The magnetic susceptibility between 1.5 and 800 K, the infrared reflectivity at room temperature and the temperature dependence of the dielectric constant at mm-wavelengths are reported for single crystalline BiFeO3. A well developed…
Infrared reflection and transmission as a function of temperature have been measured on single crystals of Cu$_{3}$Bi(SeO$_{3}$)$_{2}$O$_{2}$Cl. The complex dielectric function and optical properties along all three principal axes of the…
Reflection and transmission as a function of temperature (5--300 K) have been measured on single crystals of the multiferroic compound FeTe$_{2}$O$_{5}$Br utilizing light spanning the far infrared to the visible portions of the…
We present the results of pressure-dependent far-infrared reflectivity measurements on the multiferroic perovskite BiFeO3 at room temperature. The observed behavior of the infrared-active phonon modes as a funtion of pressure clearly…
Magnetic dc susceptibility between 1.5 and 800 K, ac susceptibility and magnetization, thermodynamic properties, temperature dependence of radio and audio-wave dielectric constants and conductivity, contact-free dielectric constants at…
BiMnO3 (BMO), ferromagnetic (FM) below Tc = 100 K, was believed to be also ferroelectric (FE) due to a non-centro-symmetric C2 structure, until diffraction data indicated that its space group is the centro-symmetric C2/c. Here we present…
Polarized infrared reflectivity spectra of a (110)-oriented TbScO3 single crystal plate were measured down to 10 K. The number of observed polar phonons active along the crystallographic c axis at low temperatures is much higher than…
We have investigated crystal field and phonon dynamics of the multiferroic orthoferrite DyFeO$_3$ via polarized infrared spectroscopy. Reflectance of single crystals was measured in the far- to mid-infrared spectral range at range of…
We present neutron inelastic scattering measurements of the low-energy phonons in single crystal BiFeO3. The dispersions of the three acoustic phonon modes (LA along [100], TA1 along [010] and TA2 along [110]) and two low energy optic…
We report on polarized infrared reflectivity measurements of multiferroic, monoclinic MnWO4 between 10K and 295K. The full dielectric tensor and the frequency dependence of the orientation of the principal axes have been determined in the…
High quality single crystals of Bi2Se3 were grown using a modified Bridgman technique, the detailed study were carried out using Raman spectroscopy and characterized by Laue diffraction and high resolution transmission electron microscopy.…
Infrared reflectivity and time-domain terahertz transmission spectra of EuTiO3 ceramics revealed a polar optic phonon at 6 - 300K, whose softening is fully responsible for the recently observed quantum paraelectric behaviour. Even if our…
We present a comprehensive study of polar and magnetic excitations in BiFeO3 ceramics and a thin film epitaxially grown on an orthorhombic (110) TbScO3 substrate. Infrared reflectivity spectroscopy was performed at temperatures from 5 to…
We present reflectance measurements in the infrared region on a single crystal the rare earth scandate DyScO3. Measurements performed between room temperature and 10 K allow to determine the frequency of the infrared-active phonons, never…
We have measured near normal incidence far infrared (FIR) reflectivity spectra of a single crystal of TbMnO3 from 10K to 300K in the spectral range of 50 cm$^{-1}$ to 700 cm$^{-1}$. Fifteen transverse optic (TO) and longitudinal optic (LO)…
We measured the temperature dependent infrared reflectivity spectra of TbMnO3 with the electric field of light polarized along each of the three crystallographic axes. We analyzed the effect, on the phonon spectra, of the different phase…
We provide a detailed study of the reflectivity of multiferroic TbMnO_3 for wave numbers from 40 cm^{-1} to 1000 cm^{-1} and temperatures 5 K < T < 300 K. Excitations are studied for polarization directions E || a, the polarization where…
We performed factor-group analysis of all phonons in possible monoclinic C2/c and C2 structures of BiMnO3 and compared it with our experimental infrared and Raman spectra. We conclude that the crystal structure is centrosymmetric C2/c in…
Raman scattering measurements on BiFeO3 single crystals show an important coupling between the magnetic order and lattice vibrations. The temperature evolution of phonons shows that the lowest energy E and A1 phonon modes are coupled to the…
We measured phonon dispersion in single crystal EuTiO$_3$ using inelastic x-ray scattering. A structural transition to an antiferrodistortive phase was found at a critical temperature $T_0$=287$\pm$1 K using powder and single-crystal x-ray…