The nonstoichiometric NaxCoO2 system exhibits extraordinary physical properties that correlate with temperature and Na concentration in its layered lattice without evident long-range structure modification when conventional crystallographic…
The sodium reordering in NaxCoO2 in the vicinity of room temperature is rationalized at high x in terms of phase transitions between square and striped phases. A striking hexagon-of-hexagons diffraction pattern observed for x=0.78 can be…
We report neutron powder diffraction measurements on a series of NaxCoO2 samples with x near 0.75 which were prepared under different synthesis conditions. Two different crystal structures for the samples are observed at room temperature.…
We have utilized neutron powder diffraction to probe the crystal structure of layered Na$_{x}$CoO$_{2}$ near the half doping composition of $x=$0.46 over the temperature range of 2 to 600K. Our measurements show evidence of a dynamic…
We report the observation of a stepwise "melting" of the low-temperature Na-vacancy order in the layered transition metal oxide Na0.7CoO2. High-resolution neutron powder diffraction indicates the existence of two first-order structural…
We report infrared spectra of a Na$_{0.5}$CoO$_2$ single crystal which exhibits a sharp metal-insulator transition near 50 K due to the formation of charge ordering. In comparison with x=0.7 and 0.85 compounds, we found that the spectral…
Single crystals of Na$_{0.5}$CoO$_2$ were obtained through a flux method followed by de-intercalation of sodium. The Na$_{0.5}$CoO$_2$ samples were found to be vulnerable to water in the air and a hydration process in which H$_2$O molecules…
Synchrotron X-ray diffraction investigations of two single crystals of Na_xCoO_2 from different batches with composition x = 0.525-0.530 reveal homogeneous incommensurate sodium ordering with propagation vector (0.53 0.53 0) at…
In the ac polarized Raman spectra of NaV2O5 we have found anomalous phonon broadening, and an energy shift of the low-frequency mode as a function of the temperature. These effects are related to the breaking of translational symmetry,…
We report a systematic study of the $c$ lattice parameter in the Na$_{x}$CoO$_{2}$ phases versus Na content $x>0.5$, in which sodium always displays ordered arrangements. This allows us to single out the first phase which exhibits an AF…
We have synthesized and characterized different stable phases of sodium cobaltates Na$_{x}$CoO$_{2}$ with sodium content $0.65<x<0.80$. We demonstrate that $^{23}$Na NMR allows to determine the difference in the susceptibility of the phases…
We have synthesized and characterized four different stable phases of Na ordered Na$_{x}$CoO$_{2}$, for $0.65<x<0.8$. Above 100 K they display similar Curie-Weiss susceptibilities as well as ferromagnetic $q=0$ spin fluctuations in the…
We have synthesized and characterized the four different stable phases of Na ordered Na$_{x}$CoO$_{2}$, for $0.65<x\lesssim 0.75$. Above 100K they display similar Curie-Weiss spin susceptibilities as well as ferromagnetic $q=0$ spin…
We prove the direct link between low temperature magnetism and high temperature sodium ordering in NaxCoO2 using the example of a heretofore unreported magnetic transition at 8 K which involves a weak ferromagnetic moment. The 8 K feature…
Raman scattering experiments on Na_{x}CoO_2 yH_2O single crystals show a broad electronic continuum with a pronounced peak around 100 cm-1 and a cutoff at approximately 560 cm-1over a wide range of doping levels. The electronic Raman…
We report the temperature-dependent synchrotron based X-ray diffraction analysis of NASICON type Na$_3$FeCr(PO$_4$)$_3$ sample, which undergoes a symmetry-lowering structural transition from a monoclinic ($C2/c$) phase with long-range…
Na$_x$CoO$_2$, the parent compound of the recently synthesized superconductor Na$_x$CoO$_2$:$y$H$_2$O, exhibits bulk antiferromagnetic order below $\sim20$ K for 0.75 $\leq x \leq$ 0.9. We have performed neutron scattering experiments in…
The influence of electrostatic interactions on the ordering of sodium ions in Na$_x$CoO$_2$ is studied theoretically through Monte-Carlo simulations. For large $x$ small di- or tri-vacancy clusters are stable with respect to isolated Na…
Phase diagram of Na$_x$CoO$_2$ (x $\gtrsim$ 0.71) has been reinvestigated using electrochemically fine tuned single crystals. Both phase separation and staging phenomena as a result of sodium multi-vacancy cluster ordering have been found.…
NaxCoO2 has emerged as a material of exceptional scientific interest due to the potential for thermoelectric applications, and because the strong interplay between the magnetic and superconducting properties has led to close comparisons…