. Magnetoelectric susceptibility was measured directly by applying an AC electric…
We present direct evidence of above room temperature magneto-electricity in single-phase Li0.05Ti0.02Ni0.93O with above-ambient antiferromagnetic ordering. Temperature-hysteresis in warming/cooling heat-flow thermograms establishes a…
We investigated complex magnetic properties of multifunctional LaCrO3-LaFeO3 system. The magnetic measurements substantiate the presence of competing complex magnetic ordering against temperature, showing paramagnetic to ferrimagnetic…
The multiferroic properties of EuTiO3 are greatly enhanced when a sample is strained, signifying that coupling between strain and structural, magnetic or ferroelectric order parameters is extremely important. Here resonant ultrasound…
We demonstrate room temperature ferroelectricity in the epitaxial thin films of magnetoelectric GaFeO3. Piezo-force measurements show a 180o phase shift of piezoresponse upon switching the electric field indicating nanoscale…
We have studied the magnetic and power absorption properties of three samples of CoFe2O4 nanoparticles with sizes from 5 to 12 nm prepared by thermal decomposition of Fe (acac)3 and Co(acac)2 at high temperatures. The blocking temperatures…
Room-temperature magnetoelectric multiferroicity has been observed in c-axis oriented GaFeO$_3$ thin films (space group $Pna2_1$), grown on economic and technologically important (100)Si substrates by pulsed laser deposition technique.…
We investigate the antiferromagnetic insulating nature of Ca3FeRhO6 both experimentally and theoretically. Susceptibility measurements reveal a Neel temperature T_N = 20 K, and a magnetic moment of 5.3 muB/f. u., while Moessbauer…
Magnetic and dielectric properties on a polycrystalline La0.7Bi0.3CrO3 have been investigated. A canted antiferromagnetic (CAF) phase transition giving weak ferromagnetism at TN = 230K has been observed. M-H at 10K shows non-saturating…
We provide a detailed study of the reflectivity of multiferroic TbMnO_3 for wave numbers from 40 cm^{-1} to 1000 cm^{-1} and temperatures 5 K < T < 300 K. Excitations are studied for polarization directions E || a, the polarization where…